化学共沉淀法制备LixCoO2的高温化学相变过程研究

以从废旧锂离子电池中回收的钴、锂为原料制备了LiCoO2粉体.讨论和分析了不同温度下的热处理对LixCoO2结构的影响.随温度升高,立方相减少,六方层状相增多.600℃时尖晶石相向六方相转变,温度继续升高(650℃～800℃)只有六方层状结构存在.再升至较高温度,层状属性增强,结构出现不稳定性,锂出现挥发,在860℃左右,产生新的相变;经过高温XRD分析,900℃时,出现大量的立方相LixCo1-xO和Co3O4,并随温度持续升高,六方LiCoO2相与立方Co3O4均有所减少,而立方LixCo1-xO相增加,1050℃时以LixCo1-xO为主,当x＜0.07时,立方LixCo1-xO为结构稳定相.     

镁合金表面冷喷涂快凝Zn-Al合金粉末的研究

对镁合金表面冷喷涂快凝Zn-Al合金粉末工艺进行了研究，观察了涂层微观组织，并分析了涂层与基体之间的结合，测定了涂层的硬度和涂层与基体的结合强度。结果表明，采用冷喷涂技术制备的快凝Zn—Al合金粉末涂层组织致密，基体与涂层的结合处只产生塑性变形并且无熔化现象，涂层硬度比基体硬度显著提高。     

Crystal and magnetic structures of Laves phase compound NdCo2 in the temperature range between 9 and 300 K

The crystal and magnetic structures of the Laves phase compound NdCo₂ in the temperature range from 9 to 300 K are determined by Rietveld refinement technique, using high-resolution neutron powder diffraction data. The compound crystallizes in space group above the magnetic ordering temperature T_C (≈100 K), in space group I4₁/amd below T_C and in space group Imma below the tetragonal–orthorhombic structural/magnetic transitions at T_M ≈ 42 K. The assignment of the space groups to the crystal structures of NdCo₂ in different temperature ranges complies with the reported Mössbauer studies. Detailed information of the crystal and magnetic structures of NdCo₂ at different temperatures are reported.     

斜楔式槽钢冲孔模

本文主要介绍了斜楔式槽钢冲孔模的结构与工作原理，凸模、双向斜楔、退料组件等主要零部件的设计方法。     

Al4SiC4陶瓷的高温氧化行为

从高温氧化动力学、组织的微观进化及高温氧化机理3部分对Al4SiC4陶瓷在1200℃-1700℃的高温氧化行为进行了系统的研究。研究结果表明，Al4SiC4陶瓷具有优异的高温抗氧化性能。氧化动力学符合抛物线规律，其氧化活化能经计算为220kJ／mol。XRD及SEM研究结果表明：Al4SiC4陶瓷在1200～1500℃的氧化表面物相为Al2O3和铝硅酸盐玻璃；而高温氧化表面（1600℃～1700℃）的物相由Al2O3，莫来石和铝硅酸盐玻璃构成。由氧化试样横截面观察得知氧化层按其特征的不同分为3个部分：具有较多细小尺寸孔洞的反应层；具有较大尺寸孔洞的中间层和致密的外氧化层。在高温抗氧化机理部分中首先从热力学上计算了氧化过程中各反应的生成焓和吉布斯自由能；然后对高温氧化过程进行了推理和分析；最后根据上述试验及推理结果建立了Al4SiC4陶瓷的高温抗氧化模型。     

表面氧化层对TiMn1.25Cr0.25储氢合金活化性能的影响

通过TiMn1.25Cr0.25合金粉活化前在空气中暴露不同的时间,探讨了表面氧化层的形成对其活化性能的影响。活化测试结果表明：合金的活化难度随着合金在空气中暴露时间的延长而加大。俄歇电子能谱(AES)结果表明,在空气中暴露后的合金表面形成了一层大约6nm-10nm厚的表面氧化层,正是这层氧化层的形成加大了合金的活化难度。扫描电镜(SEM)结果表明合金的活化过程与合金的碎化有着密切的联系。     

机械合金化制备金属间化合物MoSi2

以Si粉和Mo粉为原料采用机械合金化的方法制备了金属间化合物MoSi2.研究了球磨过程中球磨时间、球料比、转速及不同球磨机类型对机械合金化产物的影响.利用SEM观察粉末表面形貌及颗粒大小,利用XRD测定物相结构.研究结果表明,当球磨机提供的能量达到相变所需的能量时,粉末中有MoSi2相生成.通过XRD分析可以看出,随着球磨时间的延长,合金化程度逐渐提高;球磨转速的提高有助于生成MoSi2;较高的球料比可以使生成MoSi2的时间提前.在机械球磨过程中,粉末的颗粒尺寸经历了一个由较粗且不规则、不均匀粉末向细小、均匀、接近球形粉末,然后团聚增大的转化过程.此外,还研究了助磨剂对合金化产物的影响,结果表明助磨剂的加入并不能促进MoSi2的生成,但可以对颗粒的细化起到一定作用.     

Examination of wire electrical discharge machining of Al2O3p/6061Al composites

Alumina particle reinforced 6061 aluminum matrix composites (Al₂O₃p/6061Al) have excellent physical and chemical properties than those of a traditional metal; however, their poor machinability lead to worse surface quality and serious cutting tool wear. In this study, wire electrical discharge machining (WEDM) is adopted in machining Al₂O₃p/6061Al composite. In the experiments, machining parameters of pulse-on time were changed to explore their effects on machining performance, including the cutting speed, the width of slit and surface roughness. Moreover, the wire electrode is easily broken during the machining Al₂O₃p/6061Al composite, so this work comprehensively investigates into the locations of the broken wire and the reason of wire breaking.The experimental results indicate that the cutting speed (material removal rate), the surface roughness and the width of the slit of cutting test material significantly depend on volume fraction of reinforcement (Al₂O₃ particles). Furthermore, bands on the machined surface for cutting 20 vol.% Al₂O₃p/6061Al composite are easily formed, basically due to some embedded reinforcing Al₂O₃ particles on the surface of 6061 aluminum matrix, interrupt the machining process. Test results reveal that in machining Al₂O₃p/6061Al composites a very low wire tension, a high flushing rate and a high wire speed are required to prevent wire breakage; an appropriate servo voltage, a short pulse-on time, and a short pulse-off time, which are normally associated with a high cutting speed, have little effect on the surface roughness.     

MoS2-Ti复合膜的结构及其抗氧化性能

利用非平衡磁控溅射仪在碳/碳复合材料表面制备了MoS2-Ti复合膜.采用XRD,Raman光谱、X射线光电子能谱仪对其结构进行了表征,并利用X射线光电子能谱仪对复合膜的抗氧化性能进行了研究.研究结果表明:所制备的MoS2-Ti复合膜为非晶态结构;MoS2-Ti复合膜具有良好的抗氧化性能,将其在蒸馏水中浸泡200 h后,Mo4+没有被氧化.     

旋转吹氮铝液精炼方式的改进及效果研究

为了改善铝合金重力铸造中针孔及夹杂缺陷，通过对吹氮净化铝液工艺中的旋转喷头的改进，来细化氮气气泡的体积，增加氮气与铝液的接触面积，从而提高除气除渣的效果，达到铝液净化的目的，最终提高产品的质量。