Corrosion of MgO—MgAl2O4 Spinel Refractory Bricks by Calcium Aluminosilicate Slag

Microstructural analysis of MgO—MgAl₂O₄ refractory bricks corroded at 1400–1450°C by calcium aluminosilicate slag reveals secondary spinel, monticellite, merwinite, and MgO as microscopic corrosion products, generally forming in this sequence as the brick is penetrated. The secondary spinel forms an incomplete layer close to (but not at) the MgO grain. Thermodynamic calculations are used to support a detailed model of the corrosion mechanism.     

Effect of microstructures on dielectric breakdown strength of sintered reaction-bonded silicon nitride ceramics

Silicon nitride (Si₃N₄) was prepared from silicon by a sintered reaction-bonded silicon nitride method using yttria and magnesia as sintering additives. Post-sintering (PS) of nitrided compacts was carried out at 1850°C under a nitrogen pressure of 1 MPa. Effect of PS time on microstructure and dielectric breakdown strength (DBS) of the prepared Si₃N₄ ceramics was evaluated. The DBS was measured using specimens with four different thicknesses (0.30, 0.20, 0.10, and 0.05 mm) in order to examine the thickness dependence. The porosity of the sintered Si₃N₄ decreased by prolonging the PS time, and the full density could be achieved at the PS time of over 6 h. After full densification, rod-like β-Si₃N₄ grains grew up, and their maximum grain size increased from 45.1 to 154.7 μm by prolonging the PS time from 6 to 48 h. The DBS of the thick Si₃N₄ substrates (0.30 mm) showed little variation from 35.4 to 47.0 kV/mm, regardless of the PS time. On the other hand, that of the thin ones (0.05 mm) dramatically decreased from 99.5 to 9.8 kV/mm with increased the PS time from 6 to 48 h. Because the DBS sharply decreased at the thin substrate sintered for longer time in which some large-elongated grains might span the substrate thickness-wise throughout, it was inferred that the interface between β-Si₃N₄ grains and grain boundary phase/intergranular glassy films might be a path of the dielectric breakdown.     

Preparation of Aluminum Nitride–Silicon Carbide Nanocomposite Powder by the Nitridation of Aluminum Silicon Carbide

Aluminum nitride (AlN)–silicon carbide (SiC) nanocomposite powders were prepared by the nitridation of aluminum-silicon carbide (Al₄SiC₄) with the specific surface area of 15.5 m²·g⁻¹. The powders nitrided at and above 1400°C for 3 h contained the 2H-phases which consisted of AlN-rich and SiC-rich phases. The formation of homogeneous solid solution proceeded with increasing nitridation temperature from 1400° up to 1500°C. The specific surface area of the AlN–SiC powder nitrided at 1500°C for 3 h was 19.5 m²·g⁻¹, whereas the primary particle size (assuming spherical particles) was estimated to be ∼100 nm.     

Oxidative coupling of methane over LaCoO3−δ-based mixed oxides

The catalytic activity of LaCoO_3–-based mixed oxides for the oxidative coupling of methane has been tested by TPR and cyclic reaction. Characterization has been done by XRD, TGA and Mössbauer spectrometry. It is likely that the perovskite-crystal structure containing hypervalent metal ions has an important role and that unique structural oxygen species in the perovskite contribute to the partial oxidation of methane.     

Copolymerization of Vinyl Chloride and Ethylene with Cp<Superscript>*</Superscript>Ti( OCH<Subscript>3</Subscript>)<Subscript>3</Subscript>/MAO Catalyst

Summary Copolymerization of vinyl chloride (VC) and ethylene with Cp^*Ti( OCH₃)₃/MAO catalyst was investigated. The Cp^*Ti( OCH₃)₃/MAO catalyst initiated the copolymerization of VC with ethylene, although the copolymer yields were low. In the ¹³C NMR spectra of the copolymers, the peaks based on junction part between VC and ethylene was observed, but the signals were small. From DSC measurement of the copolymers, only one glass transition temperature was observed. Thus, it is clear that the copolymerization with Cp^*Ti( OCH₃)₃/MAO catalysts gave the copolymer, and the copolymer consisting of block sequence rather than random copolymer. Received: 13 November 2002/Revised: 6 January 2003/Accepted: 10 January 2003 Correspondence to Kiyoshi Endo     

