Preparation of CaO granules using the granulation method

ABSTRACT

Improving the hydration resistance of CaO particle in manufacturing and application of free CaO-containing materials has practical significance. In this study, CaO granules was made from Ca(OH)₂ particles, which were fabricated by the granulation method. The results showed that the hydration resistance of the CaO granules which was prepared under 1700?r?min^?1 was the best, the CaO granules was sintered well in calcination process, the shell of CaO granules was relatively dense, which improves the hydration resistance of CaO granules, and the rate of hydration weight increment was 0.58% after placed in the air for 20 days under a temperature of 10–14°C and a relative humidity of 57–81%.     

基于图像增强的去雾快速算法的FPGA实现

基于图像增强方法，本文提出了一种使用亮度映射的图像去雾快速算法。此算法通过调整室外多雾场景图像的对比度，提高了雾中物体的辨识度。算法的复杂度低、处理延迟小，实时性高，利于FPGA的实现。实现时不需外存储器，延时为ns级，并提供了强度调节接口，以适应较广的应用环境。     

A dense and compact laser cladding layer with solid metallurgical bonding significantly improved corrosion resistance of Mg alloy for engineering applications

Although Mg alloy attracts great attention for engineering applications because of high specific strength and low density, low corrosion resistance limits its extensive use. In this study, Mg–Al–Zn–Mn alloy was treated via a laser cladding process to generate a dense and compact laser cladding layer with solid metallurgical bonding on the substrate for improving corrosion resistance, effectively hindering the corrosion pervasion into Mg alloy. The corrosion current density declined from 103 μA/cm² for Mg alloy to 13 μA/cm² for the laser cladding layer in NaCl aqueous solution. Moreover, the laser cladding layer was slightly corroded in comparison with Mg alloy in NaCl aqueous solution. Besides, the microhardness of the cladding layer reached a mean value of 170.5 HV, 3.1 times of Mg alloy (56.8 HV) due to the in situ formation of hardening intermetallic phases. Wear resistance of laser cladding layer was also obviously improved. These results demonstrated that the laser cladding layer obviously enhanced anticorrosion property of Mg alloy for engineering applications.     

Formation of a protective layer against corrosion on Mg alloy via alkali pretreatment followed by vanillic acid treatment

Although Mg alloy possesses high specific strength, low density, and good biocompatibility, poor corrosion resistance hinders its further applications. In the present study, an innovative protective layer against corrosion was prepared on the AZ31 Mg alloy via alkali pretreatment followed by vanillic acid treatment. The alkali pretreatment supplied –OH for the AZ31 Mg alloy surface to react with vanillic acid. The vanillic acid treatment played a crucial role in enhancing the corrosion resistance due to the excellent ability to act as a barrier and retard aqueous solution penetration, which effectively isolated the underlying Mg alloy from the corrosive environment. The corrosion current density of alkali and vanillic acid-treated Mg alloy (AZ31V) almost showed two orders of magnitude lower values in comparison with that of the AZ31 Mg alloy, and the corrosion potential of AZ31V Mg alloy increased from −1.41 to −1.25 V. The immersion tests proved that there was no occurrence of severe corrosion. Hence, the alkali pretreatment and vanillic acid treatment may represent a promising method to improve the corrosion resistance of Mg alloy.     

基于DTW改进算法的孤立词识别系统的仿真与分析

传统的DTW算法在进行孤立词语音识别时着重于时间规整和语音测度的计算，而没有对数据的可靠性和有效性进行分析。本文提出了一种改进的端点检测算法，并采用一种改进的DTW算法，在计算机上进行了仿真。实验结果表明采用改进后的DTW算法有效的降低了识别时间和存储数据量，提高了系统性能。     

塔河油田成藏期次的地球化学示踪研究

应用油藏地球化学的方法对塔河油田的成藏期次进行了探讨。塔河油田稠油正构烷烃分布完整,但色谱基线不同程度抬升;原油非烃和沥青质碳同位素偏轻,族组成碳同位素发生倒转;原油中普遍含有25-降藿烷。这些特征表明该区油藏经历了至少两期成藏过程,早期充注原油遭受生物降解作用后又受到高成熟原油充注。塔河油田天然气为典型的油型气,成熟度较高,为成熟—过成熟阶段产物,亦显示了两期充注的特征:早期充注的为典型的原油伴生气,充注时间与后期原油的充注时间相同;晚期充注的为高温裂解气,充注方向为自东向西。因此,塔河油田至少存在着3次油气充注过程。