X射线ICT检测中康普顿散射效应的影响与修正

在X射线工业计算机层析检测(ICT)中,由于X射线与物质作用发生康普顿散射效应,有用信息连同散射光子一起进入探头形成伪影。运用康普顿散射强度方程,结合X射线与物质相互作用的特性,推出X射线ICT中的散射修正公式,并由圆形截面工件散射模型,求出圆形截面工件的具体计算积分限。从探测器探测到的总光子数中减去康普顿散射光子数,即可有效去除散射光子造成的伪影。     

高pH值污水杀菌剂的研究

介绍了高pH值污水细菌含量状况，研究了高pH值污水细菌生长与抗药性的变化规律，研制出针对高pH值污水应用的高效杀菌剂。     

工艺设计文件输出管理数据库的开发

文章首先研究了工艺设计文件的数据库管理问题,设计开发了工艺文件输出管理数据库,创建了一套符合要求的工艺卡片模板,实现了工艺文件卡片的在线自动填写及输出,方便了用户的使用.     

Dependence of dielectric properties on BT particle size in EP/BT composites

The polymer-ceramic composites of epoxy resin (EP) and barium titanate (BT) were prepared.BT powders of different BT particle sizes from 100 nm to 1 μm were used in the preparation.The dielectric properties, such as dielectric constant, dielectric loss and electrical breakdown strength, of the EP/BT composites were studied.The morphology of the composites was characterized by the means of scanning electron microscopy (SEM).The results show that the dielectric constant of the composites is much higher than the epoxy matrix at frequency range from 1 kHz to 10 MHz, and it is also obviously dependent on the size of BT particles.The electrical breakdown strength of the composites decreases with the increase of the BT content.The dependence of electrical breakdown strength on BT particle sizes was also discussed.     

单片机控制的电阻钎焊系统

在电阻钎焊基本原理的基础上，介绍了利用AVR单片机设计开发的电阻钎焊控制系统，分析了单片机的软硬件结合。 时给出了利用热电偶放大和数字转换器MAX6675采集和处理温度信号的基本连接电路并分析了其优点。     

LD7铝合金热变形行为的实验研究

在G1eeble-1500热模拟试验机上对LD7铝合金试样在变形程度为60％，变形温度为360～480℃、变形速率为0．0l～1s^-1的条件下进行等温压缩试验，然后对其进行固溶处理。根据试验结果分析热变形参数对合金流动应力和固溶之后显微组织的影响，可以得到如下结论：LD7铝合金是动态回复型合金，合金的流动应力随温度的升高而降低，随应变速率的升高而升高；合金的晶粒尺寸随温度的升高而增大，随变形程度和变形速率的增大而减小。     

异形坯连铸坯壳应力与鼓肚变形分析

坯壳应力引起的鼓肚变形是影响铸坯质量的重要因素,为防止过大的鼓肚变形,依据湍动能理论、热流传递理论和粘弹性理论,建立了异形坯三维热-力耦合模型,开发了鼓肚分析软件,从而避免了漏钢事故的发生.该模型将温度场和应力场的计算相互耦合,交替进行.结果表明:异形坯截面最危险点位于腹板中部,其次为翼板中点,在两者相结合的圆角部,由于凝固坯壳比较薄,其应力值也比较大;当坯壳厚度小于20 mm时,两点的鼓肚变形量将分别超过其极限变形量,铸坯出结晶器时必然发生漏钢事故.该模型通过预测坯壳应力和鼓肚变形量为现场安全生产提供了理论依据.     

Impact toughness of tungsten films deposited on martensite stainless steel

Tungsten films were deposited on stainless steel Charpy specimens by magnetron sputtering followed by electron beam heat treatment. Charpy impact tests and scanning electron microscopy were used to investigate the ductile-brittle transition behavior of the specimens. With decreasing test temperature the fracture mode was transformed from ductile to brittle for both kinds of specimens with and without W films. The data of the crack initiation energy, crack propagation energy, impact absorbing energy, fracture time and deflection as well as the fracture morphologies at test temperature of-70 ℃ show that W films can improve the impact toughness of stainless steel.     

直齿圆柱齿轮温挤压成形的数值模拟

用优化后的凹模结构对直齿圆柱齿轮的温挤压成形进行了数值模拟 ,结果表明 ,以入模角为 180°、挤压筒内径等于直齿轮齿顶圆直径 ,且在齿根圆处不倒角为特点的凹模形式对齿形成形效果良好 ,此种凹模形式能够解决齿形角隅充不满的难题 ,非常适合直齿圆柱齿轮的挤压精密成形     

新型手机用PCB板焊点的失效分析

采用多种宏微观分析手段,对新型手机用PCB板的失效焊点(BGA)与散落焊珠的组分进行了系统的表征分析.结果表明,表面贴装技术(SMT)回流焊工艺参数控制不当是主要的失效起因;焊膏质量不佳及回流焊工艺与其不匹配是导致焊点焊块失效的另一重要原因.针对上述问题,就回流焊工艺参数的调整以及焊膏质量的改善提出了具体建议,以确保该PCB板的结构完整性和安全可靠性.