Fabrication of hierarchical PANI@W-type barium hexaferrite composites for highly efficient microwave absorption

Hexagonal barium ferries is a promising and efficient microwave (MW) absorbing material, but the low dielectric loss and poor conductivity have limited their extensive applications. In this work, a simple tactic of coating conductive polymer PANI on hexaferrite BaCo₂Fe₁₆O₂₇ is presented, wherein the dielectric properties are customized, and more significantly, the electromagnetic loss is greatly enhanced. As displayed from structural characterizations, PANI were coated equably on the surface of hexaferrite grains by an in-situ polymerization process. The outcomes exhibit the as-prepared PANI@hexaferrite composite has remarkable electromagnetic wave absorption capacity. When the thickness is 6.0 mm, the minimal RL of ?40.4 dB was achieved at 2.9 GHz. The effective absorption bandwidth (RL < ?20 dB) of 0.65 GHz, 0.53 GHz, 0.65 GHz, 0.52 GHz, 0.46 GHz and 0.39 GHz was achieved separately when the thickness ranges from 4 to 9 mm. The highly efficient MW absorbing performance of PANI@hexaferrite composite were the consequence of multiple loss mechanisms and perfect impedance matching. It is demonstrated that the PANI@hexaferrite composite with excellent MW absorption performance is expected to be potential MW absorbers for extensive applications.     

Two-step method to deposit ZrO2 coating on carbon fiber: Preparation,characterization, and performance in SiC composites

Recently, ceramic matrix composites reinforced by short carbon fibers (CFs) attracted increasing attentions. To further improve mechanical properties and oxidation resistances, CFs were subjected to oxidation and acidification followed by sol-gel dip-coating to deposit ZrO₂ on their surfaces. ZrO₂-C_f/SiC composites were fabricated by joint hot compression molding and sintering, compared to C_f/SiC and SiC prepared by the same method. Microstructural analyses indicated that ZrO₂ coatings were successfully deposited on CF surfaces, formed strong bonding and interfaces between CF and the matrix. Meanwhile, CFs were found uniformly distributed in SiC matrix with random orientations. Flexural curves of ZrO₂-C_f/SiC and C_f/SiC revealed the presence of “false plasticity” regions after sharp drops, which were quite different from brittle flexural behavior of SiC ceramic. Compression strength of the three samples showed step-up growth. ZrO₂-C_f/SiC exhibited the highest value, indicating the introduction of CFs and ZrO₂ coatings do have great influence on mechanical performances. After heat treatment, ZrO₂-C_f/SiC exhibited better oxidation resistance than C_f/SiC, with weight loss ratios estimated to ??3.76% and ??6.43%, respectively. These improved properties indicated that ZrO₂-C_f/SiC would be excellent alternatives to other existence materials under ultra-high temperature environments.     

Structures and properties of chicken myofibrillar protein gel induced by microwave heating

Structures and properties of myofibrillar protein gel prepared at different power (300–800 W) were evaluated. Amino acid analysis demonstrated that changes in microwave power did not alter primary structure of gel. However, an increase in microwave power could change higher structures of gel. As microwave power increased, α-helix content decreased and β-sheet content increased. Increased microwave power probably facilitated protein to unfold and expose the internal groups, causing surface hydrophobicity and the formation of disulphide bonds were enhanced, which indicated changes in tertiary and quaternary structures of protein. At 500 W, gel had the best ultrastructure where surface morphology, springiness and water holding capacity reached the optimum. Our findings suggested that microwave at an appropriate power (500 W) could change higher structures of myofibrillar protein gel to achieve desired processing and quality protein gel characteristics.