FS-1化学镀Ni-P镀层的性能研究

采用XRD与SEM分析技术、电化学阳极极化曲线测试和 摩擦磨损试验等，系统地研究了FS-1化学镀Ni-P镀层的结构和性能.结果表明：该镀层具有 优良的耐蚀和耐磨性能，热处理虽可以显著地提高镀层的耐磨性能，但使其耐蚀性能有所降 低.     

非晶态Pd—Cu—Si合金的晶化动力学研究

本文应用DSC研究了非晶态Pd-Cu-Si合金的晶化过程动力学.根据Kissinger峰移法和Arrhenius方程分别计算了晶化激活能,发现等温晶化动力学在0.15相似文献   

Kinetics of synthesis of Li4Ti5O12 through solid-solid reaction

1. Introduction The solid-solid reaction used in synthesizing various kinds of electrochemical materials has many advantages, such as simple process, without using solvent, saving energy, friendly to the environment and easy to obtain good quality materials like nano-size materials. Recently, the manufacturing of electrochemistry materials has been paid more atten- tion due to its increasing needs. Therefore it is a natural interest to study the synthesis of electro- chemical materials by usin…     

Effect of sintering process on microstructure and magnetic properties of high frequency power ferrite

An oxide ceramic process was adopted to prepare high frequency manganese-zinc (MnZn) power ferrite. In combination with the microstructure analysis of material, the influences of sintering process on initial permeability (μi) and high frequency loss in unit volume (Pcv) of MnZn power ferrite were investigated. The results show that in order to obtain fine microstructure and high frequency properties, the preferable sintering temperature and atmosphere are 1230 ℃ and oxygen partial pressure ( PO2) of 4%, respectively.     

Microstructure and magnetic performance of Ni-substituted high density MnZn ferrite

The effects of NiO on microstructure and magnetic properties of Mn-Zn ferrite with a nominal composition of Zn0.32Mn0.60-xNixFe2.08O4 were investigated. The calcined powder of Mn-Zn ferrite was characterized by X-ray diffraction (XRD), the fracture surface of Mn-Zn ferrite was checked by scanning electronic microscope (SEM), and then the magnetic properties were measured. As a result, the substitution of Ni can cause the crystallattice constant of MnZn ferrite to decline, and the grain size to decrease, therefore improve the magnetic performance of MnZn ferrite whose density exceeds 5.0 g·cm-3.     

Continuous cleaning of A356 alloy melt using high frequency electromagnetic field

A set of device for electromagnetic separation (EMS) was designed and applied to process the continuous flowing melt. Tensile test was employed to compare effect of electromagnetic separation with that of the traditional processes. Compared with filtration by ceramic foam filter and process without filtration, multiple process combined with filtration and electromagnetic separation can effectively remove most of inclusions with diameter finer than 10μm in A356 alloy casting, hence improve its tensile properties. After being processed by electromagnetic filtration,the tensile strength of A356 scrap is enhanced by 8.27%, approaching the level of fresh A356 alloy.     

Influence of expandable graphite on fire resistance and water resistance of flame-retardant coatings

Expandable graphite (EG) coating and ammonium polyphosphate-pentaerythritol-melamine (APP-PER-MEL) coating were prepared. Thermal degradation and char formation of the coatings were investigated by differential thermal analysis (DTA), thermogravimetry (TG), X-ray diffraction (XRD), scanning electron microscopy (SEM) and X-ray photoelectron spectroscopy (XPS). The results have shown that the anti-oxidation and fire-resistant properties of expandable graphite coating containing EG with size of 74 μm are better than those of APP-PER-MEL coating. The static immersion test was applied to study water resistance of the coatings, and the fire protection test and mechanical test were used to analyse heat insulation and mechanical properties of coatings before and after water immersion. The fire-resistant and mechanical properties of APP-PER-MEL coating were severely damaged by water immersion, whereas EG coating containing 8.5% EG with size of 74 μm could retain the good fire resistance even after 500 h water immersion.     

CNG储气瓶的金属磁记忆检测

使用金属磁记忆检测方法和超声方法对在役的七组公交车CNG高压储气瓶组进行了检测,并对比分析了两种方法的检测结果。结果表明,金属磁记忆方法检测到的可疑区域涵盖了超声检测到的缺陷区域,因此用磁记忆方法检测高压储气瓶,有较高的可靠性和高效性。     

碳化硅晶须双重加热合成的研究

双重加热法是低成本、大批量合成碳化硅晶须的新技术，合成温度低、合成时间短、生成率高。对以炭黑和二氧化硅微粉为原料、用双重加热法合成碳化硅晶须的工艺过程进行了研究。观察了不同合成时间、合成温度和催化剂条件下的碳化硅晶须，揭示出不同工艺参数对合成的碳化硅晶须的产出率，微观形貌、直径和长度范围的影响。结果表明，催化剂的使用可以加快反应速度，提高碳化硅晶须的生成率，合成过程为VLS。实验中初步得到的最佳经济工艺参数为：Fe2O3的用量为2％，合成时间为1．5h，合成温度为1250℃。此时的该工艺条件下碳化硅晶须的生成率可达80％，晶须平均直径为0．6μm，平均长度为30μm。     

大中型连杆锻件的切边、冲孔、校正工艺

在分析大中型连杆类锻件生产难点的基础上，提出了通过优化锻造工艺方案，设计了切边冲孔校正复合模。提高了带大孔的连杆类锻件的产品质量和生产效率。