Processing and Tribological Properties of Si3N4/Carbon Short Fiber Composites

Si₃N₄/carbon fiber composites were fabricated using several types of fiber. All the composites had higher fracture toughness compared with monolithic Si₃N₄ ceramics. Tribological properties were investigated by a ball-on-disk method under unlubricated conditions. The composite containing fibers with a high orientation of graphite layers and high graphite content indicated a low friction coefficient. It was identified, by Raman spectroscopy, that graphite was transferred from the composite to the Si₃N₄ ball of the counterbody during the wear test. This transferred layer was effective for producing the low friction behavior of the composite.     

Efficacy of Chemical Mimicry by Aphid Predators Depends on Aphid-Learning by Ants

Chemical mimicry is an effective strategy when signal receivers recognize and discriminate models by relying on chemical cues. Some aphid enemies mimic the cuticular chemicals of aphids through various means thus avoiding detection and attack by aphid-tending ants. However, because ants have been reported to learn the chemical signatures of aphids in order to distinguish the aphids, the efficacy of chemical mimicry is predicted to depend on the experience of the ants that had tended aphids. The present study tested this hypothesis using two predator species: larvae of the green lacewing Mallada desjardinsi, and larvae of the ladybeetle Scymnus posticalis. Lacewing larvae carry the carcasses of aphids on which they have preyed upon their backs, and these function via chemical camouflage to reduce the aggressiveness of aphid-tending ants toward the larvae. Ladybeetle larvae reportedly produce a covering of wax structures, and their chemicals appear to attenuate ant aggression. We examined whether the behavior of the ant Tetramorium tsushimae toward these predators changed depending on their aphid-tending experience. Ants moderated their aggressiveness toward both predators when they had previously tended aphids, indicating that chemical mimicry by both aphid predators is dependent on previous experience of the ants in tending aphids. Chemical mimicry by the predators of ant-tended aphids is therefore considered to exploit learning-dependent aphid recognition systems of ants.     

Fabrication and Mechanical Properties of Si3N4/Carbon Fiber Composites with Aligned Microstructure Produced by a Seeding and Extrusion Method

Si₃N₄/carbon fiber composites have been produced with and without seeding by an extrusion and sintering process. In both cases the carbon fibers were aligned along the direction of extrusion, but the Si₃N₄ grains were only aligned in the seeded material. The mechanical properties of the specimens showed anisotropy with respect to the grain alignment, with both strength and toughness being highest in the direction parallel to the extruding direction. In this direction the seeded specimen, where both the Si₃N₄ grains and the carbon fibers were aligned, showed both higher fracture toughness and higher fracture strength than the nonseeded specimen where only the fibers were aligned.     

Highly Transparent Lu-α-SiAlON

Novel Lu-α-SiAlON ceramics were produced by hot pressing mixtures of Si₃N₄, Lu₂O₃, AlN, and Al₂O₃ at 1950°C for 2 h in a nitrogen atmosphere. The resultant SiAlON was fully dense and possessed a uniform, equiaxed microstructure with a grain size of ∼1 μm, which resulted in a high hardness of >19 GPa. In addition to high hardness, the sample showed very high optical transparency in the visible light region, with >70% transmission at higher wavelengths. This high transparency was attributed to the uniform, dense microstructure and lack of residual grain-boundary phase.     

Enantioselective addition Of diketene to aldehydes promoted by chiral schiff base—titanium alkoxide complex. Application to asymmetric synthesis of potential inhibitors of HMG coenzyme reductase

Highly enantioselective addition of diketene to aldehydes was achieved by using novel Schiff base—titanium alkoxide complexes. Up to 92% ee of 5-hydroxy-3-oxoesters was obtained. This procedure provides an efficient method for the asymmetric synthesis of potential inhibitors of HMG coenzyme reductase.