Effects of annealing on microstructure, mechanical and electrical properties of AlCrCuFeMnTi high entropy alloy

The multi-component A1CrCuFeMnTi high entropy alloy was prepared using a vacuum arc melting process. Serial annealing processes were subsequently performed at 590 ℃, 750 ℃, 955 ℃ and 1 100 ℃ respectively with a holding time of 4 h at each temperature. The effects of annealing on microstructure, mechanical and electrical properties of as-cast alloy were investigated by using differential thermal analysis （DTA）, X-ray diffraction （XRD）, scanning electron microscopy （SEM） and transmission electron microscopy （TEM）. The experimental results show that two C14 hexagonal structures remain unchanged after annealing the as-cast A1CrCuFeMnTi alloy specimens being heated to 1 100℃. Both annealed and as-cast microstructures show typical cast-dendrite morphology and similar elemental segregation. The hardness of alloys declines as the annealing temperature increases while the strength of as-cast alloy improves obviously by the annealing treatment. The electrical conductivities of annealed and as-cast alloys are influenced by the distribution of interdendrite re~ions which is rich in Cu element.     

等离子喷涂ZrO2／NiCoCrAlY梯度涂层中ZrO2组元的显微结构特征

Ｚｒｏ２／ＮｉＣｏＣｒＡｌＹ梯度涂层中的８％Ｙ２Ｏ３部分稳定ＺｒＯ２组元在等离子喷涂后的快速凝固和冷却过程，发生了ｃ→ｔ’非扩散型相变的ｃ→ｔ扩散型相变，以及少量的ｔ→ｍ相变。涂层中ＺｒＯ２主要由未转变的ｃ相及转变产物ｔ相和ｔ’相组成，并存在少量的ｍ相。     

氧化硼掺杂钛酸锶钡梯度陶瓷致密化及介电性

研究了氧化硼(B2O3)掺杂量及烧结温度对钛酸锶钡(Ba1-xSrxTiO3，x=0～0．4)致密化行为及其微观组织的影响，确定了不同成分钛酸锶钡中氧化硼掺杂量．随后，采用一系列Ba1-xSrxTiO3掺杂粉体，烧结制备了钛酸锶钡梯度陶瓷，并测试了其介电性能．结果表明，钛酸锶钡掺杂适量氧化硼明显降低烧结温度，在1300℃即可烧结致密化，比未掺杂相同成分的钛酸锶钡陶瓷烧结温度至少降低100℃；烧结后各成分单层陶瓷与梯度陶瓷介电性能随温度的变化表明，梯度组成陶瓷的居里峰温度区间显著展宽，大大降低了该温区的介温系数，可望提高该系列陶瓷元器件精度及稳定性。     

超高强度马氏体时效钢的发展

马氏体时效钢是以无碳(或超低碳)铁镍马氏体为基体的经时效生产金属间化合物沉淀硬化的超高强度钢。该钢在高强度时效处理前具有良好的成形性，时效处理几乎不变形，时效处理后有高强韧性。文中论述了典型Ni-Co-Mo-Ti-Al马氏体时效钢和Ni-Mo-Ti(-Cr-Al)无钴马氏体时效钢的化学成分和力学性能，阐述了马氏体时效钢在400～500℃时效时马氏体基体内产生大量强化效果极高、韧性损失极小的金属间化合物沉淀相的时效结构和强化机制，以及Ni、Co、Mo、Cr、Mn、Ti等元素在马氏体时效钢中的合金化作用。概述了马氏体时效钢的生产工艺，应用和发展趋向。     

Influence of deformation parameters on microstructure and mechanical properties of TA 15 titanium alloy

The influence of deformation parameters including deformation temperature, degree and speed on the microstructure and mechanical properties of TA15 titanium alloy was studied. The volume fraction, size and aspect ratio of primary a phase in deformed TAI 5 titanium alloy were quantitatively characterized. With increasing deformation temperature, the volume fraction and size of primary α phase decrease. The aspect ratio of primary a phase decreases with increasing deformation temperature. The tensile strength of TA15 alloy deformed at 0.1 mm/s is higher than that at 0.3 mm/s. After therlnoforming at 960℃, 0.1 mrn/s, the tensile strength is the highest up to 1 035 MPa and the elongation is 13.5%. When the thermoforming temperature is 1 050℃, the strength and elongation are both relative low, because the microstructure is Widmanstaten structure.     

