Highly active sites of low spin FeⅡN4species:The identification and the ORR performance

Over recent years,catalytic materials of Fe-N-C species have been recognized being active for oxygen reduction reaction(ORR).However,the identification of active site remains challenging as it generally involves a pyrolysis process and mixed components being obtained.Herein Fe₃C/C and Fe₂N/C samples were synthesized by temperature programmed reduction of Fe precursors in 15%CH₄/H₂and pure NH₃,respectively.By acid leaching of Fe₂N/C sample,only single sites of FeN₄species were presented,providing an ideal model for identification of catalytic functions of the single sites of FeN₄in ORR.A correlation was conducted between the concentration of Fe^ⅡN₄in low spin state by Mossbauer spectra and the kinetic current density at 0.8 V in alkaline media,and such a structure-performance correlation assures the catalytic roles of low spin Fe^ⅡN₄ species as highly active sites for the ORR.     

Control of the particle microstructure during the synthesis of bulk-polymerized transparent methacrylate-acrylonitrile-butadiene-styrene resin

A series of methacrylate-acrylonitrile-butadiene-styrene (MABS) resins was prepared using bulk polymerization. The polarity of the continuous phase and the compatibility of two phases were changed by adjusting the methyl methacrylate (MMA) content, choosing values that were close to styrene-butadiene rubber solubility value. The possibility of controlling the microstructure of the MABS resin by changing the polarity of the components and the compatibility of two phases was assessed. The dynamic mechanical analysis shows that the compatibility of two phases varies with the MMA content. The morphological analysis shows that increasing MMA contents results in a gradual decrease in the sub-inclusion structure with a network skeleton of rubber particles, and that all the particles become solid rubber when the MMA content reaches 75%. The sub-inclusion structure reappears but does not have a network skeleton when the MMA content is 90%. The impact strength and morphological analysis indicate that the solid rubber particles and the sub-inclusion structure with a network skeleton provide excellent toughness, while the sub-inclusion structure without a network skeleton does not. In contrast, the transmittance of the ABS resin first increased and then decreased with increasing MMA content.