纳米尺度下结构力学行为因为表面效应和尺寸效应而与宏观尺度下结构力学行为有着本质的不同，分子动力学方法因其能通过原子运动理解结构变形细节而在纳米结构力学行为模型中得到广泛应用，本文综述了近期在纳米丝结构力学研究方面的进展，包括自由弛豫态，应力应变关系，表面效应和尺寸效应，应变率效应等。     

镍基单晶合金枝晶典型区域相成分最优化测算法

建立了用于测算镍基单晶高温合金枝晶典型区域相成分的最优化数学模型.根据电子探针对枝晶典型区域成分的测定结果,运用BFGS拟Newton法及CONSTR约束优化算法,可以计算枝晶各典型区域中γ和γ＇相成分.以镍基单晶合金CMSX-2和CMSX-4为对象,对优化测算结果进行了分析,证实了该方法的可行性.     

APPLICATION OF MAXIMUM ENTROPY METHOD TO CALCULATE RDF OF Ni-P AMORPHOUS ALLOY FROM X-RAY DIFFRACTION DATA

Experiments clarified that application of the maximum entropy method to calculate the RDF(radial distribution function)of the Ni-P amorphous alloy from fewer data of its X-raydiffraction data shows a higher resolution and good consistent with known results.It is be-lieved that this method is available for the analysis of amorphous structure.     

碳离子注入对Ti—6Al—4V合金疲劳寿命的改善

3×10~(17)Cion/cm~2在80keV的能量下注入到Ti-6Al-4V合金中。在应力控制的拉-零试验条件下,发现C~+注入试样的疲劳极限提高了28%。利用扫描电镜、透射电镜和二次离子质谱等研究了试样在注入前后和疲劳前后的表面层微观组织与结构以及注入元素沿表面层深的浓度分布。结果表明,注入层的微观组织中含有大量的辐照损伤并有许多细小的TiC相颗粒;注入与未注入试样的裂纹源在低应力疲劳中出现在亚表面区;注入元素在循环载荷作用下向基体中扩散。     

金属注射成形Ti-6Al-4V烧结坯的力学性能与烧结时间关系

研究了在1260℃烧结时,烧结时间对Ti-6Al-4V烧结坯力学性能的影响.结果表明平均晶粒尺寸为45 μm的氢化-脱氢粉末样品在1 260C烧结3 h～6 h,其相对密度为95.6%～96.7%、拉伸强度648 MPa～686 MPa、屈服强度526 MPa～615 MPa,但延伸率仅小于4%.90%气雾化(晶粒尺寸为32.5 μm)和10%氢化-脱氢混合粉末样品在1 260℃烧结2 h～6 h,其相对密度大于95%、拉伸强度800 MPa～848 MPa、屈服强度712 MPa～762 MPa、延伸率7.4%～9.5%.混合粉末样品的力学性能几乎达到美国ASTM粉末冶金的标准.     

Thermal Shock Property of Al/Ni-ZrO_2 Gradient Thennal Barrier Coatings

THERMAL BARRIER COATINGS can holdbackintrusion of high temperature,high heat to increaseapplied temperature and life of substrate metal parts,and have been applied on heat position of rocket,satellite,aero engine and gas engine"31.But thermalstresses are produced during thermal shock due tomismatch of thermal properties between ceramiccoatings and substrate metal,therefore thermal shockproperties of coatings are very poor.Gradient thermalbarrier coatings make materials gradually chang…     

镍基合金中γ′相界面的强化设计

采用第一原理分子轨道离散变分Xα法，研究在镍基合金中加Ir合金化的作用，以及在镍基合金中存在B，C，N，H，O，P或S时对γ相和γ′相界面结合强度的影响。证明Ir合金化后，使γ相和γ′相的晶格错配度向负值变化，提高键重叠集居数和总键序。在镍基合金中存在的S，P，H，O，N，B或C，对γ－Ni/γ′-Ni3Al相界面结合力有明显影响，其中C，B和N显著增强两相的界面，相反S和P则减弱相界的结合。     

INFLUENCE OF Al ON DUCTILITY IMPROVEMENT BY B IN Ni_3Al ALLOYS

The “order-disorder” model was adopted to calculate the lattice vacancies related to the com- position change in Ni_3Al alloys.A great deal of vacancies,i.e.,the non-stoichiometric vacan- cies,may exist in the Ni_3Al alloys containing Al over stoichiometry,i.e.25 at.-%.This was confirmed by the positron annihilation technique.Therefore,the influence of Al content on the enhancing behaviour of B towards the ductility of Ni_3Al alloys can be understood by the interaction of non-stoiehiometric vacancies and B atoms.     

Nb_2O_5-MnO-SiO_2渣中Nb_2O_5和MnO活度的研究SCIEI

本文利用含NbFe液与Nb_2O_5-MnO-SiO_2渣之间平衡,在1828K温度下应用固体电解质浓差电池方法测定了Fe液中氧的活度,从而计算出渣中Nb_2O_5及MnO的活度,并绘制了Nb_2O_5-MnO-SiO_2三元系的等α_(Nb_2O_5)和等α_(MnO)图。     

表面处理对球墨铸铁接触疲劳性能的影响

本文研究了激光微熔处理和高频感应加热淬火对球墨铸铁表面组织、接触疲劳强度和接触疲劳破坏过程的影响。结果表明,激光处理和高频淬火均可提高球铁的接触疲劳强度,但其接触疲劳破坏过程和形式却不同,前者是由于硬化层与基体间裂纹扩展造成大块深层剥落,后者则是表层裂纹在油楔作用下造成小块浅层脱落。