掺磁性膨胀石墨水泥浆体的电磁屏蔽效能

将二茂铁与可膨胀石墨混合物在高温下膨化,制备了附着铁氧化物的磁性膨胀石墨.利用同轴法兰法测试了掺磁性膨胀石墨水泥浆体的电磁屏蔽效能（SE）.结果表明：掺加磁性膨胀石墨能大幅提高水泥浆体电磁屏蔽效能;掺15%磁性膨胀石墨水泥浆体电磁屏蔽效能值最高可达302dB.     

含20%石膏硫铝酸盐水泥的高温稳定性

钙矾石一直是水泥化学的研究热点之一,近几年来,延迟性钙矾石形成过程中产生的膨胀得到越来越多的重视。硫铝酸盐水泥水化产物中含有大量的钙矾石,这些钙矾石在高温下的稳定性如何,延迟性钙矾石对硫铝酸盐水泥的耐久性有何影响等一直是人们所关心的问题。本文主要对石膏掺量２０％的硫铝酸盐水泥在高温下的行为进行了研究,对其中的ＡＦｔ和ＡＦｍ之间的转变进行了探讨。     

矿物掺合料对混凝土抗压强度和氯离子渗透性能的影响

就单掺粉煤灰、单掺矿渣微粉,以及复掺粉煤灰与矿渣微粉对混凝土抗压强度和氯离子渗透性能的影响进行了试验研究。结果表明,粉煤灰和矿渣微粉明显降低了混凝土的早期抗压强度,但后期强度发展良好,而两者复掺更有利于后期强度的增长;粉煤灰和矿渣微粉都不同程度的降低了混凝土的氯离子扩散系数,随着龄期的延长,矿物掺合料提高混凝土抗氯离子渗透性能的能力越显著。     

粉煤灰对外掺轻烧MgO水泥浆体膨胀的影响

研究了粉煤灰对MgO膨胀剂(MEA)水泥浆体膨胀变形的影响,MEA的活性指数为50、100、190 s,MEA的掺量为6％和8％,养护温度为20、80℃.结果表明:当MEA掺量由6％增加到8％时,粉煤灰对MEA水泥浆体膨胀的抑制作用减弱.粉煤灰对掺高活性MEA水泥浆体膨胀的影响比对掺低活性MEA水泥浆体小.20℃水中养...     

约束条件下外掺MgO混凝土的强度与膨胀应力

研究了掺0％,5％,8％,12％(质量分数)MgO混凝土的自由膨胀、约束膨胀及其在约束条件下的抗压强度和膨胀应力.结果表明:混凝土的自由膨胀随着MgO掺量的增加而增大,560 d龄期时,MgO掺量为0％,5％,8％和12％的混凝土其最大膨胀量分别为-33× 10-6,90×10-6,230×10-6和320×10-6.MgO掺量相同时,三维约束试件强度＞二维约束试件强度＞自由试件强度,三维约束条件下,混凝土膨胀应力随MgO掺量的增加而增大;在三维方向上膨胀应力大小规律为pc,x＞pc,z＞pc,y;膨胀应力随养护龄期的延长而增加并在一定龄期内趋于稳定.     

怎样进行企业内部的招标工作

我局建材厂是一座利用煤矸石为原材料生产矸石砖的首创厂家,连年亏损,为了解决长期以来存在着“只负盈、不负亏”的老大难问题,为此,我们把竞争机制引入企业内部,实行全局范围内公开招标。实践证明,招标不仅使企业经济效益提高,使优秀人才脱颖而出,促进了干部管理体制改革,还蕴含着更为深远的意义。现将招标工作程序归纳如下: 一、准备阶段 成立招标委员会,下设招标办公室、资产评估小组专家考评小组。 1.招标办公室的任务是:制定招标方案和招标书;发布招标公告;接待投标人的报名、咨询,即向投标人解释招标书及有关的政策,回答问题,组织投标人到招标企业进行实地考察,提供有关资料;草拟承包经营合同,并主     

