Feasibility study of the minimum quantity lubrication in high-speed end milling of NAK80 hardened steel by coated carbide tool

High-speed milling of hardened steels generates high cutting temperature and leads to detrimental effects on tool life and workpiece surface finish. In this paper, feasibility study of the minimum quantity lubrication (MQL) in high-speed end milling of NAK80 hardened steel by coated carbide tool was undertaken. Flood cooling and dry cutting experiments were conducted also for comparison. It is found that cutting under flood cooling condition results in the shortest tool life due to severe thermal cracks while the use of MQL leads to the best performance. MQL is beneficial to tool life both in the lower speed cutting and the higher speed cutting conditions. A less viscous oil of MQL is essential in high cutting speed so that cooling effect can be effective. SEM micrograph of the insert shows that the use of MQL in high-speed cutting can delay welding of chips on the tool and hence prolongs tool life as compared with dry cutting condition. The application of MQL also improves machined surface finish in high-speed milling of die steels.     

不锈钢活性激光焊工艺研究

以不锈钢SUS304作为试验对象,分别研究了焊接速度、散焦离焦量、激光功率和保护气体等工艺参数以及活性剂和活性元素硫对不锈钢YAG激光焊焊缝成形的影响.试验结果表明,各焊缝表面成形良好,焊接速度和激光功率能明显影响焊缝成形,散焦离焦量和保护气体种类对YAG激光焊焊缝成形的影响较小.与硫含量较低的情况相比,活性剂和活性元素硫含量较高的情况下均能使得焊缝熔宽发生明显收缩,随着热输入量增加,活性剂增加熔深的效果也越明显,表明活性剂对熔深的影响效果与焊接过程的热输入量有密切联系.     

铝合金液态与半固态压铸件的组织性能研究

对A356铝合金液态与半固态压铸成形件在压铸态和T6热处理态下的力学性能与微观组织进行了研究。试验得出，与液态压铸成形件相比，半固态压铸成形件可以获得更佳的综合力学性能；经同样T6热处理后，两者抗拉强度都得到提高，伸长率下降，但半固态压铸成形件抗拉强度提高的幅度更大，伸长率降低得更少。从微观角度解释了两种不同成形方法产生这一性能差异的内在原因。     

一种新型振动下料机的PLC控制

在分析了新型振动下料机采用继电器－接触器控制方式存在不足的基础上，指出了对其进行PLC控制的必要性。分析了该振动下料机的基本构成及工作原理，建立了相应的液压系统。针对下料机正常工作对控制系统要求，确定了PLC的输入量及输出量，建立了PLC控制的硬件接线图，编制了相应的梯形图控制软件。大量实验验证了该控制方案的可行性和实用性。     

The significance of deposition point standoff variations in multiple-layer coaxial laser cladding (coaxial cladding standoff effects)

Direct laser deposition (DLD) is an additive manufacturing process that builds up a part layer-by-layer by fusing metal powder to a solid substrate. A coaxial laser and powder delivery head is commonly used, and here a critical process variable is the standoff distance between the nozzle and the material deposition point. This contribution investigates the role of this variable and the effect that it has on the final part geometry. The experimental results show that good layer consistency can, in fact, be obtained with no movement of the substrate between layers for more than 20 layers, or 10 mm under tested conditions, and that poorer results are obtained by regular movement of the substrate by a badly chosen constant amount. A theoretical analysis of the situation establishes a method to estimate melt pool size using an analytically calculated temperature near the heat source. Based on this, simple heat and mass flow models are established to allow some of the results to be explained.     

原位TiC颗粒增强铸造钢基复合材料制备工艺

利用钢液自身的高温直接引燃压入其中的Ti-C-Fe预制块，原位合成TiC增强颗粒，然后，对含有TiC颗粒的钢液进行铸造形成，即可获得TiC颗粒增强钢基复合材料。着重研究了钢液温度、合成的TiC颗粒含量以及钢液保温时间对复合材料组织的影响。在此基础上，优化了复合材料的制备工艺参数，并制备出了具有较理想组织的复合材料。     

堆焊结构的氢浓度分布及其对剥离断裂的影响

采用有限元分析方法计算堆焊结构中氢浓度的分布，并将电解充氢试验条件下试块中氢扩散行为的计算结果和高压釜试验条件的计算结果进行对比分析。计算结果表明，采用电解充氢方法，可以在熔合线附近获得与高压釜充氢数值相近的氢浓度峰值，而到达这一峰值的时间较短。通过解析模型比较了不同试样条件和电解充氢条件对试验结果的影响。结果显示，增大充氢电流密度，延长充氢时间，减薄母材厚度，均使氢浓度峰值升高，从而使堆焊层剥离     

高锰铝青铜的微生物腐蚀行为研究

利用AFM、SEM和XRD等现代表面分析手段研究了高锰铝青铜(ZQA112-8-3-2)合金在含硫酸盐还原菌(SRB)的海水环境中的腐蚀行为.结果表明,SRB不容易在高锰铝青铜表面吸附而形成完整的微生物膜.高锰铝青铜的微观组织由β相、κ相与α相组成,在腐蚀过程中β相、κ相与α相组成了腐蚀微电池,β相和κ相相对于α相是阳极,发生了阳极溶解.从腐蚀形貌中可看出在培养基溶液中腐蚀比在3.5%NaCl溶液中的腐蚀发生了更严重的选择性腐蚀,培养基溶液中SRB的代谢产物加剧了脱铝腐蚀.     

高膜厚PU防腐系统在油气管道上的应用

高膜厚PU防腐系统可解决防腐工程上的死角，包括异形、补口、三通、弯头、法兰、阀门等几何形状复杂金属外表面的防腐，以及老龄在役管线的防腐结构的修复。这种防腐系统的使用寿命可达30a。对国内油气管道防腐涂层常用的国产环氧粉末防腐结构和高膜厚PU防腐结构各项技术性能指标进行了对比，又以环氧粉末和高膜厚PU防腐系统用于管道防腐和储罐防腐进行了详细的对比，论证了使用高膜厚PU防腐系统技术的可行性和经济性。     

燃烧法制备SOFC用Ni/YSZ阳极材料

以Y(NO3)3、Zr(NO3)4、Ni(NO3)2和有机燃料为原料,采用低温燃烧法制备了NiO/YSZ复合粉料,然后于800℃在H2中还原制备了Ni/YSZ阳极材料.研究了燃烧合成过程中氧化物与有机燃料的配比对反应产物的影响.结果表明当氧化物与燃料的比例为23时,低温燃烧后可成功合成结晶充分的NiO/YSZ粉体.对合成粉体的SEM、TEM观察以及制备的Ni/YSZ阳极材料的SEM观察结果表明,低温燃烧合成的NiO/YSZ粉体细小且两相混合均匀,颗粒粒径为0.5 μm～1 μm.与机械混合法相比,采用燃烧法合成粉体,干压成型制备的Ni/YSZ阳极材料,不仅Ni在YSZ基质中分布更均匀,而且金属陶瓷中的两相均形成了连续的网络结构.