TA15钛合金的形变热处理

研究了形变热处理对TA15钛合金组织与力学性能的影响。在α＋β两相进行形变热处理使组织中的条状初生α相碎化。对水冷的试样进行930℃／1h／空冷＋915℃／1h／空冷＋530℃／6h／空冷的处理，抗拉强度明显提高，组织中的条状初生α相发生球化。在β相进行形变热处理使强度略有降低，魏氏组织中的α层片增厚。     

C／C复合材料Mo-Si-N抗氧化涂层的制备

在C／C复合材料表面采用熔浆法制备Mo—Si系涂层的烧结过程中通入氮气，开发了Si3N4．MoSi2／Si—SiC（Mo-Si-N系）多层抗氧化涂层，并初步考察了涂层的抗氧化性能。结果表明，多层涂层的致密性主要受制于起始氮化温度。只有在Si熔点以上通入氮气，才能获得致密无缺陷的涂层。多层涂层的底层为SiC，外层为Si3N4，中间层为MoSi2／Si。这种多层涂层的抗氧化性能与涂层中MoSi2的含量有关；MoSi2含量为30％（体积分数，下同）和40％时，与真空中合成的Mo-Si涂层相比，高温抗氧化性能显著改善，抗氧化温度提高到1400℃～1450℃。     

Hot pressing of hydroxyapatite(HA)-Ti material and stability of HA

1　ＩＮＴＲＯＤＵＣＴＩＯＮＡｔｐｒｅｓｅｎｔ ,ｔｈｅｈｙｄｒｏｘｙａｐａｔｉｔｅ (ＨＡ )ａｎｄｔｈｅＨＡ ｂａｓｅｄｃｏｍｐｏｓｉｔｅｃａｎｎｏｔｂｅｕｓｅｄｆｏｒｈｅａｖｙｌｏａｄ ｂｅａｒｉｎｇａｐｐｌｉｃａｔｉｏｎｓａｓｈａｒｄｔｉｓｓｕｅｒｅｐｌａｃｅｍｅｎｔｉｍ ｐｌａｎｔｓｂｅｃａｕｓｅｏｆｔｈｅｉｒｐｏｏｒｍｅｃｈａｎｉｃａｌｐｒｏｐｅｒｔｉｅｓ[1] .Ｏｎｔｈｅｏｔｈｅｒｈａｎｄ ,ｔｈｅＨＡｃｏａｔｉｎｇｓｕｓｅｄｔｏｉｍｐｒｏｖｅｔｈｅｓｕｒｆａｃｅｂｉｏａｃｔｉｖｉｔｙｏｆＴｉａ…     

18Ni（200）马氏体时交钢的循环相变晶粒细化新工艺

研究了一种18Ni(200)马氏体时效钢的晶粒细化热处理新工艺。将高温固溶后具有粗大原努奥休氏晶粒的试样在不同温度短时保温，通过金相观察确定再结晶温度点，将试样加热到此点以上不同温度后冷却至室温，进行α=γ循环相变以细化晶粒，结合相变精细微观组织分析，开发出变温循环相变晶粒细化新工艺，达到了较好的细化效果，并较大幅度地提高了18Ni(200)马氏体时效钢的强度和塑性。     

TA15钛合金热变形工艺-组织的人工神经元预报

TA15钛合金经过不同条件的热约束变形之后进行金相观察,获得了工艺(温度、应变、应变速率、冷却方式)和组织(初生α相含量、初生α相尺寸、初生α相长径比)参数数据,分别以这些数据作为输入和输出,建立了结构为4×6×8×3的BP人工神经网络.研究结果表明:所建立的网络可以很好地反映出材料的工艺-组织之间的关系并且具有一定的精度,网络模型可以用来预测不同变形条件下TA15钛合金的组织,且对于TA15钛合金的实际生产具有有效的指导作用.