微量元素对焊缝扩散氢含量的影响

本文首次采用熔池添加合金过渡法（简称熔池法）系统地研究了微量元素钇（Ｙ）和碲（Ｔｅ）对焊缝扩散氢含量的影响，研究表明：与通常的药皮过渡法比较，熔池法降氢效果显著，可减少烧损昂贵的微量元素。改善焊接工艺性能，因此，对于微量元素在焊接材料中的应用与提高焊接工程质量都具有重要的意义，本文还探讨了微量元素钇和碲的降氢机理。     

Investigation on mechanism of fixing nitrogen in self-shielded flux cored arc welding

Prevention of nitrogen porosity in weld metal deposited with self-shielded flux cored wire with CaF_2-TiO_2-MgO slag system can be accomplished by using a "killing agent" such as titanium to react with nitrogen dissolved in the weld metal. The amount of titanium needed to prevent porosity is calculated thermodynamically for various dissolved nitrogen levels. Experimental flux cored wires are used to verify the thermodynamic model. It is concluded that approximately O.11 wt％ titanium in the weld deposit is need to prevent nitrogen porosity when welding without externally applied shielding.     

自保护药芯焊丝熔敷金属韧化的机理

自保护药芯焊丝是近年来国际上发展较快而我国的研究和开发相对滞后的一种焊接材料。其研究的核心是焊丝的工艺质量和熔敷金属的韧性。本通过在高铝系熔敷金属中添加微量元素，控制熔敷金属中夹杂物的形态、数量、尺寸等特征参数，对熔敷金属的成分、微观组织和性能进行了深入研究，获得了针状铁素体较多的显微组织，使其0℃的冲击吸收功达到97J。其研究结果对于提高高铝系熔敷金属的韧性具有重要的参考价值。     

再论药芯焊丝在船舶焊接中的缺陷及对策（上）

对药芯焊丝在船舶焊接中常见缺陷的产生机理和影响因素进行更深入的研究，从选材、焊接工艺和现场控制等提出防止措施，三英公司新研制的高质量SQJ501L药芯焊丝对于减少焊接缺陷的产生，提高船舶焊接质量起到重要作用。     

中国焊接技术的发展成就及行业概览(2)

3 中国焊接工艺应用现状 焊接已不再是一种单纯意义上的加工技艺，它已发展成为集多种学科于一体的一门工程工艺科学，并显现出极高的技术含量和附加值。     

再论药芯焊丝在船舶焊接中的缺陷及对策（下）

3．药芯焊丝角焊缝冷裂纹防止对策 为防止药芯焊丝角焊缝出现冷裂纹,从选材、控制焊接工艺、适当预热三方面提出有效措施（如图7所示）。选材上,要限制母材的碳当量,要限制焊丝的成分或强度。HIO级别的焊丝扩散氢含量越低越好,优选H5级别的焊丝;要控制保护气体的纯度,限制气体的露点。控制焊接工艺方面,焊接冷裂敏感性较大的接头时,要控制焊接电流和干伸长度,确保气保护效果尤其是现场防护、焊机、气阀、把线等是否能正常。焊接高拘束度、大板厚的结构,可以适当增加预热。     

低含金高强钢焊接冷裂判据

本文通过 PRRC 试验,研究了焊接接头防止冷裂纹的临界应力,局部预热附加热应力与预热和后热规范的关系,提出了国产低合金高强钢焊接接头的冷裂敏感系数判据,然后在实际工程中对所建立的判据进行了验证与应用。     

局部预热对焊接接头抗裂性能的影响

本文采用平板刚性拘束裂纹试验方法探讨了局部预热对焊接接头抗裂性能的影响。试验证明,局部预热对一定拘束条件下的焊接接头抗裂性能有双重作用,一是改善,二是降低。因此,在其一定的拘束条件下,存在一个不产生裂纹的“最佳局部预热温度范围”。Y形坡口的14MnMoNbB钢接头的最佳预热温度范围为150℃左右。     

国产低合金高强钢焊接冷裂纹专家系统初探

研制的焊接冷裂纹专家系统能系统地提供已有的国产低合金高强钢插销冷裂研究资料,判断被焊材料的冷裂敏感性,判定已有焊接工艺在防止冷裂方面的合理性,为新产品制定焊接工艺。