The superplastic deformation of electron beam welded aluminum lithium alloy

The superplastic deformation behavior and microstructure evolution of electron beam welded 5A90 aluminum lithium alloy were investigated. The results indicated that the electron beam weld joint had good superplasticity under a suitable deformation condition. The elongation increased first and then decreased with increasing deformation temperature and initial strain rate,and the maximal elongation of 171.1% was obtained at the temperature of 450 ℃ and the strain rate of 5 × 10~(-3) s~(-1).The microstructure observation indicated that the fine equiaxed dendrite of weld bead transformed into coarse equiaxed in the initial stage( strain ε≤0.7),then refined in the later stage of superplastic deformation.The eutectic structure gradually decreased with the increase of strain. While the microstructure of HAZ was refined and equiaxed with the increase of strain.     

基于触摸屏的点焊人机界面设计

本文以触摸屏为研究对象,设计出了精美、实用、多窗口的人机界面。研究结果表明：所组成的触摸屏控制系统电气连接简单、功能完善、运行稳定,通过对人机界面的操作可运行设备的各项功能。     

Fe颗粒含量对Sn35Bi/Cu钎焊接头组织性能影响

采用扫描电镜(SEM)、能谱仪(EDS)以及万能力学试验机等研究了Fe颗粒含量对Sn35Bi-xFe/Cu钎焊接头组织和性能的影响,并研究了Fe颗粒含量对Sn35Bi-Fe合金钎料的铺展面积和润湿性的影响.结果表明:向Sn35Bi合金钎料中加入少量Fe颗粒,会在Fe颗粒周围生成很薄的FeSn2化合物,降低固相/液相的界...     

置氢TC4钛合金激光焊接接头超塑变形组织均匀性分析

文中采用置氢处理的方式对钛合金激光焊接接头超塑性变形组织均匀性展开研究,研究不同的置氢量对TC4钛合金激光焊接头变形均匀性和组织均匀性的影响,并引进变形不均匀性系数和组织均匀化系数来进行表征. 结果表明,置氢可以调节钛合金激光焊接接头中相组成,改善焊接接头超塑性变形均匀性. 随着置氢量的增大,组织均匀化系数越大,组织均匀化程度越高;在相同置氢量,变形温度的升高或初始应变速率的降低均会使均匀化程度上升,并在置氢量1.30%、变形温度920 ℃、应变速率1×10-4s-1的条件下接头组织均匀化系数达到了95%.     

Co颗粒含量对SnBi/Cu接头微观组织与性能的影响EI北大核心CSCD

采用扫描电镜(SEM)观察Sn35Bi-x Co(x=0%,0.3%,0.7%,1.0%,1.2%,1.5%,质量分数,下同)复合钎料/Cu接头的微观组织,结合能谱(EDS)和XRD分析,研究接头组织差异。利用万能试验机测试接头力学性能,研究Co颗粒含量对SnBi/Cu接头组织及性能的影响机制。结果表明:随Co颗粒含量增加,Sn35Bi-Co复合钎料的润湿性呈现先增大后降低的趋势,当Co颗粒含量为0.7%时,润湿性最佳;在凝固阶段,向Sn35Bi/Cu接头中加入适量的Co颗粒后,能有效细化焊缝组织,界面IMC层更为平坦,焊缝中Co原子置换界面Cu_(6)Sn_(5)层中Cu原子,生成(Cu,Co)_(6)Sn_(5)固溶体,对界面IMC层具有固溶强化作用;Sn35Bi-Co/Cu接头的抗剪强度随Co颗粒含量增加先增大后降低,当Co颗粒含量为0.7%时,获得最大值54.09 MPa。     

Fe颗粒对时效过程中SnBi/Cu接头组织及性能影响

针对SnBi/Cu接头在服役过程中组织和性能变差的问题,通过用扫描电镜(SEM)观察时效前后Sn35Bi-1Fe/Cu接头组织,结合EDS和XRD分析,分析接头组织变化;利用万能试验机,测试接头力学性能,研究Fe颗粒对时效过程中SnBi/Cu接头组织及性能影响. 结果表明,焊后Sn35Bi-xFe/Cu (x = 0%,0.3%,0.7%,1.0%和1.5%)接头的抗剪强度随Fe颗粒含量先增加后降低. 当Fe颗粒含量为1% (质量分数,%)时,取得最大值50.23 MPa,且Sn35Bi-1.5Fe/Cu接头的力学性能依旧比Sn35Bi/Cu接头好;在恒温时效阶段,Sn35Bi-1Fe/Cu接头中Fe颗粒通过对Bi相的钉扎作用,以及与Sn反应生成FeSn₂化合物,消耗晶界能量,降低Bi相的迁移速率,抑制Bi相粗化,还能有效降低界面IMC层的生长速率,抑制界面Cu₃Sn的生成,改善接头在服役阶段的力学性能.     

焊丝成分对铝/铜激光熔钎焊接头组织和性能的影响

通过添加Zn-Al焊丝成功实现了2A16铝合金/T2铜异种材料的激光熔钎焊连接,并采用扫描电子显微镜和能谱仪对接头的微观组织进行表征,同时,研究了Zn-2％Al,Zn-5％Al和Zn-10％Al?3种焊丝对接头成形、微观组织以及力学性能的影响.结果表明,铝/铜激光熔钎焊接头主要由CuZn相,Al2Cu相,Al4Cu9相...     

激光叠焊接头显微组织及力学性能分析

采用OM,SEM分析了TC4钛合金激光叠焊接头各部分显微组织特征,研究了接头力学性能.结果表明,TC4钛合金激光叠焊接头显微组织由焊缝及热影响区组成,焊缝为针状马氏体α'交织成的网篮状组织.0.8 mm厚TC4钛合金薄板激光叠焊最佳工艺参数为功率1 800～2 350 w,焊接速度为1.5～2.5 m/min,此时拉伸试样平均单位长度焊缝承载力为458 N/mm,连接焊缝最大抗剪强度达732 MPa.拉伸过程焊缝截面轴线偏转角θ与接头承载能力相关,θ角越大,接头承载能力越强.     

树脂基CFRP/金属异种材料激光连接工艺研究现状

树脂基碳纤维增强复合材料(CFRP)作为新型轻质结构复合材料,广泛应用于航空航天器件的零部件中.CFRP与航空常用金属传统连接主要有胶接和机械连接,但具有一定的局限性.激光连接技术具有能量密度高,可控性好等特点,可用于复合材料和金属的连接.本文针对当前树脂基CFRP与金属(铝合金、钛合金、钢等)激光连接接头成形机理以及...     