Synthesis of Nanocrystalline Lanthanum Strontium Manganite Powder by the Urea–Formaldehyde Polymer Gel Combustion Route

Nanocrystalline lanthanum strontium manganite (LSM) powder has been synthesized by combustion of a transparent gel obtained by the polymerization of methylol urea and urea in a solution containing La³⁺, Sr²⁺, and Mn²⁺ (LSM ions). Chemistry of the transparent urea–formaldehyde (UF) polymer gel formation and structure of the gel have been proposed such that the LSM ions act in between the growing UF polymer chains by interacting through NH, OH, and CO groups by co-ordination and prevent polymer self-assembly through inter-chain hydrogen bonding as evidenced from infrared spectrum. Thermally stable structures formed by the decomposition of UF polymer below 300°C undergo combustion in the presence of nitrate oxidant in a temperature range from 350°–450°C. A perovskite LSM phase has been formed by self-sustained combustion of the dried gel initiated with little kerosene. The powder obtained after deagglomeration and calcination at 600°C for 2 h has a D ₅₀ value of 0.19 μm, and the particles are aggregates of crystallites 10–25 nm in size.     

Interpolymer complex microparticles based on polymethacrylic acid‐chitosan for oral insulin delivery

In the present study, microparticles composed of polymethacrylic acid‐chitosan (PMAA‐CS) were prepared by a novel interionic gelation method. Free‐radical polymerization of methacrylic acid was carried out in the presence of CS, using a water‐soluble initiator, and application of these microparticles toward oral insulin delivery was evaluated. Microparticles obtained were characterized by scanning electron microscopy (SEM) and Fourier transform infrared (FTIR) studies. From SEM studies, it was observed that microparticles had an aggregated morphology with size ～20 μm, while FTIR confirmed the presence of ionic interaction between PMAA and CS chains. Protein loading was done by diffusion filling method, and from in vitro release study, it was observed that insulin‐loaded microparticles displayed a pH depended release profile at alkaline/acidic pH. Microparticles exhibited sustained release of insulin for 3–4 h at neutral pH, and enzyme linked immunosorbent assay (ELISA) proved that encapsulated protein maintained 100% biological activity at neutral pH. Preliminary study suggests that these microparticles can serve as good candidate for oral protein delivery. © 2005 Wiley Periodicals, Inc. J Appl Polym Sci 99: 506–512, 2006     

Chitosan/calcium–alginate beads for oral delivery of insulin

A mild chitosan/calcium alginate microencapsulation process, as applied to encapsulation of biological macromolecules such as albumin and insulin, was investigated. The microcapsules were derived by adding dropwise a protein-containing sodium alginate mixture into a chitosan–CaCl₂ system. The beads containing a high concentration of entrapped bovine serum albumin (BSA) as more than 70% of the initial concentration were achieved via varying chitosan coat. It was observed that approximately 70% of the content is being released into Tris-HCl buffer, pH 7.4 within 24 h and no significant release of BSA was observed during treatment with 0.1M HCl pH 1.2 for 4 h. But the acid-treated beads had released almost all the entrapped protein into Tris-HCl pH 7.4 media within 24 h. Instead of BSA, the insulin preload was found to be very low in the chitosan/calcium alginate system; the release characteristics were similar to that of BSA. From scanning electron microscopic studies, it appears that the chitosan modifies the alginate microspheres and subsequently the protein loading. The results indicate the possibility of modifying the formulation in order to obtain the desired controlled release of bioactive peptides (insulin), for a convenient gastrointestinal tract delivery system. © 1996 John Wiley & Sons, Inc.     

Mechanistic origins of multi-scale reinforcements in segmented polyurethane-clay nanocomposites

The objective of the present work is to get insights into the mechanistic origin of the reinforcement effects of nanoclay on a segmented polybutadiene polyurethane-urea system. To this end, a convergent analysis of the hard domain morphology and conformational state of soft segment in the nanocomposites was carried out by using a combination of complementary characterization techniques, namely, Fourier transform infrared spectroscopy, small angle neutron scattering, transmission electron microscopy, modulated differential scanning calorimetry and dynamic mechanical analysis. Analysis of small angle neutron scattering data by a combination of Percus–Yevick hard sphere and Zernike-Ornstein model coupled with direct visualization of the dispersed hard domain morphology from transmission electron microscopy provided insight on clay induced changes in the hard domain morphology. A monotonic decrease in the domain size as well as the average interdomain distance was observed with increasing nanoclay content in the polymer matrix. Analysis of the carbonyl stretching region from FTIR showed increased degree of hydrogen bonding for the urethane carbonyl groups of the nanocomposites compared to the neat matrix. A combination of calorimetric and dynamic mechanical analysis revealed the existence of a constrained amorphous region; quantified to be ≈ 16% at the highest clay content experimented. The manifestation of these morphological and conformational changes on the nano-, micro- and macro scale reinforcements in the nanocomposites was investigated by mechanical properties at these length scales using nanoindentation, DMA and tensile testing, respectively.     

