Direct ethoxylation of fatty methyl ester over Al-Mg composite oxide catalyst

For the purpose of estimating the reaction mechanism of the direct ethoxylation of a fatty ester in the presence of an Al-Mg composite oxide catalyst, a labeled fatty methyl ester C₁₁H₂₃CO¹⁸OCH₃ containing ¹⁸O isotope was synthesized and directly ethoxylated. The product was evaluated by gas chromatography-mass spectrometry (GC-MS). The GC-MS spectra showed that the ¹⁸O isotope label was present only in the methoxy group at the molecular end of the ethoxylated fatty methyl ester. This supports the reaction mechanism of coordination anionic polymerization where the bond between the acyl and methoxy groups of the fatty methyl ester molecule was broken, caused by the bifunctional effect of the acid-base active sites; an intermediate chemisorption species was formed; and then ethylene oxide was addition-polymerized sequentially, in parallel.     

Low-temperature selective reduction of NO with propene over alkaline-exchanged mordenites

Partially protonated alkaline mordenites showed higher activity per acid amount below 573 K than acidic zeolites for the selective reduction of NO with C₃H₆ in the presence of O₂, which can be related to a high concentration of NO₃ ^- species in the zeolite channels. This revised version was published online in July 2006 with corrections to the Cover Date.     

Effect of cell structure on oil absorption of highly oil absorptive polyurethane foam for on-site use

This article reports the effect of cell structure on oil absorption of highly oil-absorptive polyurethane foam (ON-PUR), which is suitable for on-site foaming. We have developed ON-PUR as an oil absorbing polyurethane foam using a very reactive recipe. ON-PUR was synthesized by mixing polyol, water, additives, and polymeric diphenylmethane diisocyanate (P-MDI) using a high-pressure foaming machine. Density, airflow, oil absorption of this foam, and cell structure by microscopy were measured. From these results, it was found that the airflow of this foam increased by crushing, and the oil absorption of this foam increased sharply in a narrow airflow range (from 0.1 to 0.8 scfm). This increase is estimated to be due to the decrease of closed cell structures by crushing treatment. Furthermore, we constituted on-site foaming system in bench scale, which was expected to be applicable to on-site preparation of ON-PUR. © 1997 John Wiley & Sons, Inc. J Appl Polym Sci 65: 179–186, 1997     

Improvement on sulfate resistance of blended cement with high alumina slag

This paper is focused on the effect of limestone and calcium sulfate content on sulfate resistance of ground granulated blast furnace slag (GGBS) blended cement. Sulfate resistance was evaluated using ASTM C 1012, and a variety of mechanisms of the sulfate resistance of GGBS blended cement were revealed by the analyses of hydration products and sulfate ion ingress. Although GGBS suppresses sulfate ion ingress, it is probable that alumina in GGBS tends to form ettringite with externally supplied sulfate ions. Addition of limestone and increase in calcium sulfate content allow both monocarboaluminate and ettringite to form prior to immersion in sulfate solution. These hydration products remain in the hardened cement matrix and act to suppress further formation of ettringite with external sulfate ions during immersion in sulfate solution. GGBS blended cement with a suitable amount of limestone powder and a controlled content of calcium sulfate exhibits markedly long term sulfate resistance.     

Synthesis of Red-Light-Responsive Pheophorbide-a Tryptamine Conjugated Photosensitizers for Photodynamic Therapy

Six methyl pheophorbide-a derivatives were prepared by linking a tryptamine side chain at the C-13 ¹ , C-15 ² and C-17 ³ positions of pheophorbide-a. P repared conjugates were characterized and evaluated for their photocytotoxicity against A549 cells. The conjugate 6 a with strong absorption at 413 nm (Soret band), 663–671 nm (Q bands) and comparable fluorescence quantum yield (0.26) was found to exhibit significant cytotoxicity (659 nM). Molecular integration of pheophorbide-a and tryptamines showed synergistic effects as the most potent conjugate 6 a was identified with enhanced photocytotoxicity when compared to methyl pheophorbide-a. T he conjugate 6 a was smoothly taken up by A549 cells and exhibited intracellular localization predominantly to lysosome in the cytoplasm. Upon photoirradiation 6 a generated singlet oxygen to show potent cytotoxicity toward A549 cells.     

Enhancing low-temperature energy harvesting by lead-free ferroelectric Ba(Zr0.1Ti0.9)O3

The energy-harvesting ability of the lead-free ferroelectric Ba(Zr,Ti)O₃ was investigated and greatly enhanced using the Kim novel electrothermodynamic cycle for low-temperature application. Ba(Zr,Ti)O₃ was synthesized with a Zr:Ti ratio of 10:90 (BZT10) by hot-press sintering, which exhibited a mix relaxor-ferroelectric behavior. For power generation using the Kim cycle with low and high temperatures of T_L = 25°C, T_H = 120°C, the most optimized temperature pattern occurred for a heating time of 12.5 s and a cooling time of 22.5 s. Under these conditions, the electric field increased during the novel isodisplacement process, and the displacement variation in the isoelectric step reached the highest value and maximized the BZT10 cycle loop area. Applying these conditions while lowering T_L to 20°C, an energy density N_D = 504 mJ/cm³ was achieved. This value is the highest obtained energy density in a practical test for lead-free ferroelectric bulk material in the BaTiO₃ family.     

