Properties of poly(ethylene terephthalate)–poly(ethylene naphthalene 2,6‐dicarboxylate) blends with montmorillonite clay

The production and properties of blends of poly(ethylene terephthalate) (PET) and poly(ethylene naphthalene 2,6‐dicarboxylate) (PEN) with three modified clays are reported. Octadecylammonium chloride and maleic anhydride (MAH) are used to modify the surface of the montmorillonite–Na⁺ clay particles (clay–Na⁺) to produce clay–C18 and clay–MAH, respectively, before they are mixed with the PET/PEN system. The transesterification degree, hydrophobicity and the effect of the clays on the mechanical, rheological and thermal properties are analysed. The PET–PEN/clay–C18 system does not show any improvements in the mechanical properties, which is attributed to poor exfoliation. On the other hand, in the PET–PEN/clay–MAH blends, the modified clay restricts crystallization of the matrix, as evidenced in the low value of the crystallization enthalpy. The process‐induced PET–PEN transesterification reaction is affected by the clay particles. Clay–C18 induces the largest proportion of naphthalate–ethylene–terephthalate (NET) blocks, as opposed to clay–Na⁺ which renders the lowest proportion. The clay readily incorporates in the bulk polymer, but receding contact‐angle measurements reveal a small influence of the particles on the surface properties of the sample. The clay–Na⁺ blend shows a predominant solid‐like behaviour, as evidenced by the magnitude of the storage modulus in the low‐frequency range, which reflects a high entanglement density and a substantial degree of polymer–particle interactions. Copyright © 2005 Society of Chemical Industry     

Morphology and properties of poly[2‐methoxy‐5‐(2′‐ethyl‐hexyloxy)‐para‐phenylene vinylene]/silica nanoparticle hybrid films

Poly[2‐methoxy‐5‐(2′‐ethyl‐hexyloxy)‐para‐phenylene vinylene] (MEH‐PPV)/silica nanoparticle hybrid films were prepared and characterised. Three kinds of materials were compared: parent MEH‐PPV, MEH‐PPV/silica (hybrid A films), and MEH‐PPV/coupling agent MSMA/silica (hybrid B films), in which MSMA is 3‐(trimethoxysilyl) propyl methacrylate. It was found that the hybrid B films could significantly prevent macrophase separation, as evidenced by scanning electron and fluorescence microscopy. Furthermore, the thermal characteristics of the hybrid films were largely improved in comparison with the parent MEH‐PPV. The UV‐visible absorption spectra suggested that the incorporation of MSMA‐modified silica into MEH‐PPV could confine the polymer chain between nanoparticles and thus increase the conjugation length. The photoluminescence (PL) studies also indicated enhancement of the PL intensity and quantum efficiency by incorporating just 2 wt% of MSMA‐modified silica into MEH‐PPV. However, hybrid A films did not show such enhancement of optoelectronic properties as the hybrid B films. The present study suggests the importance of the interface between the luminescent organic polymers and the inorganic silica on morphology and optoelectronic properties. Copyright © 2004 Society of Chemical Industry     

Properties of nanoporous organosilicate hybrid thin films with a bimodal pore size distribution

Low dielectric poly[methylsilsesquioxane‐ran‐trifluoropropylsilsesquioxane‐ran‐(2,4,6,8‐tetramethyl‐2,4,6,8‐tetraethylenecyclotetrasiloxane)silsesquioxane]s {P[M‐ran‐TFP‐ran‐(TCS)]SSQs} having various compositions were synthesized using trifluoropropyl trimethoxysilane, methyl trimethoxysilane and 2,4,6,8‐tetramethyl‐2,4,6,8‐tetra(trimethoxysilylethyl)cyclotetrasiloxane. The chemical composition of the polymers and the content of SiOH end‐groups were controlled by adjusting the reaction conditions, and they were characterized by ¹H‐NMR. The thermally decomposable trifluoropropyl groups on the P[M‐ran‐TFP‐ran‐(TCS)]SSQ backbone and heptakis(2,3,6‐tri‐O‐methyl)‐β‐cyclodextrin (CD) were employed as pore generators. The dielectric constants of the porous CD/P[M‐ran‐TFP‐ran‐(TCS)]SSQ films were in the range 2.0–2.7 (at 100 kHz) depending on the concentration of the porogens, and showed no change over 4 days under aqueous conditions. The pore size of the films showed a bimodal distribution, with diameters of ca 0.5–1.0 nm for those originating from the trifluoropropyl groups and 1.7 nm from the CD. The elastic modulus and hardness of the 30 vol% CD‐blended film with a dielectric constant of 2.26 were 2.40 and 0.38 GPa, respectively, as determined by a nanoindenter. Copyright © 2005 Society of Chemical Industry     

A simple handling technique for mammalian oocytes and embryos during preparation for transmission electron microscopy

Due to their small size, mammalian oocytes and embryos pose unique problems during preparation for transmission electron microscopy. This paper outlines a method which combines protein embedding with centrifugation to locate the specimens on the face of a Beem capsule mould. This method facilitates both the processing of oocytes with minimal loss and rapid location of the specimens within the block for simultaneous sectioning, staining and examination.     

