17-4PH沉淀硬化不锈钢氮离子注入及其复合改性的研究

采用N+注入，N-C-O共渗结合N+注入的表面复合改性方法，探索强化17－4PH钢表面的有效途径，该方法赋予基体表面一定深度的改性范围与低摩擦系数，因而强化效果达到最佳。同时还探索了不同时效温度下，基体心部硬度变化的规律。     

红外测温技术在离心复合铸造轧辊生产上的应用

本文分析了离心复合铸造轧辊生产过程中离心机停机温度和时间对轧辊质量的影响 ,提出了用先进的红外测温技术来预报停机温度和时间 ,以实现微机监控适时停机 ,保证轧辊内外层熔合良好 ;同时指出了红外测温技术在离心复合铸造轧辊生产上的应用前景     

NANO-MULTILAYERS WITH HIGH PERPENDICULAR ANISOTROPY FOR MAGNETIC RECORDING

(FePt/Ag)n nano-multilayers were deposited on MgO (100) single crystal with laser ablation and then subjected to annealing. FePt L1o grains with (001) texture and thus a large perpendicular magnetic anisotropy constant Ku of the order of 106 J/m3 were formed. A thick Ag layer is found to be favorable for decreasing the dispersion of the easy axis for magnetization. The measurement of time decay of magnetization gave rise to a small activation volume of the order of 10-25m3, showing the promising of being the recording medium for future high density perpendicular recording.     

金品纯度的比重法测定

介绍了金品纯度的测定方法,推导出了比较实用的纯度计算、杂质估算和温度影响等几个表达式。     

回火过程应力场计算机模拟

回火过程应力场计算机模拟林家骝，杨振枢，于震宗，段贵明（清华大学）郭剑仁，史全兴，谢克仁（内蒙古第一机器厂）ＡＳｔｕｄｙｏｆＮｕｍｅｒｉｃａｌＳｉｍｕｌａｔｉｏｎｏｆＳｔｒｅｓｓＦｉｅｌｄｄｕｒｉｎｇＴｅｍｐｅｒｉｎｇ￥ＬｉｎＪｉａｌｉｕ；ＹａｎｇＺ...     

国产气相聚乙烯浆液催化剂的工业应用

本文简要阐述了北化院BCS01和上海院SLC-S两种国产气相聚乙烯浆液催化剂的性能、催化剂结构,在Unipol聚乙烯工业装置上应用结果,以及和进口同类催化剂UCAT-J的性能比较。     

NIT-Ph-p-BEN氮氧自由基的制备及催化降解性

以对醛基苯甲酸为原料，通过醛酸与2,3-二甲基-2,3-二羟胺基丁烷缩合，再经NaIO4氧化最终制得4-(4,4,5,5-四甲基-1,3-二氧化物)咪唑基-1-苯甲酸（NIT-Ph-p-BEN氮氧自由基）。采用FTIR、UV、ERP（电子顺磁共振波谱仪）和元素分析等对其结构进行表征；通过催化降解废水中有机染料甲基橙、甲基蓝和罗丹明B对其催化活性进行了评估。结果表明，当甲基橙、甲基蓝和罗丹明B浓度为15 mg/L，NIT-Ph-p-BEN质量浓度为0.15 g/L，H2O2浓度为30 mmol/L时，NIT-Ph-p-BEN对甲基橙有更好的催化降解性，仅在1 h内甲基橙的降解率达到94.26%。此外，反应机理表明，H2O2有助于实现NIT-Ph-p-BEN自由基的再生和循环利用。     

抗蚜威原药和制剂的气相色谱分析

本文报道了抗蚜威的气相色谱分析方法，其标准偏差为０．０１９，变异系数为０．２４４％，回收率为９９￣１０１％，适于抗蚜威原药和制剂的分析。     

Effect of preparation conditions on the properties of a coal-derived activated carbon honeycomb monolith

Activated carbon honeycomb (ACH) monoliths were prepared by extruding of a mixture of bituminous coal and organic additives and subsequent carbonization and steam activation. Preparation parameters that were varied were carbonization temperature and activation time. The carbonization conditions were 500, 650 and 800 °C for 1 h and the steam activation conditions were 850 °C for 2, 4 and 6 h. The monoliths at various states were characterized by SEM, XRD, nitrogen adsorption and compression test. It was found that carbonization temperature has significant effects on pore size distribution and mechanical strength of ACH monoliths. The ACH monoliths prepared from high carbonization temperatures exhibited lower values of the BET surface area and total pore volume and higher value of the mechanical strength than those of the ACH monoliths prepared from low carbonization temperatures. This was attributed to the effect of high temperature carbonization that results in the formation of relatively less defective structures.