Properties and Microstructuresof Three Kinds of Silversheathed Bi-2223 Tapes

ＰｒｏｐｅｒｔｉｅｓａｎｄＭｉｃｒｏｓｔｒｕｃｔｕｒｅｓｏｆＴｈｒｅｅＫｉｎｄｓｏｆＳｉｌｖｅｒｓｈｅａｔｈｅｄＢｉ－２２２３ＴａｐｅｓＺｅｎｇＲｏｎｇ；ＺｈｏｕＹｉｒｕ；ＹｅＢｉｎ；ＺｈｏｕＭｉｎ；ＺｈａｎｇＪｉａｎｇｕｏ（曾荣）（周贻茹）（叶斌）...     

提高金刚石工具电镀沉积速率的新工艺

本文从电镀理论分析入手，确定了影响沉积速率的因素，指出了常用的改进措施，并结合实际，提出了一套新的电沉积金刚石工具的工艺，该工艺通过提高镀液中主盐的浓度，不仅加快了电沉积的速率，而且改善了电镀层的质量。     

一种新的Kossel定向方法

本文提出一种新的Kossel定向方法。它只要求测出透射Kossel花样上的三个Kossel线交点之间的距离就能定向,从而减少了误差的来源,提高了定向精度。通常的透射Kossel照片定向误差为σ=±0.3°     

人工智能在冷轧带肋钢筋工艺参数优化中的应用

论述了人工智能在冷轧带肋钢筋工艺参数优化中的应用,首先利用神经网络建立起冷轧带肋钢筋工艺参数与产品抗拉强度之间关系的数学模型,然后用遗传算法对工艺参数优化。按优化后的工艺参数在某拉丝加工厂进行了大批量生产试验,产品的合格率达到98%以上,从而为控制冷轧带肋钢筋工艺参数提供了一条行之有效的途径。     

异形坯连铸坯壳应力与鼓肚变形分析

坯壳应力引起的鼓肚变形是影响铸坯质量的重要因素,为防止过大的鼓肚变形,依据湍动能理论、热流传递理论和粘弹性理论,建立了异形坯三维热-力耦合模型,开发了鼓肚分析软件,从而避免了漏钢事故的发生.该模型将温度场和应力场的计算相互耦合,交替进行.结果表明:异形坯截面最危险点位于腹板中部,其次为翼板中点,在两者相结合的圆角部,由于凝固坯壳比较薄,其应力值也比较大;当坯壳厚度小于20 mm时,两点的鼓肚变形量将分别超过其极限变形量,铸坯出结晶器时必然发生漏钢事故.该模型通过预测坯壳应力和鼓肚变形量为现场安全生产提供了理论依据.     

热处理工艺对低合金耐磨钢组织和性能的影响

研究了淬火和回火温度对低合金钢组织和力学性能的影响。结果表明:890℃保温1h后油淬,250℃×2h回火后,组织为回火马氏体+残奥+少量碳化物。洛氏硬度大于50HRC,冲击韧度大于40J/cm2,且冲击试样断口为韧性断口。     

ZrC含量对TiC基金属陶瓷组织和性能的影响

真空烧结制备了TiC-ZrC-Co-Ni系金属陶瓷,研究了ZrC对TiC基金属陶瓷显微组织和室温力学性能的影响。结果表明:未加ZrC的TiC基金属陶瓷的显微组织表现为经典的黑芯-灰壳组织,硬质相形状多为球形;而加入ZrC后的金属陶瓷随着ZrC加入量的增多,组织逐渐细化,硬质相形状大多数为方形,硬质相与粘结相界面呈现直线,在黑芯周围出现白色球状(Ti,Zr)C固溶体。由于Co、Ni对ZrC的润湿性不理想,金属陶瓷的致密度随着ZrC含量的增加而下降,室温力学性能(抗弯强度、硬度、断裂韧性)也随之降低。     

Analysis of Intermetallic Phases Formed on Surface Vapor Oxidized H13 Hot Work Steels in Molten Aluminum

In this paper, the author dipped surface vapor oxidized H13 steel specimens into 700℃ molten aluminum liquid for a certain period of time. Analyze the intermetallic phases formed on the H13 samples surface with optical microscope and X-ray diffraction method. The observation of immersion test sample's cross-section shows that Fe3O4 film will protect die substrate from molten aluminum erosion. The identification of the intermetallic phases reveals that they consist of 2parts, which is named as the composite layer and the compact layer. Further investigations are made in order to know the phase constituents of the 2 layers, they are Al8Fe2Si (outer composite layer), (AlCuMg) and Al5Fe2 (compact layer),respectively. The experimental results show that on the same specimen, a convex surface with bigger radius of curvature is more likely to be molten and the melting loss speed is also faster than a flat and smooth surface. The thickness of compact layer on a smooth surface is much bigger than that of the convex surface. Therefore, the author supposes the compact layer is favorable in stabilizing the die surface material from further melting loss, as their formation on the die surface, the melting loss speed will decrease.     

低温熔体获得方式对熔体温度处理效果的影响

利用熔体温度处理工艺研究了A3 5 6铝合金低温熔体的不同获得方式对其凝固组织的影响 ,用直接炉内保温和机械搅拌 2种方式改变低温熔体的结构 ,以获得理想的凝固组织。实验结果表明 ,熔体温度处理过程中 ,对低温熔体机械搅拌可以明显改善混合后熔体的组织形貌 ,使组织形貌由树枝晶转变为等轴晶 ;在搅拌基础上选取较低的低温熔体温度 ,能够得到很好的凝固组织。     

过共晶铝硅合金半固态浆料表观粘度研究

通过自制的双筒旋转粘度计对过共晶ZL117合金的表观粘度进行了研究。结果表明,随着保温温度的降低,即固相率的升高,ZL117合金浆料的表观粘度随之增加;随着搅拌电流的增加,其表观粘度先降低,在搅拌电流为14A左右时达到最低,然后增大;随着冷却速度的增大,其表观粘度增大。