Two-step pyrolytic engineering to form porous nitrogen-rich carbons with a 3D network structure for Zn-air battery oxygen reduction electrocatalysis

It is of great urgency to design inexpensive and high-performance oxygen reduction reaction (ORR) electrocatalysts derived from biowastes as substitutes for Pt-based materials in electrochemical energy-conversion devices. Here we propose a strategy to synthesize three-dimensional (3D) porous nitrogen-doped network carbons to catalyze the ORR from two-step pyrolysis engineering of biowaste scale combined with the use of a ZnCl₂ activator and a FeCl₂ promotor. Electrochemical tests show that the synthesized network carbons have exhibited comparable ORR catalytic activity with a half-wave potential (~0.85 V vs. RHE) and outstanding cyclical stability in comparison to the Pt/C catalyst. Beyond that, a high electron transfer number (~3.8) and a low peroxide yield (<7.6%) can be obtained, indicating a four-electron reaction pathway. The maximum power density is ~68 mW cm^?2, but continuous discharge curves (at a constant potential of ~1.30 V) for 12 h are not obviously declined in Zn-air battery tests using synthesized network carbons as the cathodic catalyst. The formation of 3D porous structures with high BET surface area can effectively expose the surface catalytic sites and promote mass transportation to boost the ORR activity. This work may open a new idea to prepare porous carbon-based catalysts for some important reactions in new energy devices.     

Photopolymerization synthesis of polyacrylic acid dispersant with methoxysilicon end groups and its application in a nano‐SiO2 aqueous system

In order to improve the dispersity and stability of the nano‐SiO₂ aqueous system with high solid content, a kind of polyacrylic acid dispersant with methoxysilicon end groups (KH590‐PAA) was synthesized by photopolymerization of acrylic acid (AA) initiated with (3‐mercaptopropyl)trimethoxysilane (KH590). After adding KH590‐PAA into the nano‐SiO₂ aqueous dispersion system (20 wt% solid content), the viscosity and the curing time of the system were measured with a rotational viscometer and the inverted bottle method. Moreover, the dispersion mechanism of KH590‐PAA for the nano‐SiO₂ aqueous system was researched by measuring the adsorption capacity, the particle size and the zeta potential of the nanoparticles with a conductivity meter, dynamic light scattering, SEM and TEM, respectively. The results showed that the methoxysilicon groups in KH590‐PAA could react with hydroxyl groups on the surface of nano‐SiO₂ in the process of stirring, which enhanced the adsorption capacity of the dispersant and then increased the surface charge of the particles. Therefore, electrostatic repulsion and steric hindrance effects between the SiO₂ nanoparticles could be further enhanced by adding the KH590‐PAA dispersant, and then the nano‐SiO₂ aqueous system exhibited better dispersity and stability. Besides, the dispersion properties of SiO₂ nanoparticles in water were closely related to the addition amount and the molecular weight of the KH590‐PAA dispersant. © 2018 Society of Chemical Industry     

餐饮废油生物柴油低温流动性的改进研究

使用气-质联用仪测定餐饮废油生物柴油(WCME)和-10号柴油(-10PD)的组成,使用冷滤点试验器和运动黏度试验器测定WCME的低温流动性,同时使用调合、添加低温流动性改进剂的方法改进WCME的低温流动性。实验结果表明,WCME主要由饱和脂肪酸甲酯和不饱和脂肪酸甲酯组成,质量分数分别为27.63%和71.81%;WCME冷滤点为0℃,运动黏度(40℃)为4.41mm2/s;WCME与-10PD调合后,冷滤点降低,其中B20的冷滤点最低,为-13℃,运动黏度随着WCME的体积分数的减少,逐渐接近-10PD的运动黏度。通过添加低温流动性改进剂,WCME,B10,B20的冷滤点分别从0,-8,-13℃降至-4,-26,-25℃。     

离子液体中α,β-不饱和化合物的绿色合成

芳香醛和活泼亚甲基化合物为原料,在离子液体中进行Knoevenagel缩合反应。本工艺避开了传统方法中在加入催化剂的有机溶剂中进行Knoevenagel缩合反应的步骤,采用离子液体为反应提供环境和催化,具有操作简单、成本低、对设备无特殊要求和环境友好的优点。