Synthesis of nanopowders with low agglomeration by elaborating Φ values for producing Gd2O3-MgO nanocomposites with extremely fine grain sizes and high mid-infrared transparency

Refining ceramic microstructures to the nanometric range to minimize light scattering provides an interesting methodology for developing novel optical ceramic materials. In this work, we reported the fabrication and properties of a new nanocomposite optical ceramic of Gd₂O₃-MgO. The citric acid sol-gel combustion method was adopted to fabricate Gd₂O₃-MgO nanocomposites with fine-grain sizes, dense microstructures and homogeneous phase domains. Nanopowders with low agglomeration and improved sinterability can be obtained by elaborating Φ values. Further refining of the microstructure of the nanocomposites was achieved by elaborating the hot-pressing conditions. The sample sintered at 65 MPa and 1300 °C showed a quite high hardness value of 14.3 ± 0.2 GPa, a high transmittance of 80.3 %–84.7 % over the 3?6 μm wavelength range, due mainly to its extremely fine-grain size of Gd₂O₃ and MgO (93 and 78 nm, respectively) and high density.     

一株产羧酸酯酶菌的鉴定及酯酶特征的研究

目的:鉴定中国白酒发酵过程中的微生物种类，研究关键酶的特征与作用机制有利于提高白酒的优质品率。方法:本研究用形态学和生理学、16S rRNA、gyr B基因和antiSMASH分析的方法对酒曲中的一株微生物进行了验证；对该菌株的特性进行了研究，采用分子建模的方法获得了羧酸酯酶的3D模型，用分子对接的方法探讨了该菌株的羧酸酯酶的机理。结果:该菌株为产羧酸酯酶的革兰氏阴性菌Pb1（MW580690）；该菌株呈现典型的S型生长曲线，产物曲线为S型，羧酸酯酶活化最优pH范围为5.0~9.0。分子对接结果显示Phe21A为该酶具有催化活性的主要氨基酸，水解三丁酸甘油酯为丁酸和甘油。分子对接结果显示三丁酸甘油酯经过构象变化被转移到催化中心后，进一步被加工；酶的亲水性和疏水性的相互作用表面有利于配体向下转移，进而从疏水性通道释放产物到的酶表面。结论:产羧酸酯酶的菌株为贝莱斯芽胞杆菌，并为羧酸酯酶水解三丁酸甘油酯类物质的底物识别、转移和催化机理提供了新的见解。     

Decreased CD10-positive granulocytes for the differential diagnosis of myelodysplastic syndrome

Myelodysplastic syndromes (MDS) are highly heterogeneous myeloid neoplasms, and a large number of patients are difficult to diagnose and classify by blood and bone marrow examination. As a surface marker of granulocyte, studies have shown CD10 can be used to define the degree of granulocyte maturation in MDS patients. However, whether it can be used for differential diagnosis of MDS and other hematological diseases remains inconclusive. To explore the value of CD10 for differential diagnosis of MDS, 60 newly diagnosed MDS, 20 aplastic anemia (AA) patients, and 35 iron-deficient anemia (IDA) patients were selected for this study. Bone marrow (BM) specimens were processed for surface marker analysis and labeled with pre-conjugated monoclonal antibodies. Stained cells were detected by flow cytometry. Our results indicated that CD10-positive granulocytes were significantly decreased in BM of MDS patients than AA and IDA patients, and the level of CD10-positive mature granulocytes was not associated with the clinical stages of malignancy. Receiver operating characteristic (ROC) areas under the curve (AUC) of CD10-positive granulocytes was 0.86 and 0.85, respectively, in MDS patients than the IDA group and AA group with good specificity and sensitivity. Further, CD10-positive granulocytes were increased after effective treatment. In conclusion, we found the decrease in CD10-positive granulocytes has a differential diagnostic value of MDS.     

An index structure supporting rule activation in pervasive applications

World Wide Web - Rule mechanism has been widely used in many areas, such as databases, artificial intelligent and pervasive computing. In a rule mechanism, rule activation decides which rules are...     

Characterizations of friction welding joint interface for AISI 316

Because of heat amount is different from peripheral to central of friction welding interface, which is leaded to vary the characterizations along that interface. Current study, respectively, focused on the effect of different friction pressure on micro-structural and mechanical properties of that friction welding joint interface. Presently, these friction pressures are 110, 130, 150 and 170 MPa while kept all other conditions constant. The effects of different friction pressure on welding interface characterization were investigated by EDX, SEM, tensile, compression, impact and hardness tests. The tensile tests carried out on the standardized test piece with diameter 6 mm and 8 mm, thus, compression tests were extracted from the positions of 0°, 45° 90° with test specimen of 4 mm diameter and 6.5 mm length at weld center. Whereas, the impact test pieces were picked up in two positions, the first one is symmetrical, which it obtained to the respect of the rotation axis and the interface, on the other hand, the second one is non-symmetrical with the axis of rotation and symmetrical to the interface, for making the notch head coincide with the center of the welded joint, The obtained results showed that with reducing of friction pressure will present lack of bonding increasing from peripheral toward the welding center, which will responsible on reducing of the mechanical properties such as tensile, compression and impact strength.     

床温及SNCR脱硝对CFB锅炉NOx和N2O排放影响的试验研究

为了研究循环流化床（CFB）锅炉燃用无烟煤时床温及选择性非催化还原（SNCR）脱硝对于NO和N2O排放的影响，在1 MW CFB试验装置上开展了试验研究。结果表明:床温由880 ℃提高到970 ℃，NO排放质量浓度由119.5 mg/m3上升到226.0 mg/m3，N2O排放质量浓度由216.0 mg/m3降低到102.2 mg/m3；在氨氮摩尔比（NSR）为0~3.7之间，随着NSR的提高，脱硝效率从0上升到50.72%；进一步提高NSR到5.2，脱硝效率升至53.61%，增加较为缓慢；随着NSR从0提高到1.7，N2O排放质量浓度由84.3 mg/m3上升至118.3 mg/m3，增长较为缓慢；进一步提高NSR至2.0，N2O排放质量浓度上升至187.7 mg/m3，增长速度提高；继续提高NSR至5.2，N2O排放质量浓度上升至381.4 mg/m3；CFB锅炉采用以尿素为还原剂的SNCR脱硝工艺时，单纯通过加大NSR来提高脱硝效率不仅效果有限，过量喷入的还原剂会造成N2O排放量的显著提高。     

蛋类礼盒包装结构的缓冲性能研究

目的研究蛋类礼盒包装结构的缓冲性能。方法以蛋类尺寸为基础,建立可发性聚乙烯(expandable polyethylene. EPE)缓冲单元结构和组合结构,进行静态仿真分析和实验验证,比较结构在形状、叠合层数、组合形式等参数变化时的载荷与位移。结果结构层数变化相同时,单元结构的极限载荷从143N增加到236 N,组合结构的极限载荷从224 N增加到476 N,均呈近线性增长。结论蛋类礼盒包装中,组合结构的承载能力优于单元结构,通过单元结构的组合,可满足不同蛋类的包装要求。