响应面法优化超声波-微波协同辅助酸法提取猕猴桃皮果胶工艺及果胶理化性质分析

为实现猕猴桃皮高值化利用,采用超声波-微波协同辅助酸法提取猕猴桃皮果胶。首先通过单因素试验确定提取液pH、超声波功率、微波功率、提取温度、提取时间、液料比等因素的取值范围,然后通过Plackett-Burman试验筛选影响果胶得率的关键因素,再采用Box-Behnken试验对工艺参数进行优化,最后对获得的猕猴桃皮果胶的分子质量、单糖组成、酯化度等理化性质进行分析。结果表明,提取液pH、提取温度、微波功率为关键因素,最佳提取工艺参数为：提取液pH 1.7、提取温度91℃、微波功率215 W、超声波功率250 W、提取时间35 min、液料比30∶1 （mL∶g）。在此条件下,实际果胶得率为34.88%。所得果胶的总糖含量为60.83%,蛋白质含量为1.78%,半乳糖醛酸含量为67.85%,酯化度为54.53%,重均分子质量（M_w）为741.78 kDa,单糖组成及摩尔百分比为鼠李糖4.2%、阿拉伯糖18.2%、半乳糖13.6%、葡萄糖5.5%、半乳糖醛酸58.5%。猕猴桃皮渣果胶分子以RG-Ⅰ型结构域为主。电镜扫描显示该果胶样品表面粗糙,由结构紧致的微球颗粒构成。     

Adsorption and Desorption Characteristics of Alkali Ions in Hydrated C_3S-nano SiO_2 Pastes

C_3S pastes containing 0%,5%,10%,and 15%nano-SiO_2 mixed with de-ionized water and alkali solutions were prepared.When C_3S was completely hydrated,the pastes were ground into powders with a particle size less than 80μm.Adsorption and desorption characteristics of alkali ions adsorbed by C_3S-nano SiO_2 pastes mixed with de-ionized water immersed in alkali solutions and those in C_3S-nano SiO_2 pastes mixed with alkali solutions,were investigated.Meawhile,the adsorption mechanisms of alkali ions were discussed.Results showed that the contents of alkali ions adsorbed by C_3S-nano SiO_2 pastes mixed with de-ionized water increased with increasing substitution levels of nano-SiO_2 and/or the initial alkali concentrations.In C_3S-nano SiO_2 pastes mixed with de-ionized water,each paste was characterized by having a fixed alkali-adsorption capacity that was essentially independent of alkali concentration.No obvious difference between the adsorption capacity of a given paste for K~+and Na~+was observed.Adsorption of alkali ions in the pastes is considered to be caused by surface force which is related to the BET specific surface area of the paste,and charge compensation of C-S-H gel,mainly by electrostatic interactions.In C_3S-nano SiO_2 pastes mixed with alkali solutions,alkali ions may enter the structure of C-S-H gel to replace a part of Ca~(2+)in the interlayer.This assumption is supported by the structural characterization of C-S-H gel using ~(29)Si MAS NMR.     

轨道交通综合监控系统用户与权限管理功能的设计与实现

针对城市轨道交通综合监控系统(简称ISCS)用户与权限管理的需求,基于对综合监控系统的用户画像分析,提出一种基于"用户-用户组-权限"的用户与权限设计方法,通过对综合监控用户画像、综合监控权限、用户及权限管理等进行分析,介绍了主要功能的实现机制。模型设计简洁易懂,具有易实现和高可靠的优点,对轨道交通及其他类似工程有一定的借鉴意义。     

RFID中嵌入式EEPROM的超低功耗设计

基于SMIC 0．35μm嵌入式EEPROM工艺实现了一款256byte的超低功耗EEPROMIP核。典型情况下．读电流为40μA，页编程电流为250μA，特别适合RFID（Radio Frequency Identiffcation）标签芯片的应用。针对芯片中各种功耗的来源进行了详细的分析，并给出了相应的实现方法。