Electro-rheological effect and dynamic rheological properties of a blend composed of two liquid crystalline materials with different molecular weight

Electro-rheological (ER) effect of a blend composed of two liquid crystalline materials with different molecular weights is described in this article. The results indicated that ER effect of the blend was observed at the temperature range where each neat sample did not show ER effect. Furthermore, both storage modulus (G′) and loss modulus (G″) decreased drastically at the temperature range for the blend in dynamic viscoelastic measurements. We show that steady ER effect could be obtained by using a blend made up of two liquid crystalline components, whereas remarkable increment in shear stress was not observed for each component under applied electric field.     

Hydrothermal Formation of Hydroxyapatite Layers on the Surface of Type-A Zeolite

Type-A zeolite evenly covered with hydroxyapatite thin layers was prepared using hydrothermal treatment at 120°C for 8 h under autogenous pressure. The hydroxyapatite needlelike nanocrystals, 100–200 nm in diameter and 30 nm in thickness, were grown under the reaction between discharged Ca²⁺ ions from type-A zeolite and PO₄³⁻ ions in (NH₄)₃PO₄ solution. The preferential orientations of the c -axis of hydroxyapatite crystals perpendicular to a zeolite surface were observed using transmission electron microscopy. The crystal structure of type-A zeolite was not destroyed under the reaction, but the surface morphology was changed only with complete covering of scaly hydroxyapatite particles.     

Bromine addition and successive amine substitution of mesoporous ethylenesilica: Reaction, characterizations and arsenate adsorption

Bromination and subsequent ethylenediamine substitution of the CC double bond in mesoporous ethylenesilica were carried out to explore the characteristics of this periodic mesoporous organosilica. The structures of the products (BrPMO and EDA–BrPMO, respectively) were analysed by IR, Br K-edge EXAFS and NMR spectroscopies, as well as X-ray diffraction and nitrogen adsorption. We showed (1) that the formulae of the two products that formed were [CHBrSiO_1.5]_0.45[CHSiO_1.5]_0.55 and [NH₂CH₂CH₂NHCHSiO_1.5]_0.05 [CHBrSiO_1.5]_0.40[CHSiO_1.5]_0.55, respectively, (2) that the addition of Br₂ at room temperature occurred on the CC double bonds with disturbing the framework structure, (3) that IR absorption band of CC bonds that reacted with Br₂ is significantly different from that of inactive CC bond, (4) that the length of the C–Br bond was considerably longer than in conventional alkyl bromides, and (5) that a large proportion of the ν(C–Br) band remained at the same position in the IR absorption spectrum after the ethylenediamine (EDA) substitution, while a new ν(C–Br) absorption also appeared. The mechanisms of these reactions are discussed at both the micro and mesoscopic levels.

Arsenate adsorption on EDA–BrPMO, in which the EDA is directly bound to the “surface” of the mesopores, was compared with adsorption on EDA–Pr–PMO, which was prepared by the direct synthesis of 3-chloropropyl-functionalized mesoporous ethanesilica followed by the substitution of Cl with EDA. The strength of the adsorption, as measured with the distribution coefficient, was greater for the former adsorbent than the latter. The origin of this difference was attributed to the distance between amino group and the surface.     

Synthesis and luminescence properties of Pr3+ doped CaxBa1?xTiO3 (0.3?x<1) fine particles

Ca _x Ba_1−x TiO₃ (CBT) fine particles doped with red luminescence center of Pr³⁺ ions (Pr: CBT) were successfully synthesized by salt assisted spray pyrolysis (SASP) process. Scanning electronic microscope (SEM) and laser scattering analysis demonstrate that salt can be removed from the surface of particles by washing with Milli-Q water and the particles can be further separated by ball-milling to get well-dispersed Pr³⁺ ions doped CBT fine particles. The luminescence properties, such as photoluminescence (PL) and mechanoluminescence (ML), of as-synthesized Pr: CBT particles were investigated. For Pr: CBT fine particles with different Ca molar ratios, all the samples show one emission at 612 nm, with increasing Ca molar ratio, PL intensity of Pr: CBT fine particles become stronger and stronger. When pressure was loaded on the Pr: CBT pellet, mechanoluminescence(ML) emission was measured. The results show that the ML intensity is proportional to the applied pressure.     

Synthesis of High Density and Transparent Forsterite Ceramics Using Nano-Sized Precursors and Their Dielectric Properties

Forsterite (Mg₂SiO₄) ceramics were prepared using Mg(OH)₂ and SiO₂ as precursors, and the effect of powder characteristics of Mg(OH)₂ on calcination and sintering was investigated. The use of highly dispersed Mg(OH)₂ powder (HD powder) resulted in a lower calcination temperature. Forsterite powder of high homogeneity and small particle size prepared from the HD powder enabled synthesis of high-density forsterite ceramics by ordinary sintering without applying external pressure. Moreover, transparent forsterite ceramics were successfully synthesized through addition of excess Mg to the precursors to compensate for Mg evaporated during the sintering process. Subsequent dielectric measurements revealed that the transparent forsterite ceramics had a very low dielectric loss (tan δ<10⁻⁴).     

