Irreversible deformation and the superplasticity of a TN-1 alloy during thermal cycling through the martensitic transformations ranges under loading

The influence of the thermal cycling conditions on the thermal-cycling creep of a TN-1 alloy and the related irreversible deformations is studied. The conditions under which an anomalous increase in the irreversible deformations begins are determined. The structural mechanism of the irreversible deformations of an equiatomic alloy is shown to be analogous to the structural mechanism of metal creep at high temperatures: it predominantly has a dislocation character. It is proposed to use the effect of anomalous increase in the deformation of materials with reversible martensitic transformations for forming parts made of these materials at low temperatures.     

基于Cortex-M的嵌入式设备固件更新方法研究

本文提出了一种基于分散加载技术实现Boot程序和用户应用程序在同一个工程编写开发的固件更新方法 .通过编写分散加载规范文件在工程中实现代码存储区分区.为了保证固件更新的稳定性和可靠性,在固件下载过程中引入CRC校验、丢包错包重传等容错技术.实验结果 验证了方法的有效性和可靠性.     

Effects of Prior Annealing on the Spark Plasma Sintering of Nanostructured Y2O3 Powders

The effects produced by annealing Y₂O₃ nanopowders on their spark plasma sintering (SPS) behavior are systematically investigated in this work. It is found that the annealed powders display higher sinterability with respect to the as‐received ones. Indeed, the maximum densification level reached from pristine powders is about 97.5%, whereas density decreases when further increasing either the sintering temperature or the dwell time. In contrast, the density of SPS products obtained from pretreated powder monotonically increases with temperature and processing time, thus leading to fully dense materials in 30 min at 1050°C and 60 MPa. Correspondingly, it is found that the annealing treatment markedly inhibits grain coarsening during SPS. Thus, dense translucent samples with grain size below 100 nm can be attained from annealed powders. On the other hand, white‐opaque specimens with significantly coarser microstructures (up to 1‐μm‐sized grains) are obtained when pristine powders are directly processed under the same sintering conditions. Furthermore, it is observed that the annealing treatment of SPS samples in air allows for graphite contamination removal, whereas no improvement in term of light transmittance is produced.     

强碱三元复合驱色谱分离及其影响因素——以大庆油区喇嘛甸油田为例

三元复合驱油体系中驱油剂的协同效应,会使油水间的界面张力大幅度下降,原油采收率大幅度提高;但三元复合驱油体系的色谱分离现象也会破坏其协同效应和完整性,揭示色谱分离现象及其影响因素对于改善三元复合驱油效果具有十分重要意义。以油藏工程和分析化学理论为指导,以化学分析和物理模拟为技术途径,并以大庆喇嘛甸油田典型区块地质特征和流体性质为研究对象,开展强碱三元复合驱色谱分离现象及其影响因素研究。结果表明,采用前置高浓度聚合物段塞后,可以有效扩大波及体积,但表面活性剂与碱和聚合物之间无因次等浓距增加,色谱分离现象加剧。大庆油区喇嘛甸油田不同区块油水性质差异对色谱分离现象存在影响,原因在于部分重烷基苯石油磺酸进入油相,影响水相中浓度检测值。强碱三元复合驱油体系中表面活性剂与碱和聚合物之间色谱分离程度比较严重,碱与聚合物之间较弱。     

Improvement of dielectric breakdown strength and energy storage performance in Er2O3–modified 0.95Sr0.7Ba0.3Nb2O6-0.05CaTiO3 lead-free ceramics

In this study, 0.95?Sr_0.7Ba_0.3Nb₂O₆-0.05CaTiO₃-x wt% Er₂O₃ ceramics (SBNCTEx; x?=?0–5) were synthesized using traditional solid-state method, and we investigated the microstructure, energy storage properties as well as the relationship between dielectric breakdown strength and interfacial polarization. As compared with pure 0.95?Sr_0.7Ba_0.3Nb₂O₆-0.05CaTiO₃ ceramics, the Er₂O₃ dopants suppressed the grain growth of SBNCTEx, and the doped ones showed the dense microstructure. The secondary phase was found for x?≥?1 according to the EDS results, and the influence of the secondary phase on relative dielectric breakdown strength has also been studied. The dielectric breakdown strength increased from 18.1?kV/mm to 34.4?kV/mm, which is good for energy storage. The energy storage density of 0.28?J/cm³ and the energy storage efficiency of 91.4% were obtained in the SBNCTE5 ceramics. The results indicate that SBNCTE ceramics can be used as energy storage capacitors.     

Thin-Film Nanotechnology for Power Sources

Russian Engineering Research - Thin-film vacuum technology permits the creation of new electrode materials on the basis of a flexible carbon matrix with a highly developed surface. Supercapacitor...     

Preparation and characterization of calcium phosphate cement with enhanced tissue adhesion for bone defect repair

Anti-washout and tissue adhesion properties are essential for the clinical application of injectable bone materials. In this study, we prepared calcium phosphate cement (CPC) with anti-washout and tissue adhesion properties and attempted to build covalent bonds between CPC and the amino groups in bone tissue under a self-regulating pH system in the CPC (acidic to basic). The results of push-out tests demonstrated that a significant enhancement (from 6.42 ± 0.76 N to 61.5 ± 4.09 N) in tissue adhesion was obtained with the addition of 6% (w/w) oxidized sodium alginate (OSA) in CPC. The FTIR, XRD, anti-washout test, XPS, pH test, and SEM results suggested that the synergistic effect of OSA-citric acid (CA) led to the formation of a three-dimensional gel network structure in the CPC, and the Schiff base reaction between aldehyde and amino groups induced adhesion between CPC and the bone tissue. Further, the addition of less OSA had no significant negative effect on the hydration properties of CPC. Our work aims to promote the development of injectable bone material in clinical applications.