耐盐性树脂PAA的合成及应用研究

以丙烯酸-丙烯酰胺为单体，过硫酸钾为引发剂，N，N-亚甲基双丙烯酰胺为交联剂。水浴阶梯升温共聚合成耐盐性树脂，采用正交试验通过分析，研究了主要因素对产物性能的影响，确定较佳反应条件：T=50℃(2h)～65℃(3h)，单体配比nAM：nAA=1：11，单体中和度[N]=90％～95％。引发剂浓度[I]=0．3％，单体浓度[M]=30％～35％，交联剂浓度[C]=0．025％～0．03％，并将此树脂作为缓释剂应用于固载二氧化氯中，取得了良好的效果。     

Water-soluble and amphiphilic polymers

Summary Three PEO-PSt-PEO triblock polymers and their parent ho-nopolystyrene have been studied by means of light scattering technique in chloroform, toluene and ethyl acetate. It has been found that the weight average molecular weights calculated by using the equation Mapp- were unbelievable negative values; and the largest deviation appeared for the sample with PEO mole content of about 50%. Data of PSt-PEO-PSt triblock polymers in literature have been quoted and discussed.     

中央空调的水处理

本文扼要介绍了中央空调循环冷却水和冷冻水系统中常见的问题及其原因,并对冷却水和冷冻水的处理程序作了初步的阐述.     

ATO包裹硅酸锆的制备与应用

采用化学共沉淀技术制备了锑掺杂二氧化锡(ATO)包裹硅酸锆的导电粉体,对比了该导电粉体与ATO在防静电陶瓷中的应用效果。结果表明与掺纯ATO相比较,掺入ATO包裹硅酸锆的防静电陶瓷颜色比较浅,并且能明显减少氧化锡的用量,当陶瓷的表面电阻为107Ω/□量级时,用ATO包裹硅酸锆作为导电填料可以节省25%左右的ATO。     

The determination of the pore structural parameters of isoporous resins by inverse GPC

The swollen pore structure of a series of microporous isoporous resins (7.4–140 Å) are investigated with inverse GPC, n-alkylbenzenes and linear polystyrenes being used as probe molecules. The results indicated that, with the lowering of crosslinking degree of isoporous resins, the average pore diameter increased and the pore distribution curve broadened. All pore volume distribution obeyed a log-normal distribution. Based on the linear regression method, the experimental data were fitted to a monotonously declining exponential function and a normal distribution function by a computer, and some important structural parameters such as average pore diameter, pore volume distribution, specific surface area, etc. were obtained. The specific surface area of swollen gels were found much greater than those in the dry state measured by N₂ adsorption.     

降维方法监督分类的比较研究

对ISOMap、LDA、LLE、PCA这4种典型降维算法的主要思想和算法步骤进行了详细分析,并将它们用于有监督分类。从实验结果分析得到结论 ,其可为有监督分类提供有益的借鉴。     

Preparation and Photoluminescence of Partially Filled ZnO Microtubes Using Block Copolymers

Partially filled ZnO microtubes were synthesized in large scale using block copolymers. The growth mechanism of this unique construction is proposed on the basis of adsorption of block copolymers on {0002} plane of wurtzite ZnO. The photoluminescence property of these unique ZnO microtubes is also studied using a Xe lamp as the excitation source at room temperature. Blue emission band at 425 nm is a much stronger ultraviolet emission band, which is due to laminar structure of ZnO microtubes.     

炭黑填充硬聚氯乙烯的改性

为使聚氯乙烯具有抗静电性能,采用加入具有导电性填料的方法,但加入大量的填料,会使硬聚氯乙烯的冲击性能降低,加工性能变差。本文是在以炭黑为填料的基础上,研究不同的改性剂和加工助剂改进硬聚氯乙烯的效果,结果表明,加入冲击改性剂和加工助剂后,大大增加了硬聚氯乙烯的冲击强度,且加工性能也得到改善,同时由于炭黑具有补强效果,其拉伸强度和弯曲强度在加入改性剂后也能满足使用要求。     

Kinetics for benzoylation of sodium 4-acetylphenoxide via third-liquid phase in the phase-transfer catalysis

In this research, the kinetics for synthesizing 4-acetylphenyl benzoate (R^*COOR) from benzoylation of sodium 4-acetylphenoxide via third-liquid phase-transfer catalysis was investigated. The reaction rate was observed to be strongly dependent on agitation speeds in the third-phase catalytic reaction. By forming the third-liquid phase, the observed reaction can be greatly enhanced to give a product yield of 100% in a duration of 3 min at 20 °C and 200 rpm. If a third-liquid phase was not formed in the liquid–liquid system, the reaction rate is very slow and the product yield is only 2% in 3 min at 20 °C. The reaction conducted in third-liquid phase-transfer catalytic system is faster than that in LLPTC system by 25–28 times. The amount of catalytic intermediate (QOR) in the third-liquid phase was about 50% of the catalyst initially added and kept about 30% of it remained after 1 min, and only small amounts of a catalytic intermediate residing in the organic phase were observed during the reaction using methyl t-butyl ether as the solvent. The concentration of catalytic intermediate slightly decreased with increasing reaction time, while the molar ratio of QOR to benzyl tri-n-butylammonium cation in the third-liquid phase remained almost constant after 1 min and increased with increasing agitation speeds. The experimental results were well described by the pseudo-first-order kinetics. The present work shows an effective method to synthesize 4-acetylphenyl benzoate.     

冷却器盘管失效分析及防范措施

本文介绍了冷却器盘管破裂泄漏的情况，分析了失效破坏的原因，并提出防止冷却器盘管破裂泄漏的措施。