Preparation and optical properties of CdxHg1-xTe doped silica glass

In this paper, the Cd_xHg_1-xTe (x=1-0.7) doped silica glass was prepared through two step sol-gel process and in-situ growth technique from tetraethoxysilane (TEOS), cadmium acetate, mercury acetate and telluric acid. The influence of various factors on the glass was studied. The structure of the microcrystals was investigated by XRD. The absorption and transmittance spectrum of the composite showed that the shift of absorption edge was in conformity with the quantum size effect. The third-order nonlinear optical susceptibility χ⁽³⁾ was measured by the degenerate four wave mixing (DFWM). The values of χ⁽³⁾ was in the range of 10^-11-10^-12 MO esu at wavelength of 1.06 μm.     

High voltage (>1kV) and high current gain (32) 4H-SiC power BJTs using Al-free ohmic contact to the base

This letter reports the design and fabrication of 4H-SiC bipolar junction transistors with both high voltage (>1kV) and high dc current gain (/spl beta/=32) at a collector current level of I/sub c/=3.83A (J/sub c/=319 A/cm/sup 2/). An Al-free base ohmic contact has been used which, when compared with BJTs fabricated with Al-based base contact, shows clearly improved blocking voltage. A specific on-resistance of 17 m/spl Omega//spl middot/cm/sup 2/ has been achieved for collector current densities up to 289 A/cm/sup 2/.     

A polymerizable photoredox initiation system for vinyl photopolymerization

A polymerizable photoredox system consisting of 4-methacryl oxbenzophenone (MABP) and N,N-dimethlaminoethyl methacrylate (DMAEMA) used for the photopolymerization of acrylonitrile (AN) was studied. It was found that the polymerization rate is proportional to the 0.93th power for the AN concentration, the 0.28th power for the MABP concentration, and the 0.25th power for the DMAEMA concentration. The overall activation energy of the polymerization obtained is 30.43 kJ/mol. The recorded ESR spectrum indicates that the excited-state MABP abstraets hydrogen mainly from the methyl group of the dimethylamino moiety. The comparison of the initiation ability of polymeric MABP or polymeric DMAEMA with their monomeric forms has also been done and the results indicate that in good solvents P (MABP) has a much higher initiation ability than that of monomeric MABP, but monomeric DMAEMA and P (DMAEMA) display almost the same initiation ability. In poor solvent, the initiation ability of P (MABP) is not so obviously higher than that in good solvents. The result of UV analysis of P (AN) initiated by the MABP–DMAEMA system indicates that both MABP and DMAEMA not only initiate the photopolymerization of AN, but also enter into P (AN) polymer chains. © 1994 John Wiley & Sons, Inc.     

STRUCTURE REPRESENTATION OF THE SPECIFIC FRACTIONS FROM PINGSHUO COAL

Basic data of four fractions, PM₁, PM₆, PM₇and PM₈, derived from Pingshuo bituminous coal were obtained by ultimate analyses, mean molecular weight measure, GC/MS, ¹³C-NM R, ¹H-NM R and FTIR technigues. A method of calculating the average molecular parameters of the fractions is introduced. Based on the calculated parameters, the molecular structure models of the fractions of PM₆, PM;and PM₈are constructed. Significant structural information about the saturated hydrocarbon and aromatic hydrocarbon with heteroatom groups is given also.     

Using thermally stimulated currents to find defective capacitors

BaTiO₃ multilayer capacitors with a nominal capacitance of 3.5nF have been carefully measured using the thermally stimulated current (TSC) technique. When a 300V polarization voltage is applied at room temperature, a new TSC peak appeared in defective sample A after it has been immersed in water. No new peak was found in good-quality sample B after a similar treatment. The accelerated life test shows that sample A hasa much shorter life than sample B in terms of insulation resistance.