HRTEM observation of the monoclinic-to-tetragonal m-t) phase transition in nanocrystalline ZrO2

The orientation relations m(100) || t(001), m[001] || t[110]; m(011) || t(100), m[100] || t[001]; m(100) || t(110), m[001] || t[001]; m(013) || t(116), m[001] || t[001] (indices for the primitive tetragonal cell) have been found between the tetragonal (t) and monoclinic (m) domains during the electron irradiation-induced m-t phase transition observed in-situ with HREM within isolated zirconia nanoparticles. Geometric models of the m-t interfaces are proposed.     

Potential for integration of electrophoretic deposition into electronic device manufacture; demonstrations using silver/palladium

A silver palladium (Ag/Pd) alloy powder is used as an example material to illustrate potential applications of electrophoretic deposition (EPD) in electronics manufacturing, in particular the forming of multilayer devices. The dispersion and deposition of the Ag/Pd powder in acetic acid is characterized. It is found that deposition can be explained by the direct action of electrostatic force on individual particles. Depositions of this Ag/Pd powder are then used to demonstrate: forming of a continuous layer on a rigid substrate; forming of continuous layers in laminated and sintered BaTiO₃ multilayers; and incorporation of patterned depositions into a multilayer by either overcasting the patterned deposition with a particulate slip to form a multicomponent tape, or direct lamination of the patterned deposition to a low temperature co-fired ceramic (LTCC) tape. It is shown that electrically conducting layers can be formed at an average thickness of only two times the diameter of the starting powder. Continuous conductor lines thirty times the average diameter of the starting powder were formed.     

Magnetic properties and thermal stability of CoFeNi-based amorphous films

CoNiFe-based amorphous films were magnetron-sputtered to investigate their structural and magnetic properties, including annealing-induced effects and interfacial influence from additional layers of Ta and Cu. The amorphous structure was confirmed by diffraction experiments. The magnetic measurements showed a well-defined uniaxial anisotropy in plane, arising possibly from atom oblique incidence effects competing with the stray field of the magnetron. The anisotropy could be influenced by using a Ta buffer layer, though the interfacial reaction gives rise to a dead layer. A coercive force H _c of 1–2 Oe and a magnetization of 680 emu/cm³ were measured at room temperature; properties which show promise for application in magnetotunneling junction devices. Thermal analyses showed a two-stage crystallization behavior, which started at 400°C and ended at about 600°C. The Curie temperature of the amorphous phase was estimated to be about 440°C.     

Electrophoretic deposition of monochrome and color phosphor screens for information displays

This paper reviews our research on the electrophoretic deposition (EPD) of phosphors for the processing of monochromatic and color screens for information displays. Our investigation began with the study of the fundamentals of the EPD process for phosphors. The processing variables which enhance the adhesion strength of phosphor deposits were determined. The optical performance of phosphors deposited by EPD was shown to be not affected by the process itself nor by the conditions which enhance phosphor adhesion. Processes developed to produce high-resolution color screens by combining EPD and photolithography techniques are described. Also, a method to electrophoretically deposit phosphor in a thermo-reversible gel from mixtures of poly(butyl methacrylate) and isopropanol was examined.