Effect of microstructures on dielectric breakdown strength of sintered reaction-bonded silicon nitride ceramics

Silicon nitride (Si₃N₄) was prepared from silicon by a sintered reaction-bonded silicon nitride method using yttria and magnesia as sintering additives. Post-sintering (PS) of nitrided compacts was carried out at 1850°C under a nitrogen pressure of 1 MPa. Effect of PS time on microstructure and dielectric breakdown strength (DBS) of the prepared Si₃N₄ ceramics was evaluated. The DBS was measured using specimens with four different thicknesses (0.30, 0.20, 0.10, and 0.05 mm) in order to examine the thickness dependence. The porosity of the sintered Si₃N₄ decreased by prolonging the PS time, and the full density could be achieved at the PS time of over 6 h. After full densification, rod-like β-Si₃N₄ grains grew up, and their maximum grain size increased from 45.1 to 154.7 μm by prolonging the PS time from 6 to 48 h. The DBS of the thick Si₃N₄ substrates (0.30 mm) showed little variation from 35.4 to 47.0 kV/mm, regardless of the PS time. On the other hand, that of the thin ones (0.05 mm) dramatically decreased from 99.5 to 9.8 kV/mm with increased the PS time from 6 to 48 h. Because the DBS sharply decreased at the thin substrate sintered for longer time in which some large-elongated grains might span the substrate thickness-wise throughout, it was inferred that the interface between β-Si₃N₄ grains and grain boundary phase/intergranular glassy films might be a path of the dielectric breakdown.     

Shock-induced phase transition of oriented pyrolytic graphite to diamond at pressures up to 15 GPa

In studies of shock-induced phase transition of ordered pyrolytic graphite to a diamond-like phase, the lowest transition onset pressure was observed at 19.6 GPa. The phase transition in that case was considered to be martensitic. In the present study ordered pyrolytic graphite with voids between particles was loaded at pressures up to 15 GPa using a planar shock wave propagating along the basal plane of the graphitic crystal structure. As a result, both diamond-like carbon and diamond were observed in the postshock sample. The phase transition of graphite to diamond was assumed to occur by the release of distortional energy stored in the graphite particles, that is, diffusional-controlled reconstructive mechanism, on the basis of the data by high resolution electron microscopy together with electron energy loss spectroscopy.     

Dietary conjugated linolenic acid in relation to CLA differently modifies body fat mass and serum and liver lipid levels in rats

The present study compared the effect of dietary conjugated linolenic acid (CLNA) on body fat and serum and liver lipid levels with that of CLA in rats. FFA rich in linoleic acid, α-linolenic acid, CLA, or CLNA were used as experimental fats. Male Sprague-Dawley rats (4 wk old) were fed purified diets containing 1% of one of these experimental fats. After 4 wk of feeding, adipose tissue weights, serum and liver lipid concentrations, serum tumor necrosis factor (TNF)-α and leptin levels, and hepatic β-oxidation activities were measured. Compared with linoleic acid, CLA and, more potently, CLNA were found to reduce perirenal adipose tissue weight. The same trend was observed in the weight of epididymal adipose tissue. CLNA, but not CLA, was found to significantly increase serum and liver IG concentrations. Serum FFA concentration was also increased in the CLNA group more than in the other groups. The activity of β-oxidation in liver mitochondria and peroxisomes was significantly higher in the CLNA group than in the other groups. Thus, the amount of liver TG exceeded the ability of hepatic β-oxidation. Significant positive correlation was found between the adipose tissue weights and serum leptin levels in all animals (vs. perirenal: r=0.557, P<0.001; vs. epididymal: r=0.405, P<0.05). A less significant correlation was found between adipose tissue weights and serum TNF-α level (vs. perirenal: r=0.069, P<0.1; vs. epididymal: r=0.382, P<0.05). Although the mechanism for the specific effect of CLNA is not clear at present, these findings indicate that in rats CLNA modulated the body fat and TG metabolism differently from CLA.     

Production of 5,8,11-cis-eicosatrienoic acid by a Δ12-desaturase-defective mutant ofMortierella alpina 1S-4

A mutant defective in Δ12-desaturase of an arachidonic-acid producing fungus,Mortierella alpina 1S-4, was shown to be a novel potent producer of Mead acid (5,8,11-cis-eicosatrienoic acid, 20:3ω9). The fungus produced several fatty acids of the n-9 family,i.e., 6,9-cis-octadecadienoic acid (18:2ω9), 8,11-cis-eicosadienoic acid (20:2ω9) and 20:3ω9. Significantly high levels of these fatty acids were produced during growth at low temperatures (12–20°C). On submerged cultivation at 20°C for 10 days in a 5-L fermenter containing 2% glucose plus 1% yeast extract (pH 6.0), the production of 20:3ω9 reachedca. 0.8 g/L (56 mg/g dry mycelia), accounting for 15% (by wt) of the total mycelial fatty acids. The other major fatty acids were palmitic acid (6%), stearic acid (11%), oleic acid (45%), 18:2ω9 (12%) and 20:2ω9 (3%). Studies on the distribution of fatty acids among lipid classes showed that, irrespective of the growth temperature employed (12–28°C),ca. 70% (by mol) of 20:3ω9 was present in the triglyceride and the remainder in the phospholipid fraction, especially in phosphatidylcholine (PC). When the fungus was grown at 12°C, the proportion of 20:3ω9 in the PC fraction wasca. 55%. On leave from Suntory Ltd.