Mold-filling characteristics of AZ91 magnesium alloy in the low-pressure expendable pattern casting process

The magnesium (Mg) alloy low-pressure expendable pattern casting (EPC) process is a newly developed casting technique combining the advantages of both EPC and low-pressure casting. In this article, metal filling and the effect of the flow quantity of inert gas on the filling rate in the low-pressure EPC process are investigated. The results showed that the molten Mg alloy filled the mold cavity with a convex front laminar flow and the metal-filling rate increased significantly with increasing flow quantity when flow quantity was below a critical value. However, once the flow quantity exceeded a critical value, the filling rate increased slightly. The influence of the flow quantity of inert gas on melt-filling rate reveals that the mold fill is controlled by flow quantity for a lower filling rate, and, subsequently, controlled by the evaporation of polystyrene and the evaporation products for higher metal velocity. Meanwhile, the experimental results showed that the melt-filling rate significantly affected the flow profile, and the filling procedure for the Mg alloy in the low-pressure EPC process. A slower melt-filling rate could lead to misrun defects, whereas a higher filling rate results in folds, blisters, and porosity. The optimized filling rate with Mg alloy casting is 140 to 170 mm/s in low-pressure EPC.     

活性酯硬化水玻璃砂的研究

用焙烧活性砂混制而成的活性酯硬化水玻璃砂与普通酯硬化水玻璃砂相比，强度成倍提高，从而减少水玻璃的加入量，改善水玻璃砂的溃散性。实验证明：原砂的表面活性直接影响在水玻璃砂中水玻璃的加入量，是改善水玻璃砂溃散性的关键之一。焙烧活性砂的水玻璃加入量只要１．５％～２．０％，即能满足实际生产的强度要求。     

含CO2气体混合物在60℃时的混合性质

测定了６０℃和２－６００ｂａｒ时由ＣＯ２和Ｈｅ、Ａｒ、ＳＦ６以及ＣＨＦ３组成的等分子二元混合物的压缩因子，根据纯物质和混合物的压缩因子计算了压力混合效应和过剩体积。对于真实气体混合性质的描述，本文采用五参数的ＢＡＣＫ方程，方程计算值与实验值符合较好。     

Relative image similarity learning with contextual information for Internet cross-media retrieval

With the fast explosive rate of the amount of image data on the Internet, how to efficiently utilize them in the cross-media scenario becomes an urgent problem. Images are usually accompanied with contextual textual information. These two heterogeneous modalities are mutually reinforcing to make the Internet content more informative. In most cases, visual information can be regarded as an enhanced content of the textual document. To make image-to-image similarity being more consistent with document-to-document similarity, this paper proposes a method to learn image similarities according to the relations of the accompanied textual documents. More specifically, instead of using the static quantitative relations, rank-based learning procedure by employing structural SVM is adopted in this paper, and the ranking structure is established by comparing the relative relations of textual information. The learning results are in more accordance with the human’s recognition. The proposed method in this paper can be used not only for the image-to-image retrieval, but also for cross-modality multimedia, where a query expansion framework is proposed to get more satisfactory results. Extensive experimental evaluations on large scale Internet dataset validate the performance of the proposed methods.     

降维方法监督分类的比较研究

对ISOMap、LDA、LLE、PCA这4种典型降维算法的主要思想和算法步骤进行了详细分析,并将它们用于有监督分类。从实验结果分析得到结论 ,其可为有监督分类提供有益的借鉴。     

Preparation and Photoluminescence of Partially Filled ZnO Microtubes Using Block Copolymers

Partially filled ZnO microtubes were synthesized in large scale using block copolymers. The growth mechanism of this unique construction is proposed on the basis of adsorption of block copolymers on {0002} plane of wurtzite ZnO. The photoluminescence property of these unique ZnO microtubes is also studied using a Xe lamp as the excitation source at room temperature. Blue emission band at 425 nm is a much stronger ultraviolet emission band, which is due to laminar structure of ZnO microtubes.     

炭黑填充硬聚氯乙烯的改性

为使聚氯乙烯具有抗静电性能,采用加入具有导电性填料的方法,但加入大量的填料,会使硬聚氯乙烯的冲击性能降低,加工性能变差。本文是在以炭黑为填料的基础上,研究不同的改性剂和加工助剂改进硬聚氯乙烯的效果,结果表明,加入冲击改性剂和加工助剂后,大大增加了硬聚氯乙烯的冲击强度,且加工性能也得到改善,同时由于炭黑具有补强效果,其拉伸强度和弯曲强度在加入改性剂后也能满足使用要求。     

Kinetics for benzoylation of sodium 4-acetylphenoxide via third-liquid phase in the phase-transfer catalysis

In this research, the kinetics for synthesizing 4-acetylphenyl benzoate (R^*COOR) from benzoylation of sodium 4-acetylphenoxide via third-liquid phase-transfer catalysis was investigated. The reaction rate was observed to be strongly dependent on agitation speeds in the third-phase catalytic reaction. By forming the third-liquid phase, the observed reaction can be greatly enhanced to give a product yield of 100% in a duration of 3 min at 20 °C and 200 rpm. If a third-liquid phase was not formed in the liquid–liquid system, the reaction rate is very slow and the product yield is only 2% in 3 min at 20 °C. The reaction conducted in third-liquid phase-transfer catalytic system is faster than that in LLPTC system by 25–28 times. The amount of catalytic intermediate (QOR) in the third-liquid phase was about 50% of the catalyst initially added and kept about 30% of it remained after 1 min, and only small amounts of a catalytic intermediate residing in the organic phase were observed during the reaction using methyl t-butyl ether as the solvent. The concentration of catalytic intermediate slightly decreased with increasing reaction time, while the molar ratio of QOR to benzyl tri-n-butylammonium cation in the third-liquid phase remained almost constant after 1 min and increased with increasing agitation speeds. The experimental results were well described by the pseudo-first-order kinetics. The present work shows an effective method to synthesize 4-acetylphenyl benzoate.     

Synthesis of Biodiesel from Soybean Oil using Heterogeneous KF/ZnO Catalyst

Biodiesel was produced by transesterification of soybean oil with methanol using ZnO loaded with KF as a solid base catalyst. It was found that the catalyst with 15 wt.% KF loading and calcined at 873 K showed the optimum activity. XRD, IR and Hammett indicator method were employed for the catalyst characterization. The results showed the activity of the catalysts was correlated with their basicity. The influence of various reaction variables on the conversion was also discussed.