Sr对高铁Al-Si合金组织和性能的影响

研究了Sr元素（加入量分别为0．03％、0．06％、0．09％、0．12％和0．18％）对含Fe量为1．2％的ZL102合金的组织和性能的影响。研究发现，随着Sr元素的加入，合金中粗大的针状Fe相开始出现断裂分叉现象，同时针状Fe相的长度也随Sr元素加入量的增加而减小，但Sr对Fe相的针状形貌没有明显改变。随着Sr元素加入量逐渐增加，合金的抗拉强度和伸长率均呈现出先增后减的变化趋势。当Sr元素加入量达到0．12％时，合金材料的综合力学性能最佳。     

Friction and the development of hard alloy surface microstructures during wear

Investigations of wear in sliding friction of WC-Hadfield steel hard alloy against cast tool steel have been carried out in a broad range of velocities and pressure values. Structural and phase composition variations have been revealed. Friction-affected zone was found to be 450 μm in depth. Structural γ → α, γ → transformation regions are located within 100 μm of the surface. These transformations contributed to the total solid solution deformation hardening.     

Pd—DBS—偶氮胂新显色体系的分光光度法测定钛合金中微量钯

在较高酸度的H_3PO_4介质中钯与DBS—偶氮肿的新显色反应有较高的选择性。钯含量在0～10μg/10ml符合比尔定律,ε_(610)=2.37×10~4。提出不经分离,准确、快速测定钛合金中微量钯的方法。     

Banding formation and eutectic lamellar growth in directional solidified Ni50Al20Fe30 alloy

Banding formation and eutectic lamellar growth in a directionally solidified Ni₅₀Al₂₀Fe₃₀ alloy were investigated. It was found that the banding area consists of two layers. The first layer is a γ layer, while the subsequent one is a γ layer. The composition of various phases around the banding area changes with the solidification process. The banding is formed by two steps process and caused by factors such as the fractions during the sample growth process. It was found that the band was found at relatively low growth rate. Therefore. this study indicates that increasing the growth rate is an effective method to eliminate the band formation. Eutectic lamellae nucleate and grow again after the banding formation. During the initial transition lamellar growth, the relationship between the square lamellar spacing, γ₂, and the distance from, the banding, d, can be described by the following equation: γ₂ = K [1-exp(A.d)] where K and A are constant.     

表面氧化层对TiMn1.25Cr0.25储氢合金活化性能的影响

通过TiMn1.25Cr0.25合金粉活化前在空气中暴露不同的时间,探讨了表面氧化层的形成对其活化性能的影响。活化测试结果表明：合金的活化难度随着合金在空气中暴露时间的延长而加大。俄歇电子能谱(AES)结果表明,在空气中暴露后的合金表面形成了一层大约6nm-10nm厚的表面氧化层,正是这层氧化层的形成加大了合金的活化难度。扫描电镜(SEM)结果表明合金的活化过程与合金的碎化有着密切的联系。     

Stability of austenite in chrome-nickel stainless steel and susceptibility to corrosion cracking

Conclusions The susceptibility to corrosion cracking of austenitic chromium-nickel steels does not depend on the occurrence of the transformation in the process of deformation.Translated from Metallovedenie i Termicheskaya Obrabotka Metallov, No. 3, pp. 73–75, March, 1967.     

用PID控制弧焊逆变电源的试验研究

本文介绍了对逆变电源进行数字PID控制的原理和方法,分析了采样周期、PID参数及不同的焊接工况对控制特性的影响。试验表明,只要恰当地选择PID(或PI)参数,不仅能实现高精度的恒流控制,而且能使系统的动态性能显著提高。