Erosion behavior of SiC–WC composites

Dense silicon carbide (SiC) ceramics were prepared with 0, 10, 30 or 50 wt% WC particles by hot pressing powder mixtures of SiC, WC and oxide additives at 1800 °C for 1 h under a pressure of 40 MPa in an Ar atmosphere. Effects of alumina or SiC erodent particles and the WC content on the erosion performance of sintered SiC–WC composites were assessed. Microstructures of the sintered composites consisted of WC particles distributed in the equi-axed grain structure of SiC. Fracture surfaces showed a mixed mode of fracture, with a large extent of transgranular fracture observed in SiC ceramics prepared with 30 wt% WC. Crack bridging by WC enhanced toughening of the SiC ceramics. A maximum fracture toughness of 6.7 MPa*m^1/2 was observed for the SiC ceramics with 50 wt% WC, whereas a high hardness of 26 GPa was obtained for the SiC ceramics with 30 wt% WC. When eroded at normal incidence, two orders of magnitude less erosion occurred when SiC–WC composites were eroded by alumina particles than that eroded by SiC particles. The erosion rate of the composites increased with increasing angle of SiC particle impingement from 30° to 90°, and decreased with WC reinforcement up to 30 wt%. A minimum erosion wear rate of 6.6 mm³/kg was obtained for SiC–30 wt% WC composites. Effects of mechanical properties and microstructure on erosion of the sintered SiC–WC composites are discussed, and the dominant wear mechanisms are also elucidated.     

Phytol Derivatives as Drug Resistance Reversal Agents

Phytol was chemically transformed into fifteen semi‐synthetic derivatives, which were evaluated for their antibacterial and drug resistance reversal potential in combination with nalidixic acid against E. coli strains CA8000 and DH5α. The pivaloyl ( 4 ), 3,4,5‐trimethoxybenzoyl ( 9 ), 2,3‐dichlorobenzoyl ( 10 ), cinnamoyl ( 11 ), and aldehyde ( 14 ) derivatives of phytol ((2E,7R,11R)‐3,7,11,15‐tetramethyl‐2‐hexadecen‐1‐ol) were evaluated by using another antibiotic, tetracycline, against the MDREC‐KG4 clinical isolate of E. coli. Derivative 4 decreased the maximal inhibitory concentration (MIC) of the antibiotics by 16‐fold, while derivatives 9 , 10 , 11 , and 14 reduced MIC values of the antibiotics up to eightfold against the E. coli strains. Derivatives 4 , 9 , 10 , 11 , and 14 inhibited the ATP‐dependent efflux pump; this was also supported by their in silico binding affinity and down‐regulation of the efflux pump gene yojI, which encodes the multidrug ATP‐binding cassette transporter protein. This study supports the possible use of phytol derivatives in the development of cost‐effective antibacterial combinations.     

Numerical study of heat and moisture transport through concrete at elevated temperatures

This research article focuses on numerical investigation of heat and moisture transport through concrete exposed to high temperatures such as fire. The conservation equations for moisture and energy transport through concrete have been represented in terms of temperature, pore pressure and vapor content as field variables. As the resulting governing equations are coupled and non-linear, the equations were solved numerically using Galerkin’s weighted residual finite element method and an iterative solution technique. After validating the model, a detailed simulation study has been carried out to understand the role of gradients of temperature, pore pressure and vapor content on heat and moisture transport through concrete exposed to ISO 834 fire curve. Results obtained at the end of 30 minutes exposure of concrete show that the temperature gradients become very steep after 12 minutes of exposure of concrete, which in turn results in increased vapor generation and 93% of vapor generation is completed at the end of 20 minutes. Due to steep temperature gradient along the length of concrete, condensation of vapor takes place which is followed by blockage of pores giving rise to sudden peak pore pressure rise and 97% of peak pore pressure is attained at the end of 18 minutes itself. It is observed that for the initial 18 minutes, the peak pore pressure front and peak vapor content front follow the same path and after 18 minutes the peak vapor content front moves slightly ahead of the peak pore pressure front.     

Multiple sourcing decisions using integrated AHP and knapsack model: a case on carton sourcing

Purchase allocation is a multi criteria decision making (MCDM) problem. Multitude of qualitative and quantitative factors is involved in the multiple sourcing decisions. Analytic hierarchy process (AHP) has widely been used to find out the relative rankings of suppliers. AHP can be combined with regular supplier quantitative audit process. In classical AHP, decision maker (DM) has to pair wise compare suppliers for each factor, whereas the proposed audit based simplified AHP will remove the complexity of comparison. Quarterly audit-based AHP rankings and supplier performance probability products can be used in place of revenues in the backward recursive resource allocation knapsack model. This combined model will decompose purchase allocation problem into different stages and combine one supplier at each stage and provide the optimum and feasible solution in the end. Solution at each stage is also a feasible option. This model is only applicable when the total order quantity and the capacity of all suppliers are integer multiples of economic or minimum order quantity. This integrated model thus provides number of orders/supplier.     

Dry sliding wear of short glass fibre reinforced zinc–aluminium composites

The present investigation aims to evaluate the wear rate of ZA-27 alloy composites reinforced with short glass fibres from 1 to 5% in steps of 2 wt%. The compocasting method was used to fabricate the composites. A pin-on-disc wear testing machine was used to evaluate the wear rate. The results indicated that the wear rate of the composites was less than that of the matrix alloy, but increased with the increase in load and the sliding distance. It was found that above a critical applied load, there exists a transition from mild to severe wear both in the unreinforced alloy and in the composites, but the transition loads for the composites are much higher than that of the unreinforced alloy, and increases with the increase in weight% of glass fibres. The observations have been explained using scanning electron micrography (SEM) analysis of the worn surfaces and the subsurface of the composites.