Technological Evaluation of Nitrogen Containing Starch Derivatives as Sizing Agents

The structural changes brought about by introducing different nitrogen containing groups via cyanoethylation, carbamoylethylation and carbamation in the molecules of rice and maize starches and oxidized starches derived thereof and the onset of these changes on the technical properties of yarns sized with such starch products were investigated. It was found that the apparent viscosity of pastes prepared from those products depends on the nature of starch, the degree of oxidation prior to chemical modification, the nature of modification as well as the measuring conditions, i. e. the rate of shear and temperature. Cotton yarns sized using these starch derivatives were measured for yarn number, tensile strength, C.V.%, elongation at break and C.V.% in elongation. Besides, the weavability test expressed as the minimum number of cycles due to abrasion (St₁) and average number of cycles due to abrasion (St₆) were investigated. A comparison among modified starches prepared from rice starch would reveral that the highest value of St₁ is obtained with yarns sized using carbamoylethylated sample derived from unoxidized starch. With maize starch, on the other hand, the highest value of St₁ is obtained with cotton yarns sized using carbamoylethylated starch derived from starch oxidized by 1 g/l active chlorine.     

Investigation of structural,optical, electrical,and magnetic properties of Fe-doped La0.7Sr0.3MnO3 manganites

In this work, the physical properties of nanocrystalline samples of La_0.7Sr_0.3Mn_1−xFe_xO₃ (0.0 ≤ x ≤ 0.20) perovskite manganites synthesized by the reverse micelle (RM) technique were explored in detail. The phase purity, crystal structure, and crystallite size of the samples were determined using X-ray diffraction (XRD) and Fourier transform infrared (FTIR) spectroscopy. All the samples had rhombohedral crystal structure and crystallite size increased with increase in Fe content in La_0.7Sr_0.3MnO₃. The scanning electron micrographs (SEMs) exhibited smooth surface morphology and nonuniform shape of the particles. The optical properties studied using UV-visible absorption spectroscopy revealed a decrease in the absorbance and optical band gap with an increase in Fe content in La_0.7Sr_0.3MnO₃ compound. The temperature-dependent resistivity measurements revealed semiconducting nature of x = 0 and 0.1 samples up to the studied temperature range, while a metal-to-insulator transition was observed at higher Fe doping. Magnetic studies revealed weak ferromagnetism in all the samples and a reduction in the maximum magnetization with an increase in Fe content. A close correlation between electrical transport and magnetic properties was observed with the doping of Fe ion in La_0.7Sr_0.3MnO₃ at Mn site. These results advocate strong interactions associated with the double exchange mechanism among Fe³⁺ and Mn³⁺ ions.     

Analysis of illumination-intensity-dependent j–V characteristics of ZnO/CdS/CuGaSe2 single crystal solar cells

Current–voltage characteristics of ZnO/CdS/CuGaSe₂ single crystal solar cells measured at room temperature are investigated depending on illumination intensity. The characteristics can be described using the two-diode model, indicating two current transport mechanisms acting in the cells. The first and dominant mechanism is recombination of carriers at the interface between CdS and CuGaSe₂. The second one is recombination in the depletion region, which has been found to have a small effect on the solar cell photovoltaic performance. Both the diode ideality factor and the saturation current density of the dominant diode increase under illumination. A model based on interface recombination can explain these results. This model allows the estimation of diffusion voltage, capture cross-section of holes at the interface and mobility of electrons in the CdS layer.     

Impacts of conservation agriculture on soil aggregation and aggregate-associated N under an irrigated agroecosystem of the Indo-Gangetic Plains

