焦磷酸钠在混凝土模拟孔溶液中的缓蚀性能

采用动电位极化曲线和电化学阻抗谱研究了焦磷酸钠在模拟混凝土孔溶液中对钢筋的保护作用。焦磷酸钠的加入导致混凝土中钢筋的腐蚀电位正移,主要通过抑制钢筋的阳极电化学过程起缓蚀作用。其缓蚀效果随焦磷酸钠浓度的增加而增大,在含0．04mol／L Cl-的混凝土模拟液中,当焦磷酸钠浓度为0．03mol／L时,其缓蚀效率可达到97．...     

电沉积溶液浓度及温度对修复混凝土裂缝的影响

研究了电沉积法修复混凝土裂缝中溶液浓度及温度的影响,测定了电沉积过程中的试件质量增加率、表面覆盖率、裂缝愈合率及裂缝填充深度.结果表明,表面覆盖率、裂缝愈合率随电沉积溶液浓度的增加而降低,而裂缝填充深度随浓度的增加而增大,质量增加率随浓度的变化无明显规律;表面覆盖率随电沉积溶液温度的升高而减小,裂缝愈合率随温度的升高而增大,质量增加率随温度变化的规律不明显,温度对裂缝填充深度的影响较小.     

电化学沉积法修复混凝土裂缝的研究进展

从电沉积法修复混凝土裂缝的机理、电沉积溶液的选择、电沉积效果的表征及其影响因素、电沉积方法修复后混凝土性能的改善4个方面论述了电化学沉积法修复混凝土裂缝的研究进展.探讨了对电沉积法修复混凝土裂缝的机理,分析了电沉积溶液的选择要求,对比了不同学者关于电沉积效果的表征方法及其影响因素,并归纳了电沉积方法修复后混凝土性能的改善,最后提出电沉积方法对混凝土裂缝的修复机制、愈合效果评价、电沉积层与钢筋混凝土结构基体材料界面结合机制等方面还有待进一步的研究.     

膨润土种类及掺量对塑性混凝土性能的影响

通过塑性混凝土和易性、抗压强度、弹性模量和相对渗透系数试验,对比分析钠基膨润土和钙基膨润土对塑性混凝土和易性、抗压强度、弹性模量和相对渗透系数的影响。结果表明:塑性混凝土和易性满足要求;同一龄期下随着膨润土掺量的增加,塑性混凝土的抗压强度和弹性模量都降低,但掺钠基膨润土的塑性混凝土抗压强度和弹性模量比掺钙基膨润土的塑性混凝土抗压强度和弹性模量高约1.5倍;前者的相对渗透系数小于后者;塑性混凝土中膨润土的掺量不宜超过60%,宜控制在20%～40%之间;宜用90 d龄期作为塑性混凝土力学性能试验的标准养护龄期。     

钢筋锈蚀氯离子临界浓度研究进展

鉴于钢筋锈蚀氯离子临界浓度对钢筋混凝土结构的使用寿命有很大影响,从钢筋锈蚀氯离子临界浓度的表达形式、测试方法、影响因素等方面对国内外氯离子临界浓度的研究进展进行综述,给出了已有研究成果得到的氯离子临界浓度值和有关国家标准中限定的氯离子浓度,提出氯离子临界浓度的影响机理、测试方法、影响因素的耦合作用、计算模型和提高方法等有待进一步研究的问题。     

关于聚合物改性水泥砂浆研究的思考

从水工混凝土建筑物老化病害的现象、原因和造成的后果等方面阐述了加强聚合物改性水泥砂浆研究的必要性,归纳了聚合物的种类,分析了聚合物改性水泥砂浆的国内外研究现状,在此基础上提出有待进一步研究的哪问题.     

芳纶纤维与表面处理层界面粘合机理研究

用扫描电子显微镜（SEM）和电子能谱仪（XPS）研究芳纶纤维与表面处理层界面粘合机理。结果表明,采用封闭异氰酸酯以及RFL胶乳体系浸渍处理后的芳纶纤维表面增加了一种新的结合碳,而且其它碳的结合能向高能方向移动,纤维表面处理层的氮原子所占比例增大,提高了芳纶纤维的表面活性。     

A Method of Preparation of Ag/AgCl Chloride Selective Electrode

We put forward a method of rapid preparation of chloride selective electrode (Ag/AgCl electrode) by dipping silver wire into sodium hypochlorite solution. The electrodes were prepared through different immersion time. The properties of the electrodes, such as Nernst response, response time and long-term stability, were tested in simulated concrete pore solutions (SCPS). Moreover, the surface morphology of the electrodes was also detected after immersion in solutions over three months. The experimental results reveal that the Ag/AgCl electrode with the fabrication time of 20 minutes (E-20) which is recommended to work as the chloride ion selective electrode has the best performance. Compared to that fabricated by the electrolytic process (E-EP), E-20 can be manufactured in mass. The method has almost the same good performance of Nernst response as E-EP, and has a better response time which is less than 25 seconds. The method also shows a better good long-term stability in SCPS containing chloride ions over three months.     

聚苯乙烯改性泡沫混凝土的强度和收缩性能研究

制备了不同泡沫掺量(泡浆比为0、0.5、1、1.5、2、2.5、3、4)及复掺不同聚苯乙烯颗粒(颗粒与泡沫体积比为0.5、1、1.5、2)的轻质混凝土,研究了EPS(Expanded Polystyrene,简称EPS)颗粒对轻质泡沫混凝土强度及收缩性能的影响。随着泡浆比的增大,泡沫混凝土的表观密度和抗压强度逐渐降低,收缩值也随之增大;当泡沫掺量过大时,泡沫混凝土易出现坍模现象,料浆的缺陷也会增多。而复掺EPS颗粒的泡沫混凝土采用EPS颗粒取代部分泡沫,解决了高掺量泡沫的混凝土易坍模的问题;随着EPS颗粒掺量的增加,泡沫混凝土的表观密度和抗压强度值变得稳定,同等密度条件下强度更高,延缓了泡沫混凝土的收缩。