Effect of particle size on the surface oxidation and flotation behavior of galena particles in lime system

ABSTRACT

In this research, the effect of particle size on the surface oxidation and flotation behavior of galena in the lime system was studied. Coarse (?0.074 + 0.038 mm), intermediate (?0.038 + 0.025 mm) and fine (?0.025 mm) galena particles were used in the experiment. The dissolution tests, flotation tests, and sorption tests were accomplished. Through further analysis by XPS, the effect of particle size and lime was observed. The decrease of mineral particle sizes increased the adsorption ratio of collector and the dissolution of galena, while the hydrophilic product OH^?/Ca(OH)⁺ produced by dissolution occupied the dominant position, which led to the minerals hydrophilic.     

K_2O－CaO－Al_2O_3－SiO_2系统自释釉瓷化学组成的研究

本文从酸度系数着手，证实了Ｋ２Ｏ－ＣａＯ－Ａｌ４Ｏ久－ＳｉＯ２系统中存在自释釉组成，限定了其组成范围，０．６７％＜Ｋ２Ｏ＜１．２８％，１０．６４％＜ＣａＯ＜１３．６２％，１１．５３％＜Ａｌ４Ｏ３＜１５．３２％，７２．７３％＜ＳｉＯ２＜７４．０４％，并讨论了自释釉瓷的性能。     

Formation Mechanisms of Platelet Sr3Ti2O7 Crystals Synthesized by the Molten Salt Synthesis Method

The molten salt synthesis (MSS) method is utilized to synthesize the anisotropic platelet Sr₃Ti₂O₇ (S3T2) single-crystal particles. The aim of this study is to identify the essence of platelet Sr₃Ti₂O₇ crystal growth and guide the synthesis of anisotropic platelet SrTiO₃ crystals as well as various technologically important materials. Based on the results of X-ray diffraction, scanning electron microscopy, and high-resolution transmission electron microscopy, the formation mechanism of platelet Sr₃Ti₂O₇ crystals conforms to a nucleation–structure rearrangement–dissolution–diffusion in situ epitaxial growth mechanism model. First, SrCO₃ reacts with TiO₂ to form submicrometer SrTiO₃ nuclei. Then, most of the nuclei surrounded by salt ions aggregate and rearrange to form a large SrTiO₃ matrix. The structural rearrangement and the subsequent in situ epitaxial growth processes control the morphology, composition, and size of the final Sr₃Ti₂O₇ crystals. In the synthesis process, the conversion between SrTiO₃ and Sr₃Ti₂O₇ is as follows: and the crystallographic orientation relationship between Sr₃Ti₂O₇ and SrTiO₃ in the interface is (100)_S3T2//{100}_ST, (010)_S3T2//{010}_ST, and (001)_S3T2//{001}_ST.     

Two possible emission mechanisms involved in the arc discharge method of carbon nanotube preparation

By investigating the morphologies and microstructures of the cathode deposits prepared by self-sustained arc discharge between graphite rods, we consider that there are two electron emission mechanisms occurring on the cathode: field emission and thermionic emission. The former occurs mainly on the edge of the growing surface, by which we can explain the formation of the outer hard shell of the cathode deposit; while the latter occurs mainly on the growing surface except for the edge area and it is the main cause for the growth of carbon nanotubes.     

无机颜料的表面处理

介绍了无机颜料表面处理的作用及实现途径,并对其作用机理进行了分析,还叙述了表面活性剂的选择和处理方式。     

Electrochemical micromachining of nitinol by confined-etchant-layer technique

The confined etchant layer technique has been applied to fabricate complex three-dimensional microstructures on nitinol for the first time. HF and HNO₃ were locally and simultaneously electrogenerated at the mold surface to etch a nitinol workpiece. NaOH was used as an efficient scavenger to confine the etchant close to the mold. Cyclic voltammetry was employed to study the electrochemical behavior of a Pt electrode in the etching solution in order to choose an appropriate potential for etchant generation on the mold. The thickness of the confined etchant layer was estimated to be several micrometers by inspecting the deviation of the sizes of the etched spots from the sizes of those on the microelectrode. Thus, the composition of the electrolyte could be optimized for better etching precision. By optimizing the composition of the electrolyte, complex microstructures on a Pt-Ir mold bearing the logo “XMU” of Xiamen University were successfully fabricated on nitinol. The etched patterns were approximately negative copies of the mold, and the precision of duplication could easily reach the micrometer scale.     

Polyaniline for corrosion prevention of mild steel coupled with copper

Polyaniline emeraldine base/epoxy resin (EB/ER) coating was investigated for corrosion protection of mild steel coupled with copper in 3.5% NaCl solution. EB/ER coating with 5-10 wt% EB had long-term corrosion resistance on both uncoupled steel and copper due to the passivation effect of EB on the metal surfaces. During the 150 immersion days, the impedance at 0.1 Hz for the coating increased in the first 1-40 days and subsequently remained constant above 10⁹ Ω cm², whereas that for pure ER coating fell below 10⁶ Ω cm² after only 30 or 40 days. Immersion tests on coated steel-copper galvanic couple showed that EB/ER coating offered 100 times more protection than ER coating against steel dissolution and coating delamination on copper, which was mainly attributed to the passive metal oxide films formed by EB blocking both the anodic and cathodic reactions. Salt spray tests showed that 100 μm EB/ER coating protected steel-copper couple for at least 2000 h.     

货架喷塑前处理工艺的选择与应用

介绍了CZ99-03(7)常温锌系磷化剂在货架上的应用,根据货架构件的特点,优化货架喷塑前处理工艺,讨论了影响磷化质量的工艺因素,提出了提高磷化效果的措施以及进一步改进磷化工艺的工艺设计。     

探索行动导向教学法在网络架构课程教学改革中的应用

技工学校是以技术型人才培养为目的的学生能力养成和技能操作的教育基地,为确保人才培养质量,学校需要加强对市场形势的把握和教学改革的控制。行动导向教学法是目前广泛应用于技校和职校教学课堂的、有较好实际作用的教学方法,文章以行动导向教学法为重点,以配置交换机实现VLAN学习任务为案例,在教学方法和手段等几个方面讨论了行动导向教学法在网络架构课程教学改革中的研究与实践。     

Vapor-liquid equilibria in the argon-methane system

Vapor-liquid equilibrium compositions have been measured for the argon-methane system at 115.2°, 123.4° and 137.1°K, by means of a forced-recirculation apparatus. A modified Redlich-Kwong equation of state with the incorporation of a binary interaction constant has been successfully employed to represent the data. Liquid activity coefficients have been evaluated and correlated.