过共晶高硅铸造铝合金磷－稀土双重变质处理

采用正交实验方法研究了磷、混合稀土变质剂添加量和变质处理温度对Ａｌ－２２Ｓｉ－２ｃｕ－０．９Ｍｇ－１．０Ｎｉ过共晶高硅铸造铝合金变质效果的影响。结果表明：磷、稀土的添加量和磷变质处理温度对合金的变质效果起决定作用；稀土添加量对合金室温抗拉强度无明显影响，但能显著提高其高温强度；合金变质处理的最佳工艺如下：磷添加量为０．１％，稀土添加量为０．６％，磷变质温度为８３０℃，稀土变质温度为８１０℃。     

High cycle fatigue and fracture behavior of 2124-T851 aluminum alloy

The high cycle fatigue properties and fracture behavior of 2124-T851 aluminum alloy were investigated roundly, including the fatigue crack growth rate, fracture toughness and fatigue S--N curve. Furthermore, the fatigue crack growth rate was analyzed by fitting the curves. And the microstructure of the alloy was studied using by optical microscopy, transmission electron microscopy and X-ray diffractometry, scanning electron microscop1/2 The results show that the fatigue strength and the fracture toughness of 2124-T851 thick plate are 243 MPa and 29.6 MPa.m at room temperature and R=0. 1, respectively. At high cycle fatigue condition, the characteristics of fatigue facture were observed obviously. And the higher the stress amplitude, the wider the space between the fatigue striations, the faster the rate of fatigue crack developing and going into the intermittent fracture area and the greater the ratio between the intermittent fracture area and the whole fracture area.     

F6-21Ni-4Mn合金强脉冲磁场诱发马氏体相变的研究SCIEI

采用磁性测量、光学金相和强脉冲磁场,研究了Fe-21Ni-4Mn合金的磁场诱发马氏体相变。发现在M_s点以上,当施加的磁场高于某一临界值(临界磁场)时,便能诱发马氏体相交;临界磁场随温度的升高而增加,并与ΔT(T-M_s)成直线关系;脉冲磁场强烈地促进变温转变,抑制等温转变;磁场对Fe-21Ni-4Mn合金的马氏体相变作用主要是Zeeman效应,求得在M_s点变温的熵变ΔS_(M_S)^(1t)为·13J/mol·K·同时发现磁场诱发的马氏体形貌为板条伏、片状和蝶状,其形成量随施加的最大磁场强度成线性增加。     

铂类抗癌配合物构效关系的理论探讨

基于铂抗癌配合物在体内的历程和化学反应探讨了它们的结构和活性之间的关系，获得决定抗癌活性大小的主要因素，包括配合物分子的脂溶性和空间体积、构型、离去基团的反应性以及载体基团的特性。提出了铂配合物具有较高抗癌活性的结构要求①非离子型②小的空间体积③顺式构型④含脂溶性的氨（胺）载体和以Ｃｌ￣（－）或二元羧酸作离去基团。     

In-plane anisotropy of 1545 aluminum alloy sheet

1　INTRODUCTIONThe in plane anisotropy of mechanical proper ties brings the limitation to the use of alloy sheet.At the same time, during the material processing,the difficulties of contour machining will also be in creased. For this reason, when designing high performance aluminum alloy sheets, the in planeanisotropy is an important performance parameterthat must be considered. Studies have shown thatminor Sc and Zr in the Al Mg Mn alloy can refinegrains of cast ingot, inhib…     

热风炉胆的失效原因及修复

我厂现有2台5t/h 大排距双层送风热风冲天炉。热风平均温度180℃,铁水平均温度为1455℃。密筋式热风炉胆离最高(?)排风口1m,炉胆平均寿命1000多小时。我们发现,炉胆长时间使用后,除在内胆下部出现纵向裂纹外,还出现“鼓肚”现象,甚至出现焊缝开裂,造成热风炉胆的失效,炉况变坏。     

油管损伤的磁性检测法及其实现技术

实施油管的现场探伤对防止油管泄漏或断裂事故的发生具有十分重要的意义。提出一种适于对油管损伤进行现场检测的磁性检测法并设计了多传感器子系统，它用一个包含霍尔传感器和聚磁器的聚磁检测单元阵列实现了局部损伤和壁厚损伤的综合检测。该多传感器子系统具有损伤分辨力高、效率高、结构简单及现场适应性强等特点，已成功应用于基于磁性传感器信息融合的油管损伤在役检测系统中。     

Fe76.5Cu1Si13.5B9非晶合金晶化过程的X射线衍射研究

Fe_(76.5)Cu_1Si_(13.5)B_9非晶合金在晶化过程中析山的α-Fe固溶体(α相)的X射线衍射峰存在不对称性并随退火温度而变化,对α相衍射峰进行分峰拟合证实,Cu原子可以促进α相形核并固溶其中,合金晶化与原始态中残存晶核无关,α相晶粒中Cu含量的不同导致衍射峰的不对称性,键合能准化学近似计算结果表明,Cu原子降低了周围原子的迁移势垒,导致合金的晶化首先在含Cu量较高的区域开始,使晶化温度降低。     

表面纳米化对1Cr17不锈钢耐氧化性的影响

用热重仪（TGA）、X-射线衍射（XRD）、扫描电镜（SEM）及其能谱（EDX），研究了表面纳米化对1Cr17不锈钢在700℃水蒸气中耐氧化性的影响。氧化动力学表明，在氧化开始阶段，表面纳米化后氧化速度高于原始样品，与传统喷丸处理后的耐氧化性能相当，但在氧化2小时时就很快达到钝化，氧化速度明显低于原始样品和经传统喷丸的样品。无论是否纳米化处理和经过传统喷丸处理，高温氧化时都在表面部形成T（FeCr）2O3型氧化物。但表面纳米化后由于表层高密度的晶界为Cr原子的扩散提供了快速通道，使得（FeCr）203型氧化物中Cr的浓度迅速提高，形成了致密的Cr2O3层，使得耐氧化性能提高。     

半固态连铸坯料质量及其影响因素研究

采用自行设计的半固态连铸机进行了铝合金半固态棒坯的连铸试验研究,给出了判定触变成形用半固态坯料质量好坏的若干标准,并对影响半固态坯料质量的关键因素(搅拌强度、连铸速度、冷却强度及电磁搅拌区域的温度梯度)及其相互关联性进行了分析讨论.