DISTRIBUTION AND EFFECT OF Ce IN RE BEARING DUCTILE IRON

The dependence of nodularization of graphite upon Ce content in RE bearing nodular castiron,prepared by directional solidification,has been investigated by electrolyticextraction-radioisotope assay analysis of Ce in each phase of the iron together withmeasurement of nodulized graphite.Results show that the Ce occurs mainly as alloyed form.In the graphite phase,the Ce content is believed to be characterization of nodularization.Thegraphite would completely nodulized only the Ce is over a certain content in graphite phase.     

接触疲劳过程中的诱发相变和冷作硬化SCIEI

研究了三种丝杠钢的接触疲劳性能。利用TEM和背散射Mossbauer谱研究了三种钢在接触疲劳前后的显微组织结构;测量了接触区中心线下显微硬度随层深的变化。结果表明:接触应力诱发A_R→M相变,并导致一定深度的冷作硬化。讨论了诱发相变和冷作硬化对接触疲劳性能的影响。     

MICROSTRUCTURE STUDY OF CONSTITUENT PHASES IN 2024 SERIES Al ALLOYS

X-ray microanalysis,convergent beam electron diffraction(CBD)and selected area electrondiffraction(SAD)studies on the structures and compositions of the constituent phases in2024 series Al alloys have been conducted.Partial substitution of alloying elements is found tooccur in all the constituent phases,which cause small deviations from the stoichiometric com-positions reported in these ternary compounds.The dominant phase is α-Al_(12)(FeMn)_3Si whichhas a body center cubic crystal structure with the Im■ space group and a=1.25 nm.The nextdominant phase is Cu_2FeAl_7 which has a primitive tetragonal crystal structure with theP4/mnc space group and a=0.6336 nm,c=1.487 nm.The minor phase is α'-Al_(12)Fe_3Si hav-ing α primitive cubic crystal structure with the Pm■ space group and α=1.27 nm.     

GRAIN SHAPE EFFECT IN SUPERPLASTIC DEFORMATION

The method controlling grain shape in TMT processing and the effect of grain shape on char-acteristic parameters in superplastic deformation were discussed.The accommodation velocityof grahl boundary sliding,which is the dominant mechanism in superplastic deformation,andthe contribution of each mechanism to the total strain,as influenced by grain shape,were ana-lyzed.Grain shape has been shown to be an essential structural factor for superplasticity.Thenan analysis was made about the effect of grain shape on the region transition strain rate sothat a new concept,critical aspect for superplasticity,was worked out.These predictions werecompared with the measured results in an Al-Zn-Mg alloy.     

CHARAC TERIZATION OF TiAl POWDER PRODUCED BY MECHANICAL ALLOYING

The microstructure,alloying reaction and sintering behavior of the powder produced by Mechanical Al-loying(MA)for 8 h from 64 wt.-% Ti powder and 36 wt.-% Al powder were studied by scanning electronmicroscopy,optical microscopy,X-ray diffractometry,differential scanning calorimetry(DSC)and dilatometry.The mechanically alloyed powder partictes are Ti-Al composite particles.Thus,titanium aluminides can formeasily in the powder through diffusion during heat treatment.It is shown that the sintering behavior of this pow-der,different from the behaviors of TiAl alloy powder and mixed powder of 64 wt.-% Ti powder and 36 wt.-%Al powder,changes from expansion at temperatures below 1000℃ to shrinkage at temperatures above 1000℃.Homogeneously alloyed TiAl material with a density over 96% of the theoretical density can be produced fromthe mechanically alloyed powder by compaction-sintering.     

GM模型的几何性质及统计检验

以空间向量几何理论为基础，详细地分析了Ｇａｕｓｓ－Ｍａｒｋｏｖ线性模型的几何性质；在实现了模型图形化描述的基础上，利用各解向量的几何及统计性质构造出了不同情形下的统计检验方法和相应的检验统计量，为全面、深入地研究和灵活运用该模型提出了一种简洁直观的数学方法     

扫描速度对硼铸铁气缸套表面钨极氩弧硬化效果的影响

研究了钨极氩弧扫描速度对硼铸铁表面硬化效果的影响规律。结果表明：扫描速度增加,硬化层宽度、深度减小,而硬度提高,裂纹率增大；硬化层硬度沿层深的分布是从表及里由高而低,在过渡区下降缓慢；沿层宽的分布是层中心最高,向两侧逐渐降低,直至硼铸铁基体达到最低值；在保证不出现裂纹的条件下,硬化层表面的最高硬度值可达61．4HRC,硬化层最高显微硬度值可达1156．4HV0．1；硼铸铁材料采用氩弧热源淬火时,淬硬层与基体之间过渡区明显,硬化区组织为莱氏体,过渡区为马氏体、残余奥氏体和少量石墨。     

THERMODYNAMICS ON THE SELECTIVE OXIDATION OF ELEMENTS IN MOLTEN MATTE AND METALS

总结讨论了熔锍及熔融金属中元素选择性氧化的行为,举出镍锍中 Ni 与 S,铁液中 Cr,V,Nb,Mn 或 P 与 C 作为应用的实例.利用热力学分析提出氧化的转化温度的概念,并指出二步及一步计算该温度的方法.在排除新相生成的晶核能的条件下,氧化的转化温度与氧的存在形式(无论是气态 O_2,溶于金属液中的[O]或炉渣中的 FeO)以及氧的压力或活度无关,而只决定于参加反应的物质及产物的本质及活度(压力).同时,转化温度不是一成不变的温度,而是随着熔池组成的改变而不断地在变化.降低气体氧化产物的分压将有助于降低氧化的转化温度.理论计算的转化温度可提供使熔池中一个元素的优先氧化而使另一元素保留不变的最佳条件.小型实验和工业上实践证明,转化温度的概念可以成功地控制吹炼操作,作到按意图进行选择性氧化.影响熔池内元素氧化顺序的动力学因素也作了简略的分析.对镍锍脱 S、不锈钢脱 C 以及高碳锰铁降 C 的吹炼,熔池温度永远要高于相应熔池组成的转化温度.而对铁水脱 Cr 和铁水提 V 或 Nb,熔池温度则应保持低于相应熔池组成的转化温度.P,C 在铁水中的氧化顺序,除与转化温度有关外,还取决于熔渣组成以及 CO 承担的压力.     

晶闸管式等离子弧切割机的使用与维修

本文介绍了晶闸管式等离子弧切割机的操作原理、使用和维修技术。     

Zr对Cu—Zn—Al形状记忆合金相变的影响

采用示差扫描热分析(DSC)、X射线衍射及透射电镜,研究了Zr对Cu-Zn-Al合金高温相变、马氏体正逆转变以及形状记忆效应的影响。结果表明,添加Zr0.35wt-％时,能有效地抑制α,γ相析出,促进β_2→DO_3→18RM转变。(M_s-M_f)及(A_s-A_f)温度区间较窄,马氏体相变激活能最低,马氏体变体间界面的可动性好,形状记忆效应最佳。