We evaluated impacts of conservation agriculture (zero tillage, bed planting and residue retention) on changes in total soil N (TSN) and aggregate-associated N storage in a sandy loam soil of the Indo-Gangetic Plains. Cotton (Gossypium hirsutum) and wheat (Triticum aestivum) crops were grown during the first 3 years (2008–2011) and in the last year, maize (Zea mays) and wheat were cultivated. Results indicate that after 4 years the plots under zero tillage with bed planting (ZT-B) and zero tillage with flat planting (ZT-F) had 15 % higher TSN concentrations than conventional tillage and bed planting plots (CT-B) (0.63 g kg^?1 soil) in the 0–5 cm soil layer. CT-B plots had lower soil bulk density that ZT plots in that layer. Plots under ZT-B (0.57 Mg ha^?1) contained 20 % higher TSN stock in the 0–5 cm soil layer than CT-B plots (0.48 Mg ha^?1). However, tillage had no impact on TSN concentration or stock in the sub-surface (5–15 and 15–30 cm) soil layers. Thus, in the 0–30 cm soil layer, ZT-B plots contained 6 and 5 % higher (P > 0.05) TSN stock compared with CT-B (2.15 Mg N ha^?1) and CT-F (2.19 Mg N ha^?1) plots respectively after 4 years. Plots that received cotton/maize + wheat residue (C/M + W RES) contained 16 % higher TSN concentration than plots with residues removed (N RES; 0.62 g kg^?1 soil) in the surface (0–5 cm) layer. Plots with only cotton/maize residue (C/M RES) or only wheat residue (W RES) retention/incorporation had similar TSN concentrations and stocks in the subsurface layer. Plots under ZT-B also had more macroaggregates (0.25–8 mm) and greater mean weight diameter with lower silt + clay sized particles than CT-B plots in that layer. A greater proportion of large macroaggregates (2–8 mm) in the plots under C/M + W RES compared with N RES were observed. In the 5–15 cm soil layer ZT-B and C/M + W RES treated plots had more macroaggregates and greater mean weight diameter than CT-B and N RES treated plots, respectively. Because of the greater amount of large aggregates, plots under ZT-B and C/M + W RES had 49 and 35 % higher large macroaggregate-associated N stocks than CT-B (38 kg TSN ha^?1) and N RES (40 kg TSN ha^?1) plots, respectively, in the 0–5 cm soil layer, although aggregates had similar TSN concentrations in all plots. Both tillage and residue retention had greater effects on aggregate-associated N stocks in the 5–15 cm layers. In addition to N content within large macroaggregates, small macroaggregate-associated N contents were also positively affected by ZT-B and C/M + W RES. Tillage and residue retention interaction effects were not significant for all parameters. Thus, the adoption of ZT in permanent beds with crop residue addition is a better management option for improvement of soil N (and thus possibly a reduced dose of fertilizer N can be adopted in the long run), as the management practice has the potential to improve soil aggregation with greater accumulation of TSN within macroaggregates, and this trend would likely have additive effects with advancing years of the same management practices in this region.     

Correction to: Synthesis of Co3O4 @ Organo/Polymeric Bentonite Structures as Environmental Photocatalysts and Antibacterial Agents for Enhanced Removal of Methyl Parathion and Pathogenic Bacteria

Journal of Inorganic and Organometallic Polymers and Materials -     

One-pot lithium bromide-catalyzed reaction of polyoxyethylene diglycidyl ether with carbon disulfide: synthesis of new polyoxyethylene epoxyoxathiolane-2-thione

A simple and highly efficient regio- and chemio-specific synthesis of polyoxyethylene epoxyoxathiolan-2-thione was realized from a one-pot reaction of polyoxyethylene diglycidyl ether and carbon disulfide using lithium bromide as a catalyst. The unsymmetrical obtained products were fully characterized by ¹H, ¹³C NMR and high-resolution mass spectra data.     

In-vivo study of adhesion and bone growth around implanted laser groove/RGD-functionalized Ti-6Al-4V pins in rabbit femurs

Titanium surfaces were designed, produced, and evaluated for levels of osseointegration into the femurs of rabbits. A total of 36 Ti-6Al-4V pins (15 mm length, 1.64 mm diameter) were prepared into three experimental groups. These were designed to test the effects of osseointegration on laser grooved, RGD coated, and polished control surfaces, as well as combined effects. Circumferential laser grooves were introduced onto pin surfaces (40 μm spacing) using a UV laser (λ = 355 nm). The tripeptide sequence, Arginine-Glycine-Aspartic acid (RGD), was functionalized onto laser grooved surfaces. Of the prepared samples, surface morphology and chemistry were analyzed using scanning electron microscopy (SEM) and Immunoflourescence (IF) spectroscopy, respectively. The experimental pin surfaces were surgically implanted into rabbit femurs. The samples were then harvested and evaluated histologically. Sections of the sample were preserved in a methylmethacralate mold, sliced via a hard microtome, and polished systematically. In the case of the RGD coated and laser grooved surfaces, histological results showed accelerated bone growth into the implant, pull-out tests were also used to compare the adhesion between bone and the titanium pins with/without laser textures and/or RGD coatings.     

Novel dynamic semiempirical proton exchange membrane fuel cell model incorporating component voltages

This paper introduces a novel dynamic semiempirical model for the proton exchange membrane fuel cell (PEMFC). The proposed model not only considers the stack output voltage but also provides valid waveforms of component voltages, such as the no‐load, activation, ohmic, and concentration voltages of the PEMFC stack system. Experiments under no‐load, ramping load, and dynamic load conditions are performed to obtain various voltage components. According to experimental results, model parameters are optimised using the lightning search algorithm by providing valid theoretical ranges of parameters to the lightning search algorithm code. In addition, the correlation between the vapour and water pressures of the PEMFC is obtained to model the component voltages. Finally, all component voltages and the stack output voltage are validated by using the experimental/theoretical waveforms mentioned in previous research. The proposed model is also compared with a recently developed semiempirical model of PEMFC through particle swarm optimisation. The proposed dynamic model may be used in future in‐depth studies on PEMFC behaviour and in dynamic applications for health monitoring and fault diagnosis.