充填料浆的流动特性及强度特性对矿山充填质量有着重要影响。为研究外加剂对锡尾矿充填料浆流动特性及充填体抗压强度的影响规律,选用混凝土复合泵送剂、液体早强剂开展了不同添加量条件下充填料浆塌落度、扩展度,以及3、7、28 d充填体单轴抗压强度试验。结果表明：复合泵送剂的添加大幅增加了锡矿尾砂的塌落度及扩展度,有效改善了充填料浆的流动特性。泵送剂在改善充填料浆流动性的同时会影响充填体的强度,针对锡矿全尾砂充填料浆泵送剂较为合理的添加量范围为0.5%~0.8%。早强剂对锡矿尾砂充填体早期强度影响显著,添加后充填体前期抗压强度大幅度增大,同时对后期充填体抗压强度影响较小,针对锡尾矿充填料早强剂较为合理的添加量范围为0.05%~0.15%。     

基于激光三维扫描的人体特征尺寸测量

提出了一种利用三维人体点云数据测量人体关键尺寸的方法。应用线结构光激光三维扫描仪对特定站姿的人体进行扫描,获得完整三维人体点云。根据人体视线和脚尖的同向性及两腿的自然分开特征,对点云进行方位调整,使人体朝向z轴正方向。利用手动删除和最大连通域删除相结合删除噪声点。确定人体的6个特征点和20个特征平面,分别应用对应截面y坐标差值法测量长度尺寸,凸壳法测量截面周长,测量了34个人体关键长度和周长,对影响测量精度的因素进行了分析。结果表明,典型尺寸测量误差小于3%,可满足人类工效学等领域快速测量人体特征尺寸的要求。     

返修对铝合金疲劳性能及其阳极氧化膜性能的影响

对比分析了2024和7150铝合金阳极氧化返修次数对膜层结构、耐蚀性及基体疲劳性能的影响。结果表明,返修2次对两种铝合金阳极氧化膜耐蚀性的影响不大,但7150铝合金的疲劳性能有所降低。     

钨、石墨阴极等离子弧制备碳纳米管

为研究两种电极（钨、石墨）对碳纳米管形成的影响,用直径为2 mm钨棒和直径为3 mm石墨棒作阴极,石墨基板作阳极,形成惰性气体保护下的直流等离子弧制备体系。对60～140 A电流加热下的产物进行扫描电镜、XRD分析。结果表明：碳纳米管数量随电流变大先增后减,当电流为120 A时,以石墨为阴极的等离子弧作用处产生大量的管状结构,直径约为10～20 nm,以钨为阴极的作用处未产生明显的管状结构。为阐明钨、石墨作为等离子弧时,不同物质的特性对碳纳米管形成的影响规律,基于第一性原理计算钨和石墨的功函数,分别为4.68、5.28 eV,说明石墨作阴极时,电子在轰击阳极过程携带到阳极的逸出功比钨极大,导致阳极蒸发效率高,因此石墨阴极产生碳纳米管的效率高于钨极。     

新疆马铃薯种薯综合保鲜技术的研究

对新疆马铃薯种薯进行了贮藏研究,确定了最佳贮藏条件,并对贮藏过程中的干物质、淀粉、还原糖、蛋白质和Vc含量变化进行了分析.结果表明:最佳贮藏条件是低温3～5 ℃ 套袋处理,在此条件下贮藏的马铃薯失重率、腐烂率和发芽率均最低.贮藏过程中还原糖含量的变化始终遵循着淀粉-还原糖-淀粉的可逆动态平衡;随着贮藏时间的延长,马铃薯Vc含量逐渐降低;蛋白质、干物质含量变化不明显;淀粉含量呈先下降,到了末期有所回升的趋势.     

连续炼铜环集烟气处理系统升级改造生产实践

烟台国润铜业有限公司采用富氧侧吹熔炼+多枪顸吹连续吹炼+火法阳极精炼连续炼铜生产工艺,为应对新的环保标准,对原有环集烟气处理系统也进行了工艺升级改造.根据公司现有设备基准排气量较低的现状,采取了在阳极炉工艺采用稀氧燃烧技术、将阳极炉氧化期烟气分流到制酸净化入口、将顶吹炉渣口烟气送到侧吹炉烟道、改造烟道系统、调整负压分配...     

Influence of Bath Composition on Magnetic Properties of Electrodeposited Co-Pt-W Thin Films

Effect of bath composition （[Co^2＋]/[-Pt^Ⅳ ] and [-WO4^2- ], [cit^-]） and pH on the magnetic properties of electrodeposited Co-Pt-W thin films has been investigated. Electrodeposited Co-Pt-W thin films exhibited strong perpendicular magnetic anisotropy when the ratio of [-Co^2＋ ] to [-Pt^Ⅳ ] was 10 ; cathode current efficiency and perpendicular magnetic anisotropy showed little variations when [WO4^2- ] was lower than 0. 1 mol/L, but perpendicular magnetic anisotropy had strengthened when [WO4^2-] was over 0. 1 mol/L, which could be explained by the fact that the hydrogen evolution could produce pores as magnetic domain pinnings; citrate as complexing reagent can promote the polarization of [Co^2＋] and [Pt^Ⅳ]. As a result, the equilibrium electrode potentials of cobalt and platinum moved to negative direction, which led to the co-deposition of Co, Pt, and W. It was also found out that the as-deposited Co- Pt-W hard magnetic thin films were very homogeneous, smooth, and had the maximum coercivity for the bath pH 8. 5 and the concentration of citrate 0. 26 mol/L.     

短距离通信中的塑料光纤无源器件技术

阐述了塑料光纤的真正优势在于其器件和连接的低价与便捷.着重介绍应用在短距离通信中的塑料光纤无源器件的研究进展,包括塑料光纤连接器、耦合器、塑料光纤放大器、塑料光纤光栅等.分析比较各种器件的技术特点,并指出今后面临的问题与挑战.     

不锈钢分离膜在浓缩果汁生产中的应用研究

采用非对称不锈钢分离膜在不同操作压力下对原果汁进行过滤,研究果汁中可溶性固形物含量、色值、浊度等参数的变化。研究表明:与原果汁相比,过滤后果汁中不含果胶和淀粉,果汁中的可溶性固形物含量最大损失为4%,果汁的色值(T440)可达40以上,透光度(T625)可达80以上,浊度(NTU)小于1。将非对称不锈钢分离膜引入果汁生产,替代传统的果汁生产技术中酶解工艺,其意义是十分明显,非对称不锈钢分离膜过滤在果汁行业具有很大的市场。     

聚丙烯腈纤维对引气混凝土抗冻性的影响

采用快速冻融法,以质量变化和相对动弹性模量作为混凝土抗冻性能的评定指标,研究了聚丙烯腈纤维在三个体积掺量0.07%、0.1%、0.13%时对C30、C45和C60引气混凝土抗冻性的影响,其中引气混凝土含气量为4%.结果表明掺加聚丙烯腈纤维的引气混凝土的冻融破坏形态为表面剥落破坏,纤维混凝土在冻融作用下的内部损伤减轻.掺加聚丙烯腈纤维的C30、C45引气混凝土的抗冻性得到了很大的改善,纤维体积掺量为0.1%时,抗冻性最好;但聚丙烯腈纤维对高强度等级的C60引气混凝土的抗冻性提高幅度不明显.