A facile antistatic modification of polyester fiber based on ion-exchange reaction of sulfonate-modified polyester and various cationic surfactants

A new technique for imparting antistatic properties to poly(ethylene terephthalate) (PET) fiber has been developed. In this technique, blend polyester fibers containing poly(ethylene terephthalate/5-sulfoisophthalate) (SIP-PET) were prepared by blend spinning and then treated with various cationic surfactants in the process of dyeing. The surfactants could effectively be immobilized on the fiber as the counter cations of the sulfonate groups of the 5-sulfoisophthalate (SIP) units and aid the release of static electrons formed in the fiber. Thus, the half-life time (t_1/2) of leakage of static charge and the surface resistivity (Rs) of the blend PET fibers became much lower after treating. The best result was obtained with a methylated quaternary ammonium salt of a stearylamine-ethylene oxide (EO) adduct or hydrochloride of a laurylamine-EO adduct as the surfactant of which the number of EO units was around ten. Even after five washing cycles the t_1/2 value of the fibers treated with these surfactants was kept lower than 30 s with the Rs value maintained in the order of 10¹³ Ω cm^-2. Therefore, the present technique could be useful for practical production of polyester fibers with “semi-permanent” antistatic properties which can be recovered by re-treatment even if they were lost.     

Machining accuracy for shearing process of thin-sheet metals—Development of initial tool position adjustment system

In the shearing process, clearance has a significant effect on machining accuracy. However, the relationship between uneven clearance caused by misalignment of tool position and machining accuracy remains unclear. This is attributed to the fact that, previously, the effect was small because the thickness of the workpiece was not so thin, and a method for precisely measuring and adjusting the tool position had not been established. Therefore, in the present study, a new method of adjusting the initial tool position is developed. In addition, punching experiments are conducted under the condition that the initial tool position is adjusted to an accuracy of 2 μm or better, and the effects of clearance on machining accuracy, shape of cross-section, and diameter of hole, are investigated in three types of materials. From these results, the importance of adjusting the initial tool position is clarified.     

Methanation of CO2 with the oxygen-deficient Ni(II)-ferrite under dynamic conditions

The continuous methanation of CO₂ has been accomplished over hydrogen-reduced Ni(II)-bearing ferrite (Ni_xFe_3–xO_4–; x=0.39, > 0) in a mixed gas flow of CO₂ and H₂ at 250–375 °C. The yield and the selectivity for the methanation were larger than 50% and 95%, respectively, at the initial stage of the process. They decreased to 31% and 89%, respectively, after 6 h methanation. The innovative results can be ascribed to the use of the new material; hydrogen-reduced Ni(II)-bearing ferrite. Its formation was evinced by chemical analyses and the increase in the lattice constant; the lattice constant of the Ni(II)-bearing ferrite (a₀ 0.8375 nm) was enlarged to 0.8379 nm by hydrogen reduction. The enlarged lattice constant was not changed during the methanation. These findings suggest that the methanation occurs at the oxygen-deficient site of the hydrogen-reduced Ni(II)-bearing ferrite, as well as the formation of water by combination of the incorporated oxygens with hydrogen. The methanation consists of three steps of the elementary reaction. First, the oxygen-deficient sites are formed by hydrogen reduction; second, CO₂ is reduced to elementary carbon and two oxygen ions which are incorporated into the oxygen-deficient sites; and third, the carbon deposited on the surface of the reduced ferrite is selectively hydrogenated to CH₄.     

Template‐Free Fabrication of Mesoporous Alumina Nanospheres Using Post‐Synthesis Water‐Ethanol Treatment of Monodispersed Aluminium Glycerate Nanospheres for Molybdenum Adsorption

This work reports the template‐free fabrication of mesoporous Al₂O₃ nanospheres with greatly enhanced textural characteristics through a newly developed post‐synthesis “water‐ethanol” treatment of aluminium glycerate nanospheres followed by high temperature calcination. The proposed “water‐ethanol” treatment is highly advantageous as the resulting mesoporous Al₂O₃ nanospheres exhibit 2–4 times higher surface area (up to 251 m² g^?1), narrower pore size distribution, and significantly lower crystallization temperature than those obtained without any post‐synthesis treatment. To demonstrate the generality of the proposed strategy, a nearly identical post‐synthesis “water treatment” method is successfully used to prepare mesoporous monometallic (e.g., manganese oxide (MnO₂)) and bimetallic oxide (e.g., CuCo₂O₄ and MnCo₂O₄) nanospheres assembled of nanosheets or nanoplates with highly enhanced textural characteristics from the corresponding monometallic and bimetallic glycerate nanospheres, respectively. When evaluated as molybdenum (Mo) adsorbents for potential use in molybdenum‐99/technetium‐99m (⁹⁹Mo/^99mTc) generators, the treated mesoporous Al₂O₃ nanospheres display higher molybdenum adsorption performance than non‐treated Al₂O₃ nanospheres and commercial Al₂O₃, thereby suggesting the effectiveness of the proposed strategy for improving the functional performance of oxide materials. It is expected that the proposed method can be utilized to prepare other mesoporous metal oxides with enhanced textural characteristics and functional performance.