高效防腐中温磷化液LC-1的制备及性能

制备了一种含Zn2+、Mn2+、N i2+三系离子的LC-1磷化液,通过硫酸铜点滴、氯化钠浸蚀、SEM等手段对磷化膜进行了测试,测定了磷化温度、磷化时间对膜层耐蚀性的影响。结果表明,在磷化温度大于65℃,磷化时间大于10 m in的条件下,所形成的磷化膜结晶均匀、致密、黑褐色,耐蚀性良好。LC-1三系磷化液可适用于大批量钢铁工件的磷化生产。     

乙环唑的合成研究

介绍了以2,4-二氯苯乙酮为原料通过催化溴化、缩合反应、与三氮唑钠反应制得原药,原药含量达到92%以上.并对合成条件进行了研究,取得了较为满意的结果.     

转化乳剂的离子电导和光电导研究

本文研究了ＡｇＢｒＣｌ转化乳剂的离子电导和光电导。随着乳剂中溴含量的增高，其离子电导也随之升高，而光电子寿命则降低。ＡｇＢｒＣｌ乳剂的离子电导主要取决于其组成；ＡｇＢｒＣｌ转化乳剂的光电子寿命主要受隙间银子浓度的影响，隙间银离子浓度越大，光电子寿命越短。     

丙烯酸接枝线形低密度聚乙烯的热学行为及结晶形态

利用差示扫描量热仪研究了丙烯酸接枝线形低密度聚乙烯（PE-LLD-g-AA）的热学行为，结果表明，与纯线形低密度聚乙烯（PE—LLD）相比，PE-LLD-g-AA的熔融温度（Tm）略有增加，结晶温度（Tc）增加大约4℃，熔融焓（AHm）随AA含量的增加而降低。还利用差示扫描量热仪研究了PE—LLD和PE—LLD-g—AA的等温结晶动力学，用扫描电子显微镜观察了PE—LLD-g—AA等温结晶形态。结果表明，PE-LLD-g-AA的结晶速率大于纯PE—LLD的，随着接枝率的增加，PE-LLD的球晶半径减小，接枝到PE—LLD分子链上的AA分子起到了成核剂的作用。     

粉末材料合成金刚石中工艺参数的选取

合理地选取工艺参数,有利于合成优质金刚石.文章综述了粉末材料合成金刚石中工艺参数对合成效果的影响以及粉末材料合成金刚石中工艺参数的选取原则.     

Seeded Crystallization of Leucite

The leucite crystallization kinetics from a hydrothermally derived precursor seeded with nano-crystalline leucite was investigated by X-ray diffraction and non-isothermal differential thermal analysis. The nano-crystalline leucite was prepared by high-energy milling of high-purity leucite powder and the leucite precursor was prepared by the hydrothermal method of silica sol, aluminum nitrate, and potassium nitrate. After the seeds were introduced, the crystallization temperature of the precursor was lowered by 100°C and the transition phase kalsilite did not appear during the crystallization process. When the seeded precursor was heat treated at 700°C, a small amount of cubic leucite was stabilized to room temperature. The seeded precursor showed an exothermic peak between 800° and 920°C under different heating rates. The activation energy for the growth of leucite from the seeded precursor was 256(SD9) kJ/mol.     

Synthesis and characterization of copolythiophene

Copolythiophenes (Co‐PTs), poly(3‐hexylthiophene‐co‐3‐thiophene carboxylic acid) (P3HT‐TCa), poly(3‐hexyloxylthiophene‐co‐3‐thiophene carboxylic acid) (P3HOT‐TCa), and poly(3‐phenylthiophene‐co‐3‐thiophene carboxylic acid) (P3PhT‐TCa), were synthesized by chemical oxidized polymerization to investigate the effect of copolymerization on the properties of polythiophenes (PTs). Gel permeation chromatography showed that the molecular weight (MW) of Co‐PT was lower than that of homopolythiophene. Fourier transform infrared (FTIR) spectra indicated that the copolymerization was successful between the monomers. The λ_max of Co‐PTs gave a “blue shift” in ultraviolet‐visible (UV‐VIS) spectra. Photoluminescence (PL) spectra showed that the PL intensity of Co‐PT became weaker than that of homopolythiophene and the disappearance of PL had been observed in P3HOT‐TCa. The thermal stability of Co‐PT was influenced by the carboxyl for its low decomposition temperature. Furthermore, the copolymerization between multi‐wall carbon nanotube containing thiophene ring (MWNT‐Th) and 3‐hexyloxylthiphene could also take place successfully. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci 2007     

乳液聚合中单体醋酸乙烯酯与保护胶体聚乙烯醇的接枝反应研究

研究了以聚乙烯醇为保护胶体的醋酸乙烯乳液聚合中,聚乙烯醇与单体的接枝反应。探讨了引发剂用量、聚合反应温度、保护胶体聚合度等因素对接枝反应的影响。     

汽车灯用热熔胶的研究及性能表征

介绍了生产汽车灯用热熔胶的各种原料及其在胶粘剂中所起的主要作用，为汽车灯用热熔胶原料的选择提供了参考。还介绍了汽车灯用热熔胶的制备过程和厂家所需的各种性能及其表征方法。通过选择适当的原料及配比，生产出性能优良并具有良好市场前景的产品。     

基于线性动态系统稀疏编码的异常事件检测

线性动态系统模型结合稀疏编码实现异常事件检测。线性动态系统可有效地捕捉动态纹理在时间和空间的转移信息,描述视频的时空小块。然而,线性动态系统属于非欧氏空间,无法直接用传统的稀疏编码进行异常检测。基于约束凸优化公式,将相似性变换与稀疏编码结合,可实现线性动态系统稀疏编码的优化求解。实验表明,所提出的方法具有更好的性能。