Preparation of CaO granules using the granulation method

ABSTRACT

Improving the hydration resistance of CaO particle in manufacturing and application of free CaO-containing materials has practical significance. In this study, CaO granules was made from Ca(OH)₂ particles, which were fabricated by the granulation method. The results showed that the hydration resistance of the CaO granules which was prepared under 1700?r?min^?1 was the best, the CaO granules was sintered well in calcination process, the shell of CaO granules was relatively dense, which improves the hydration resistance of CaO granules, and the rate of hydration weight increment was 0.58% after placed in the air for 20 days under a temperature of 10–14°C and a relative humidity of 57–81%.     

液压支架立柱拆装机构设计

拆柱机由电动机匹配乳化液泵将电能转化为泵的液压能,带动液压马达回转作为拆装柱的动力。     

Nb和时效时间对热轧中锰TRIP钢中P偏聚的影响

热轧态中锰TRIP钢首先经650 ℃退火2 h,随后在550 ℃进行等温时效热处理,采用场发射扫描电镜(FE-SEM)研究该钢中P的偏聚和时效析出行为的变化情况。结果表明,中锰TRIP钢中P在晶界的偏聚是一种非平衡偏聚现象,临界时间约为50 h,与理论计算结果48 h较为吻合。在局部偏聚区域内,C与P存在共偏聚的关系,即P偏聚量高的地方,C含量也高。而合金元素Nb具有抑制P偏聚的效果,在20~70 h时效时间内,可以相对降低6.57%~19.5%的最大P偏聚量。根据电子背散射衍射(EBSD)菊池线分析,P偏聚量低于2.28at%时,P为固溶状态,高于2.28at.%时,P为析出状态。     

除尘器新型褶式滤筒的结构优化及系列化设计

以新型褶式滤筒为研究对象,选取滤筒褶数N_2、褶夹角θ、褶高h、过滤风速v为影响因子,除尘器压力损失为响应值,基于响应曲面法分析影响因子对压力损失的影响,建立滤筒除尘器压力损失的预测模型并得到滤筒褶皱结构最优参数。以滤筒内径D、筒体高度D_1为标准尺寸,依据相关国家标准设计滤筒筒体部分;以锥体高度D_2、锥体上圆直径D_3为系列尺寸,利用尺寸变化法设计锥体部分;通过Access软件建立滤筒产品数据库。结果表明:当θ=5.2°,N_2=50,v=0.01 m/s,h=0.035 m时,除尘器压力损失最低;当D_1=1 000 mm,D=320 mm时,D_2和D_3最佳值分别为600,130 mm,故采用D_2/D_1=0.6,D_3/D=0.4的比值设计相应滤筒锥体系列。     

Tailoring the electron-blocking layer by addition of YSZ to Ba-containing anode for improvement of ceria-based solid oxide fuel cell

The in-situ fabrication of an electron-blocking layer between the Ba-containing anode and the ceria-based electrolyte is an effective approach in suppressing the internal electronic leakage in ceria-based solid oxide fuel cell (SOFC). To improve the thickness of the electron-blocking layer and to research the effect of the layer thickness on the improvement of SOFC, a Ba-containing compound (0.6NiO-0.4BaZr_0.1Ce_0.7Y_0.2O_3-δ) modified by Y stabilized zirconia (YSZ) was employed as a composite anode in this research. SEM analyses demonstrated that the thickness of the interlayer can be simply controlled by regulating the proportion of YSZ at anode. The in-situ formed interlayer in the cell with the anode modified by 20?mol% YSZ possesses a thickness of 0.9?µm which is more suitable for the cell achieving an enhanced performance.