Using ion implantation to adjust the transition temperature of superconducting films

We summarize a continuing investigation into using ion implantation to alter the transition temperature of superconducting thin films. The primary motivation for the work presented here was to study the feasibility of using magnetic ion doping to replace the bi-layer T_c control process currently used for certain cryogenic detector applications at National Institute for Standards and Technology. The results from work with various ion species implanted into aluminum, molybdenum, titanium and tungsten host films are presented.     

Protein binding study of isoflavone, perillyl alcohol and S-ibuprofen by high-performance frontal analysis

High-performance frontal analysis (HPFA) was used for a protein binding study of isoflavones (daidzein, genistin, and genistein), enantiomers of perillyl alcohol and S-ibuprofen to human serum albumin (HSA). The analyses were performed on a Develosil and Inertsil 100-Diol-5 column (10 cm×4.6mm). Sodium phosphate solution (pH 7.4, ionic strength 0.17) was used as the mobile phase at a flow rate of 1 ml/min. To ensure the drug to be eluted as a trapezoidal peak with a plateau, injection volumes were each fixed up the zonal profile with an evident plateau appears. The unbound drug concentration was determined from a plateau height of the plateau region after that experimental data were fitted by Scatchard equation. The binding constants (K) and total binding affinities (nK) of drugs to HSA were calculated, respectively.     

A simple mathematical analysis on the effect of sand in Cr(VI) reduction using zero valent iron

A simple mathematical model was proposed to analyze the enhancement of Cr(VI) reduction when sand materials are added to the zero valent iron (ZVI). Natural decay of Cr(VI) in a control experiment was analyzed by using a zero-order decay reaction. Adsorption kinetics of Cr(VI) to sand was modeled as a first-order reversible process, and the reduction rate by ZVI was treated as a first-order reaction. Natural decay of Cr(VI) was also included in other experiments, i.e., the adsorption to sand, the reduction by ZVI, and both adsorption and reduction when sand and ZVI are present together. The model parameters were estimated by fitting the solution of each model to the corresponding experimental data. To observe the effect of sand addition to ZVI, both adsorption and reduction rate models were considered simultaneously including the natural decay. The solution of the combined model was fitted to the experimental data to determine the first-order adsorption and reduction rate constants when sand as well as ZVI is present. The first-order reduction rate constant in the presence of sand was about 35 times higher than that with ZVI only.     

Mechanical improvement of concrete by irradiated polypropylene fibers

Fiber reinforced concrete (FRC) contains fibers physically mixed with gravel, sand, cement, and water. So far, adequate mechanical performance of FRC has been obtained at high cost and using complex technologies; important here is the geometry and surface characteristics of the polymers. We have modified polymeric‐fiber surfaces by using gamma radiation. Irradiated polypropylene (PP) fibers were submitted to 0, 5, 10, 50, and 100 kGy of gamma irradiation dosages. First, tensile strength of PP fibers was evaluated, and then fibers blended at 0, 1.0, 1.5, and 2.0% in volume with Portland cement, gravel, sand, and water. The highest values of compressive strength were obtained with irradiated‐fibers at 10 kGy and 1.5% in volume of fiber. The result is 101 MPa, as compared to 35 MPa for simple concrete without fibers. POLYM. ENG. SCI., 45:1426–1431, 2005. © 2005 Society of Plastics Engineers     

Peracetic acid pretreatment of sugarcane bagasse for enzymatic hydrolysis: a continued work

Previous work has shown that the enzymatic hydrolysis of sugarcane bagasse could be greatly enhanced by peracetic acid (PAA) pretreatment. There are several factors affecting the enzymatic digestibility of the biomass, including lignin and hemicelluloses content, cellulose crystallinity, acetyl group content, accessible surface area and so on. The objective of this work is to analyze the mechanism of the enhancement of enzymatic digestibility caused by PAA pretreatment. Delignification resulted in an increase of the surface area and reduction of the irreversible absorption of cellulase, which helped to increase the enzymatic digestibility. The Fourier transform infrared (FTIR) spectrum showed that the absorption peaks of aromatic skeletal vibrations were weakened or disappeared after PAA pretreatment. However, the infrared crystallization index (N.O'KI) was increased. X‐ray diffraction (XRD) analysis indicated that the crystallinity of PAA‐treated samples was increased owing to the partial removal of amorphous lignin and hemicelluloses and probable physical change of cellulose. The effect of acetyl group content on enzymatic digestibility is negligible compared with the degree of delignification and crystallinity. The results indicate that enhancement of enzymatic digestibility of sugarcane bagasse by PAA pretreatment is achieved mainly by delignification and an increase in the surface area and exposure of cellulose fibers. Copyright © 2008 Society of Chemical Industry