大型球磨机衬板材料的研究和应用

研究成功了一种适合于制造大型球磨机衬板的新材料.在不含钼、镍等贵重合金元素前提下,设计的中碳钢以硅、锰、铬为主要合金元素,并加入少量钛、钙、硼、钇、钾、钠等元素,改善钢的组织和淬透性.新材料具有足够的淬透性和淬硬性,经油冷淬火和中温回火处理后,硬度大于55 HRC,冲击韧性大于25 J/cm2,断裂韧性大于40 MPa·m1/2.用于制造大型球磨机衬板,耐磨性比高锰钢衬板提高1倍以上,生产成本降低15%,具有很好的经济效益.     

无氰电刷镀金技术在航天工业中的应用

应用FJY-18无氰电刷镀金技术制得的金镀层具有孔隙率低、色泽金黄、光亮、结合力好,镀厚能力大于20μm,显微硬度HV=130～150,施工温度范围宽、无毒等特点,该技术已用于航天工业中某一关键部件的表面减磨密封镀金.     

反应溅射非晶态氧化铝薄膜SCIEI

研究了平面磁控直流反应溅射法沉积氧化铝薄膜的过程。结果表明氧分压大小对反应溅射过程有决定性作用,当氧分压增大或减小过程中存在两个阈值。氧分压小于阈值为金属Al溅射区,大于阈值为氧化铝溅射区。在阈值附近总气压、溅射电压和沉积速率发生突变,溅射特性(V-J)曲线有不同规律。沉积的氧化铝膜为非晶态,高温下可晶化,本文还讨论了反应溅射的机理。     

Influence of Electrolyte Composition on the Calcium-Phosphorus compound Coating on Titanium Substrate by Micro-arc Oxidation

In recent years the biomedical material has been widelydeveloped,and application that the implant materialssubstitute for hard organ has attracted much attention.Titanium alloys are frequently utilized as skeletonimplant and modification materials because of theirlight density,high strength and proper biocompatibility.However,titanium alloys are bioinertial materials,which are not beneficial to the performance of organiccoalescence,so they are not yet the ideal implantmaterials.Therefore,impro…     

聚氧化乙烯改性水玻璃粘结剂的研究

确定了聚氧化乙烯改性水玻璃粘结剂的基本组分,测试了有机酯自硬和CO2气硬型砂的常温粘结强度和高温残留强度。研究发现,在水玻璃中加入聚氧化乙烯树脂能改善水玻璃的老化现象,充分发挥其粘结效率;粘结剂加入量相同时,型砂强度是普通水玻璃砂的1.5倍,800～1000℃时,型砂残留强度≤0.5MPa。结果表明,聚氧化乙烯改性水玻璃粘结剂加入量低,型砂工艺性能良好,浇注后出砂容易,有利于旧砂进一步干法回用。     

Synthesis and characterization of LiNi0.95-xCoxAl0.05O2 for lithium-ion batteries

Samples of LiNi0.95-xCoxAl0.05O2 （x = 0.10 and 0.15） and LiNiO2, synthesized by the solid-state reaction at 725℃ for 24 h from LiOH-H2O, Ni2O3, Co2O3, and AI（OH）3 under an oxygen stream, were characterized by TG-DTA, XRD, SEM, and electrochemical tests. Simultaneous doping of cobalt and aluminum at the Ni-site in LiNiO2 was tried to improve the cathode performance for lithium-ion batteries. The results showed that co-doping （especially, 5 at.% A1 and 10 at.% Co） definitely had a large beneficial effect in increasing the capacity （186.2 mA.h/g of the first discharge capacity for LiNio.s.42OoaoAlo.0502） and cycling behavior （180.1 mA-h/g after 10 cycles for LiNio.85CooaoAlo.osO2） compared with 180.7 mA.h/g of the first discharge capacity and 157.7 mA.h/g of the tenth discharge capacity for LiNiO2, respectively. Differen- tial capacity versus voltage curves showed that the co-doped LiNio.95_xCoxmlo.osO2 had less intensity of the phase transitions than the pristine LiNiO2.     

PLC在DU型多功能组合机床电控系统改造中的应用

从机床自动控制的实际需要出发，以DU型多功能组合机床为例，介绍了一种利用PLC的顺序编程控制功能来改造机床电控系统的具体方法。     

影响Ti合金热稳定性的因素

综述了合金元素、环境气氛、相变、涂层等因素对Ti合金热稳定性的影响.     

乙醇冷媒液中复配缓蚀剂的研究

通过失重法测定了A3钢、铜、铝在20%乙醇冷媒液中的腐蚀速率和复配缓蚀剂的缓蚀效果，筛选出不含 NO-2的复配缓蚀剂.该缓蚀剂可以有效减缓碳钢、不锈钢、紫铜和铝合金材料在乙醇冷媒液中的腐蚀，同时提高冷媒液的稳定性，改善其冰点和沸点.     

Al—Li—Cu—Mg合金应力腐蚀性能及机理研究

利用恒应变速率方法研究了Al—Li—Cu—Mg合金的应力腐蚀开裂,包括时效条件及外加电位对应力腐蚀的影响,同时研究了试样表面相对氢浓度与外加电位及应力腐蚀时间的关系,实验结果表明,合金的应力腐蚀性能取决于时效条件,其中峰时效条件下最差,自然时效条件下最好,应力腐蚀敏感性及试样表面氢浓度与外加电位有关,阳极电位增加应力腐蚀敏感性,阴极电位低于临界电位时加速应力腐蚀,认为合金在应力腐蚀过程中阳极溶解与氢脆机制联合作用。