Preparation of flexible polyhedral particles via concentrated emulsion templating polymerization

This paper presents recent efforts on the preparation of flexible polyhedral particles via concentrated emulsion templating polymerization in which the hydrophilic monomer (acrylamide) and hydrophobic monomer (butyl acrylate) are polymerized simultaneously in the continuous and dispersed phase, respectively. Such templating polymerization has been enhanced in our systems owing to the introduction of acrylamide monomer and their higher polymerization rate in continuous phase as compared with butyl acrylate in dispersed phase. Diffusion between the different phases was also inhibited. Furthermore, the stability of the concentrated emulsion and the molecular weight of the produced poly(butyl acrylate) were found to be significantly affected by the amount of redox initiator. The morphology of the particles could be controlled by varying the volume fraction of the dispersed phase and the polyhedral particles were achieved at higher volume fraction. Copyright © 2005 Society of Chemical Industry     

In-Situ observation on microfracture behavior ahead of the crack tip in 63Sn37Pb solder alloy

in-situ transmission electron microscopy (TEM) tensile tests on as-cast and aged 63Sn37Pb solder alloys were conducted, and the fracture behavior in nanometer scale ahead of the crack tip was inspected and discussed. Results show that the fracture was completed by connecting the discontinuous cracks or voids. Dislocation behavior was concentrated along the grain boundaries for as-cast samples, and displayed mainly as dislocation climb. The crack was intergranular dominated under the lower strain rate. While remarkable mutual dislocation emission was detected in the aged solder. Transgranular cracks were dominant in the fractured area, and they propagated by linking up with the nanometer scale cracks ahead of the crack tips under the effective promotion of the inverse dislocation emission. At the same time, the partial interphase or intergranular cracks in the thinned area were also found. Under this condition, a new critical stress intensity factor K _c ^′ to define the mutual dislocation emission was proposed.     

On structural and high temperature electrochemical properties of ZrO2 thin film coating on Zr metal produced by carbonate melt

Melt of NaCO₃ can favor oxidation of Zr to form ZrO₂ thin film on Zr surface, which is used to make Zr/ZrO₂ oxidation/reduction electrode of pH sensor for testing elevated temperature aqueous solutions. Using SEM, EPMA, XPS, EXAFS and HRTEM, we found that ZrO₂ film is tightness and solid with 20 μm thickness composed by nanometer-sized monoclinic crystals. Zr/ZrO₂ interface is characterized of zoning structure according to topography and chemical composition in five zones: oxygen-rich ZrO₂, ZrO₂, oxygen-rich Zr metal, oxygen-bearing Zr and Zr from outmost to center. Melt oxidation process of Zr involved oxidation time, air and temperature. The air is important effect on structural and electrochemical properties of ZrO₂ thin film for making elevate temperature electrochemical sensor. If oxygen air largely presented in carbonate melting process, ZrO₂ thin film is not tightness and not for oxidation/reduction electrode.     

Development of polyurethane elastomer composite materials by addition of milled fiberglass with coupling agent

Polyurethane elastomer composites were developed using milled fiberglass and their mechanical properties were studied. In particular, the organically chemical treatment of the milled fiberglass was investigated in detail. It was demonstrated that both strength and toughness of the resulting elastomer composites were improved considerably with the addition content of fiberglass. Furthermore, it was indicated that the optimal properties can be achieved by the proper addition of milled fiberglass that was chemically treated using coupling agent.