Fe_3O_4/PANI抗氧化水基磁流体的制备与表征 总被引:2,自引:0,他引:2
在无氮气保护条件下,用化学共沉淀法制备了四氧化三铁(Fe3O4)纳米颗粒,并通过表面原位合成法将颗粒用聚苯胺(PANI)包裹,由此获得兼具磁性和导电性能的纳米四氧化三铁/聚苯胺(Fe3O4/PANI)材料。作者称其为Fe3O4/PANI抗氧化水基磁流体。透射电子显微镜(TEM)分析表明,该法制备的Fe3O4/PANI复合粒子的粒径在30~50 nm,其分散性能比包裹前的Fe3O4粒子明显改善。红外光谱(FTIR)和X射线衍射(XRD)测试结果发现,Fe3O4粒子及Fe3O4/PANI复合粒子具有不同的物态和晶相结构。对纳米复合粒子的抗氧化性能和磁性能的检测证实,原位合成的Fe3O4/PANI复合粒子不仅能有效防止在空气中被氧化,还可在磁场环境中实现快速富集、定位,为Fe3O4/PANI纳米复合粒子在生物医学领域的应用提供了可能。 相似文献
12.
Observation of Effectiveness of Clinical Sterilization by CASP-80A Low-Temperature Plasma Sterilizer 总被引:1,自引:0,他引:1
The influence on the effectiveness of sterilization by low-temperature plasma sterilizer CASP-80A was investigated so as to provide a theoretical basis for reducing medical costs and achieving ideal sterilization effectiveness. To conduct the on-site simulation test, a clinical material sterilization test and a test of the influence of organic substance were conducted, the former by using the representative of Bacillus Stearothermophilus, preparing the bacteria-contaminated carrier through polytetrafluoroethylene (PTFE) simulated hose endoscopes, and the latter by using calf serum as the influence factor of the organic substance. The results show that the CASP-80A low-temperature plasma sterilizer could achieve effective sterilization by either the short-cycle or the long-cycle sterilization method depending on different materials, apparatus, and extent of contamination. The organic substances could influence the effectiveness of sterilization by the low-temperature plasma (H2O2) sterilizer. 相似文献
13.
14.
15.
16.
为使粉末反应喷涂技术实用化,提出并研究了反应喷涂锻造工艺。将Ti、C粉按化学计量配制,并加入少量Ni,混合后压成棒材作为喷涂材料。以铝包镍为过渡层,采用陶瓷棒喷枪,进行氧乙炔火焰反应喷涂锻造工艺试验,在316L钢板表面制备了TiC/Ni金属陶瓷涂层。工艺参数为:基体预热温度300~400℃,乙炔压力0.12~0.13MPa,乙炔流量0.7~0.8m3/h,氧气压力0.4~0.5MPa,氧气流量1.3~1.4m3/h,空气压力0.4~0.8MPa,喷涂角度90°,喷涂距离100~150mm。涂层经锻造气孔减小,与基体结合紧密,耐磨性能提高。实测锻造涂层的弹性模量147.79GPa,基体弹性模量202.99GPa。锻造试样涂层在不同载荷下的维氏硬度为541HV0.1、542HV0.2、499HV0.5,能够满足作为植入件的硬度要求。 相似文献
17.
18.
19.
20.