Crystalline morphology and isothermal crystallization kinetics of poly(ethylene terephthalate)/clay nanocomposites

A poly(ethylene terephthalate) (PET)/montmorillonite clay nanocomposite was synthesized via in situ polymerization. Microscopic studies revealed that in an isothermal crystallization process, some crystallites in the nanocomposite initially were rod‐shaped and later exhibited three‐dimensional growth. The crystallites in the nanocomposite were irregularly shaped, rather than spherulitic, being interlocked together without clear boundaries, and they were much smaller than those of neat PET. With Avrami analysis, the isothermal crystallization kinetic parameters (the Avrami exponent and constant) were obtained. The rate constants for the nanocomposite demonstrated that clay could greatly increase the crystallization rate of PET. The results for the Avrami exponent were consistent with the observation of the rodlike crystallites in the PET/clay nanocomposite during the initial stage. Wide‐angle X‐ray scattering and Fourier transform infrared studies showed that, in comparison with neat PET, the crystal lattice parameters and crystallinity of the nanocomposite did not change significantly, whereas more defects may have been present in the crystalline regions of the nanocomposite because of the presence of the clay. © 2004 Wiley Periodicals, Inc. J Appl Polym Sci 94: 1381–1388, 2004     

H4SiW12O40-PAn催化剂催化合成苯甲醛乙二醇缩醛

报道了以自制的H4SiW12 O40 (硅钨酸 ) -PAn (聚苯胺 )为催化剂 ,通过苯甲醛和乙二醇为原料合成了苯甲醛乙二醇缩醛。实验表明 :合成苯甲醛乙二醇缩醛适宜反应条件为 :n(苯甲醛 ) /n(乙二醇 ) =1 /2 .0 ,催化剂用量为反应物料总质量的 1 .0 % ,环己烷为带水剂 ,反应时间 1 .0h。上述条件下 ,苯甲醛乙二醇缩醛的收率可达 86.7% .     

红细胞瞬间磁化试剂的制备与应用

目的研制用于ABO、RHD血型检测试剂的红细胞瞬间磁化试剂。方法采用共沉淀法制备磁性粒子,并检测其主要成分及粒径大小,用此磁性粒子制备红细胞瞬间磁化试剂,并分别进行各项检测。结果磁性粒子的主要成分为四氧化三铁,粒径100nm左右。该试剂的外观及特异性均合格,磁响应时间不超过30s,重复性较好,敏感性为98.20%,与试管法检测结果比较,差异无显著意义。结论红细胞瞬间磁化试剂可用于红细胞系统的血型检测。     

磷石膏综合利用的现状和研究进展

介绍磷石膏的利用情况和研究进展。利用磷石膏作水泥缓凝剂、生产硫酸联产水泥的工艺日臻成熟，利用磷石膏生产石膏建筑材料、硫酸钾、硫酸铵和碳酸钙的技术已进入工业化阶段。磷石膏还可用于制硫脲、氯化钙和复合肥、活性硅酸钙及做建筑胶材料、加固软土地基等。另外，在农业上也有广泛的用途。     

陶瓷企业新建煤气站管理要点

目前,随着我国能源政策和成品油价格的上扬,许多陶瓷企业根据自身的发展情况以及气体燃料所具有的优越性,选择了煤炭气化方式,全国各地特别是山东、广东、河北、辽宁近年来煤气站如雨后春笋般的发展起来.从工艺上分为冷、热煤气站;从设备上分为单段、两段炉煤气站;从原料上分为块煤、粉煤、型煤煤气站.目的是生产可燃气体,用于陶瓷制品的烧成.     

ABS/镁盐晶须复合材料的研究

以（乙烯／乙酸乙烯酯／苯乙烯）三元共聚物（BS树脂）为增容荆，采用双螺杆挤出机制备了（丙烯腈／丁二烯／苯乙烯）共聚物（ABs）／镁盐晶须复合材料，研究了BS树脂、镁盐晶须用量对复合材料力学性能、流动性能的影响、结果表明，加入BS树脂有利于提高复合材料的拉伸强度和冲击强度，复合材料的熔体流动速率（MFR）随BS树脂用量增加而增大，且其MFR对温度或负荷呈非线性函数关系，比ABS对负荷更为敏感．     

Volume phase transition of polyelectrolyte gels in dimethyl sulfoxide/ tetrahydrofuran mixtures

Copolymer gels were prepared from 2-(acrylamido)-2-methylpropanesulfonic acid (AMPS), N,N-dimethylacrylamide (DMAA, comonomer) and N,N′-methylenebis(acrylamide) (BIS). The mole fraction of AMPS were 0.2674 and 0.4318, respectively, with the same BIS mole fraction of 0.013. These gels with counterions H⁺, Na⁺, and K⁺ were swollen at 25°C in mixtures of dimethyl sulfoxide (DMSO) and tetrahydrofuran (THF). A volume phase transition was observed at the THF volume fraction of about 0.58, indicating that the volume phase transition in a polyelectrolyte gel occurs when the medium polarity decreases sufficiently for ion-pair formation. On changing the counterion, the fraction of DMSO in the solvent mixture which is required to initiate swelling decreases in the order Na⁺, H⁺, and K⁺, the same as for counterion condensation in identical gels.     

石灰石在煤气化过程中的催化和固硫作用

基于CaO在煤气化中的催化和固硫作用,以及石灰石加热分解的性质,石灰石有可能作为煤气化过程中的催化剂和固硫剂。本文根据国内外对石灰石在煤燃烧和煤气化中作用的研究,从石灰石结构、Ca/C,Ca/S,可能的反应机理等几个方面进行了介绍和分析,并指出需进一步研究的内容。     

Correlation of the reactivity,the active surface area and the total surface area of thin films of pyrolytic carbon

Using thin films of pyrolytic carbon the rate of the reaction with oxygen has been measured over the temperature range 625–740°C and at pressures of oxygen from 6–100 torr. The active surface area (ASA) of the films was measured from the total concentration of strongly-bound complexes with oxygen on the surface and the relative total surface area (TSA) was measured by low-temperature adsorption of nitrogen. A maximum in reactivity and in ASA was observed for films of average thickness of about 20 nm with a TSA of about 30 m² g^?1. At the maximum the ASA and TSA were essentially equal. The results are interpreted in terms of the mechanism of formation of pyrolytic carbon in the initial stages.     