锌再生利用及发展对策探讨

本文简述了我国锌工业生产、消费和再生锌工业发展的现状,指出了我国再生锌工业发展缓慢,技术装备水平低,企业生产规模小等问题。提出了建立规范化的管理制度,在政策上鼓励发展废锌材料的回收利用,加速我国废锌材料的回收利用程度。     

钢筋脆断的原因

对20MnSi Ⅱ级带肋钢筋脆断的原因进行了分析，发现脆断的主要原因是锰含量超上限，使正常轧制条件下出现贝氏体且使组织中铁素体含量大大降低。     

水轮机组高硬度不锈钢止漏环的焊接

通过对刘家峡水轮机转轮止漏环焊接性试验研究，选择出合适的焊接材料，制定了可行的焊接工艺方案，并在实际焊接中取得了良好效果。解决了高硬度不锈钢焊接难点，保证了止漏环拼焊质量，延长了使用寿命。     

电化学扫描探针显微镜在腐蚀电化学研究中的应用

从电化学扫描探针显微镜（ECSPM）的工作原理出发，综述了近几年电化学扫描探针显微镜在腐蚀电化学领域的研究进展，指出电化学扫描探针显微镜在原位，局部腐蚀，腐蚀早期过程等电化学中有重要的应用价值。     

新安江水电站水轮机主轴的焊接

通过对新安江水电站增容改造的9号机组的主轴结构及其焊接工艺研究，设计了合理的焊接坡口，制定了可行的工艺方案，通过实施该工艺，主轴焊接一次成功，为以后同类结构的大轴焊接积累了经验。     

临邑—仪征输油管道腐蚀分析与对策

2003-04-21 调查分析了临邑—仪征输油管道防腐层状况、恒电位仪运行参数等.认为该管道腐蚀的原因是防腐层老化，出现保护死角.并提出了加强管道防腐层检补漏、大修和增设阴极保护装置等措施.     

Strength Analysis of Steam Turbine Diaphragm with a Crack

The diaphragm of steam turbine is one of the main parts of the passage unit for air flowing and the diaphragm of steam turbine is generally made by welding, but during the course of welding, some cracks often have happened, these cracks threaten safety production on the spot, so it is necessary to analyze the strength of steam turbine diaphragm with a crack. For studying its working condition and performance with a crack, the three-dimensional finite element model(FEM) with the software ANSYS 10.0 is established according to the actual working parameters. With the model, the deformation results and stress field results are analyzed and the maximum displacement and stress value are calculated, meanwhile, the maximum stress change with crack depth of steam turbine diaphragm is analyzed. It provides a good foundation for solving the problem in production.     

Robust‐Adaptive Control Strategies for a Time Delay Bioelectrochemical Process Using Interval Observers

The paper addresses the design and the analysis of adaptive and robust‐adaptive control strategies for a complex recycled wastewater treatment bioprocess. The design procedures are developed under the realistic assumptions that the bacterial growth rates are unknown and the influent flow rates are time‐varying and uncertain, but some lower and upper bounds of these uncertainties are known. The proposed control structures are achieved by combining a linearizing control law with an appropriately (asymptotic or interval based) state observer and with a parameter estimator used for on‐line estimation of unknown kinetics. These approaches are applied to a complex time delay bioprocess resulting from the association of a recycling bioreactor with an electrochemical reactor. Numerical simulations are performed in order to validate the proposed algorithms.     

Image blur and energy broadening effects in XPEEM

We report image blurring and energy broadening effects in energy-filtered XPEEM when illuminating the specimen with soft X-rays at high flux densities. With a flux of 2×10¹³ photons/s, the lateral resolution in XPEEM imaging with either core level or secondary electrons is degraded to more than 50 nm. Fermi level broadening up to several hundred meV and spectral shift to higher kinetic energies are also systematically observed. Simple considerations suggest that these artifacts result from Boersch and Loeffler effects, and that the electron-electron interactions are strongest in the initial part of the microscope optical path. Implications for aberration corrected instruments are discussed.