Microstructures of ultra-fine grained FeCoV alloys processed by ECAP plus cold rolling and their evolutions during tempering

A new processing method,equal channel angular pressing(ECAP)plus cold rolling(CR),was applied to producing ultra-fine grained FeCoV alloy.The microstructures of ultra-fine grained FeCoV alloy after ECAP,ECAP plus CR,and the effect of tempering treatment on the microstructure of FeCoV alloy produced by ECAP plus CR were investigated.The results show that an elongated substructure with a width of about 0.3μm is obtained after four-pass ECAP using Route A.Cold rolling after ECAP cannot change the morphologies of elongated substructure,and it results in higher fraction of high-angle boundaries and higher dislocation density compared with the identical ECAP without rolling.Subsequent tempering for 30 min at 853 K brings about many nano-phases precipitating at subgrain boundaries and insides the grains,and the size of precipitated phase is measured to be about 10 nm.Nano-phases grow up with increasing tempering temperature and equiaxed structure forms at 883 K.     

退火处理对超细晶Cu-Cr合金组织和性能的影响

对Cu-0．4Cr合金进行ECAP（等通道转角挤压）8道次的挤压，得到晶粒尺寸为500nm的等轴晶组织，然后在电阻炉内进行退火试验，通过对ECAP细晶的铜铬合金在473～873K退火1h，分析合金的组织和性能，研究该合金的硬度和导电性能。研究发现，弥散的Cr可以有效地阻止合金的晶粒长大；723K退火后，Cu-0．4Cr合金的电导率和硬度分别可达80．3％IACS和210．9HV，并有较好的综合性能。     

G20CrNi2MoA轴承钢控轧控冷工艺热模拟研究

控轧控冷是先进轴承钢的重要生产工艺。利用Gleeble3500热模拟试验机对G20CrNi2MoA轴承钢进行了控制轧制和控制冷却的热模拟试验，分析了变形温度、变形程度和冷却速率对G20CrNi2MoA优质滚动轴承钢微观组织和硬度的影响。基于试验结果，确定了开轧温度900 ℃、变形量30%的条件进行轧制，终轧后以5 ℃/s的冷却速率冷却到650 ℃，再以2 ℃/s的冷却速率冷却至室温的控轧控冷工艺。该工艺可获得比原始组织更细小均匀的贝氏体组织，试验钢综合力学性能有所提高，抗拉强度提升180 MPa、屈服强度变化较小、硬度提升50HV，断后伸长率提升2%。     

B92SiQL钢的高温流变行为及变形机制研究

B92SiQL钢因高强度及抗扭转能力在预应力镀锌钢丝领域备受青睐,但热加工参数对其变形行为及性能产生重要影响。本研究对B92SiQL钢进行了变形温度为1 173～1 373 K、应变速率为0.1～20 s^-1的热压缩实验,并基于Zener-Hollomon参数和线性拟合,建立了应变补偿型Arrhenius本构模型。结果表明,流变应力随变形温度的升高或应变速率的降低呈减小趋势,B92SiQL钢的热变形激活能(Q)约为305.865 kJ/mol。该模型得到流变应力预测值与实验值的线性相关系数(R)约为0.994,平均绝对相对误差(AARE)约为2.800%。在较低变形温度下,微观组织中依然存在被拉长的原始晶粒;在1 373 K-0.1 s^-1热变形条件下,B92SiQL钢几乎发生了完全的动态再结晶(DRX),晶粒产生明显粗化;应变速率增大至10 s^-1时,晶粒尺寸明显减小。根据加工硬化率与流变应力曲线确定了B92SiQL钢发生DRX的临界应力和应变,得到临界条件与Z参数呈指数关系。根据传统的Avrami方程建立了B92Si...     

40CrNiMo钢热变形行为及本构方程

用Gleeble-3500热模拟试验机对40CrNiMo钢在750~1050℃、0.1~50s-1变形条件下,进行了单道次热压缩试验,获得了其流变应力曲线。利用考虑应变补偿的双曲正弦模型、误差验证等方法,对流变应力数据进行了分析。结果表明:40CrNiMo钢的流变应力曲线呈现加工硬化型、动态回复型、动态再结晶型等几种类型;应变量一定,流变应力随着变形温度的降低和应变速率的增大而增大;应变速率较变形温度对流变应力曲线的波动影响显著,应变速率为50s-1,各变形温度下流变应力曲线均呈现明显波动;应变补偿下变形量对40CrNiMo钢的材料常数有显著影响;热变形激活能随变形增大在207.38~331.82kJ·mol-1变化;应变补偿下本构方程的平均相对误差不大于9%,近90%的相关系数大于0.90。     

Zr-4合金管材加工工艺对氢化物取向因子的影响

锆合金广泛应于水冷反应堆的堆芯包壳材料和结构材料。在核反应堆运行时,锆合金表面被水氧化的同时,还会同时生成氢气。部分氢被锆合金吸收生成片状或者针状氢化锆。氢化物取向因子是衡量核反应堆用锆合金管材氢化物的重要指标。文章通过氢化物实验研究了加工工艺参数轧制送进量、退火制度及矫直弯曲量对Zr-4合金管材氢化物取向因子的影响关系。结果表明:Zr-4合金氢化物取向因子随着轧制送进量的增加有增大的趋势;不同轧制送进量的管材再结晶退火后,氢化物取向因子呈无序紊乱状态;Zr-4合金管材氢化物取向因子随着矫直弯曲量的增大而加大。     

镁含量对铝阳极材料组织和电化学性能的影响

运用合金相电化学原理,向铝中添加合金元素镁,制备成Al-Mg二元合金,试验研究了镁含量对铝合金阳极材料组织与电化学性能的影响。结果表明,合金中Mg5Al8相随镁含量增加而增加且分布均匀。组织组成物的阳极性能良好,在浓度为3．5％的NaCl介质中,当w（Mg）从1％提高至30％时,进入稳定状态的开路电位从-0．79V负移至-1．18V,阳极极化率亦降低。