Element doping into the Cu2ZnSn(S,Se)4 (CZTSSe) absorber is an effective method to optimize the performance of thin film solar cells. In this study, the Cu2InxZn1-xSn(S,Se)4 (CIZTSSe) precursor film was deposited by magnetron cosputtering technique using indium (In) and quaternary Cu2ZnSnS4 (CZTS) as targets. Meanwhile, the In content was controlled using the direct current (DC) power on In target (PIn). A single kesterite CIZTSSe alloy was formed by successfully doping a small number of In3+ into the main lattice of CZTSSe. The partial Zn2+ cations were substituted by In3+ ions, resulting in improving properties of CZTSSe films. Morphological analysis showed that large grain CIZTSSe films could be obtained by doping In. The well-distributed, smooth, and dense film was obtained when the PIn was 30 W. The band gap of CIZTSSe could be continuously adjusted from 1.27 to 1.05 eV as PIn increased from 0 to 40 W. In addition, the CIZTSSe alloy thin film at PIn = 30 W exhibited the best p-type conductivity with Hall mobility of 6.87 cm2V?1s?1, which is a potential material as the absorption layer of high-performance solar cells. 相似文献
When solving a mathematical problem, students who do not have sufficient conceptual understanding may perform poorly and exhibit misconceptions. This study was aimed to examine students' conceptual understanding and significant misconceptions when solving number sense‐related problems. An online three‐tier diagnostic test was administered to 125 fifth‐grade students with varied socio‐economic backgrounds in Hong Kong. Only 14.40% of the students exhibited high performance with high confidence, indicating that these students had a profound conceptual understanding of number sense. In addition, the majority of the students (66.40%) did not demonstrate number sense; these students exhibited several significant misconceptions and could solve the questions only by using a rule‐based method or guessing. Accordingly, most students performed unsatisfactorily on number sense‐related problems. This study is imperative in identifying early predictors and provides information for further compatible interventions in the teaching and learning of number sense in Hong Kong in particular and worldwide in general. 相似文献
The Journal of Supercomputing - In the last decade, cloud computing has brought enormous changes to people’s lives. Cloud computing gives a client-driven computational model. In this case,... 相似文献
We present a new scheme for visibly-opaque but near-infrared-transmitting filters involving 7 layers based on one-dimensional ternary photonic crystals, with capabilities in reaching nearly 100% transmission efficiency in the near-infrared region. Different decorative reflection colors can be created by adding additional three layers while maintaining the near-infrared transmission performance. In addition, our proposed structural colors show great angular insensitivity up to ±60° for both transverse electric and transverse magnetic polarizations, which are highly desired in various fields. The facile strategy described here involves a simple deposition method for the fabrication, thereby having great potential in diverse applications such as image sensors, anti-counterfeit tag, and optical measurement systems.
Analog Integrated Circuits and Signal Processing - Fault diagnosis of analog circuit is critical to improve safety and reliability in electrical systems and reduce losses. Traditional fault... 相似文献
In this work, we synthesized Se doped MoS2@Ni3S2 with nanosheets coated nanorods structure supported on Ni foam (MoNiSeS). Firstly, MoS2@Ni3S2 (MoNiS) nanorods was synthesized by hydrothermal method. After selenization treatment, MoSe2 successfully formed on the edge of MoS2 nanosheets and particle Ni3S2 transformed into NiSe, in which MoSe2 and NiSe acted as new phase in MoNiSeS. The obtained MoNiSeS only needs a low overpotential of 68 mV to reach the current density of 10 mA cm?2, and has a low Tafel plots of 72.77 mV dec?1 and good electrochemical durability, whose electrochemical activity is much better than that of MoNiS and NiSeS, implying the introduction of Mo and Se is beneficial to improve the electrocatalytic performance of NiS for HER. In addition, the proper amount of Mo source, which has an effect on the morphology of product, has also been investigated. For MoNiSeS, the typical nanosheets coated nanarods expose more active sites and the synergic effects is good to the improvement of the catalytic activity. Meanwhile, WNiSeS has also been prepared using the same method and the corresponding results show that the electrochemical activity of WNiSeS is much better than that of NiSeS, proving the universality of this strategy. 相似文献
A novel AlSiMgAl2O4Al2O3 composite brick was prepared and evaluated in the low vessel of an RH (the initials of Ruhrstahl and Hereaeus) secondary refining furnace; it was characterized by X-ray diffraction, scanning electron microscopy, and energy-dispersive spectroscopy. The results show that after use, the AlSiMgAl2O4Al2O3 composite has a functional gradient with an erosion zone–reinforced zone–original zone phase distribution, in which the phases in the erosion zone (0–1.8?cm) are a Mg-hercynite spinel solid solution, α-Al2O3, and minor amount of Al3Fe5O12. Furthermore, the phases in the reinforced zone (1.8–5.0?cm) are γ-AlON, 21RSiAlON, SiC, Mg0.388Al2.408O4, and α-Al2O3; i.e., the Al and Si in the composite are completely converted into non-oxide reinforced phases. Finally, the phases in the original zone (>5.0?cm) show no change. The reaction mechanism is as follows. During operation, a Mg-hercynite spinel solid solution is formed in the erosion zone due to a reaction between MgAl2O4 and FeO from a refinery operation. Therefore, the slag erosion of the material is improved. The Al and Si metals undergo active oxidation, and 21RSiAlON flakes are subsequently formed from the products of the metastable Al2O(g), SiO(g), and N2(g) in the ambient. The γ-AlON is formed by a carbothermal reduction nitridation of the α-Al2O3 and residual active carbon from the resin binder. The 21RSiAlON and γ-AlON reinforce the composite brick and improve its high temperature performance accordingly. Its service life is 110% that of the magnesia-chrome bricks used in the same period. The reaction model was also established. 相似文献