Highly translucent nanostructured glass-ceramic

Transparent and translucent glass-ceramics (GCs) are found in an increasing number of domestic and high-technology applications. In this paper, we evaluated and optimized the effects of two-stage heat treatments on the resulting crystalline phases and microstructure of a glass of the SiO₂–Li₂O–P₂O₅–TiO₂–CaO–ZnO–Al₂O₃ system. The objective was to develop a transparent nanostructured glass-ceramic (GC). After numerous heat treatment trials, we found that a long nucleation period of 72 h at 455 °C followed by a crystal growth treatment at 660 °C for 2 h resulted in a highly translucent GC having homogenously distributed nanocrystals. The relatively high amount of P₂O₅ (2.5 mol%) induced the formation of lithium disilicate as the main crystal phase. We thus developed a GC having crystals under 50 nm, with a high crystallized fraction (52%vol. Li₂Si₂O₅ and 26% vol Li₂SiO₃), transmittance of approximately 80% in the visible spectrum for 1.2 mm thick specimens, nano hardness of 8.7 ± 0.1 GPa (load of 400 mN), a high elastic modulus of 138 ± 3 GPa as measured by nanoindentation, and good flexural strength (350 ± 40 MPa) as measured by ball-on-3 balls tests. Due to its high content of Li⁺, this GC has the potential to be chemically strengthened and can be further developed to be used in a number of applications, such as on displays of electronic devices.     

A formal framework for secure and complying services

Internet is offering a variety of services that are assembled to accomplish requests made by clients. While serving a request, security of the communications and of the data exchanged among services is crucial. Since communications occur along specific channels, it is equally important to guarantee that the interactions between a client and a server never get blocked because either cannot access a selected channel. We address here both these problems, from a formal point of view. A static analysis is presented, guaranteeing that a composition of a client and of possibly nested services respects both security policies for access control, and compliance between clients and servers.     

Glass-Ceramic Materials for Guided-Wave Optics

Glass-ceramics (GCs) are multiphase micro- or nano-crystalline materials produced by the controlled nucleation and crystallization of an amorphous glass through a proper heating or chemical process. Most optical applications require transparency, and this usually implies that the crystalline phase be made of nanocrystals. Transparent GCs are able to combine the advantages of all their components, glasses, and crystals. Incorporation of semiconducting, ferroelectrical, and nonlinear optical phases in glass matrices can produce very promising materials for different applications. A very important role is played by nanocrystals which are activated by luminescent species, as rare earth ions. The presence of the crystalline environment around a rare earth ion allows high absorption and emission across sections, and reduction in the nonradiative relaxations thanks to the lower phonon cut-off energy. Such materials may lead to real advances in optical amplifiers, up-conversion fibers, solid-state lasers, medical sensors, and several other devices, especially if combined with a guided-wave configuration, which allows high energy densities and efficient delivery of the transmitted optical beams. The present review article covers the properties and current state of transparent glass-ceramics for guided-wave devices, including the discussion of the preparation methods and of their spectral and luminescent properties.     

Platelet lysate and adipose mesenchymal stromal cells on silk fibroin nonwoven mats for wound healing

In this work platelet lysate (PL) and adipose‐derived mesenchymal stromal cells (ASCs) seeded on nonwoven fibroin mats were in vitro and in vivo evaluated for tissue regenerative applications. Nonwoven mats obtained by a large scale water entanglement technique were characterized for their physico‐chemical properties. Results indicated a high purity of fibroin fibers, their stability after sterilization process and appropriate technological properties suitable for tissue engineering. Moreover, the scaffolds in vitro supported adhesion and migration of ASCs and the presence of PL improved the cell proliferation. The products were then applied on epithelial/dermal wounds carried out on the dorsal surface of rabbit: the skin reparative process was solved in 9 days, with a completely restitutio ad integrum of the epithelium in animals treated with PL alone; ASCs did not further improve the wound healing. © 2015 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2016 , 133, 42942.     

Effects of Sedentarism and Treadmill Training in Mechanical Properties of Muscles of Ovariectomized Rats with High-Fat Diet

The aim of this study is to evaluate the ability of physical training in the maintenance of muscle strength in rats with HFD （high-fat diet） after OVX （ovariectomy）. Eighty Wistar rats are at eight weeks of age and weight 200 g which divided into 8 groups （n = 10） and treated for 12 weeks： GA： OVX ＋ ND （normal diet）, GB： OVX ＋ ND ＋ training, GC： sham ＋ ND, GD： sham ＋ ND ＋ training, GE： OVX ＋ HFD, GF： OVX ＋ HFD ＋ training, GG： sham ＋ HFD and GH： sham ＋ HFD ＋ training. HFD consists of standard ration for rats with addition of 30% lipids. In training groups, physical training five training/week was conducted on a treadmill with adaptation period of three weeks up to 18 m/s for one hour, training were performed for 12 weeks. The sedentary animals remained in individual box. To analyze the effects of training and diet, tensile strength tests of the gastrocnemius muscles were conducted： the speed of 0.1 mm/min. Analysis of variance was performed to compare groups. The mean （SD） obtained for the maximum load （N） were： GA 57.77 （6.89）, GB 62.74 （5.07）, GC 49.45 （6.06）, GD 59.42 （5.26） and GE 55.58 （4.72）, GF 62.50 （4.56）, GG 58.35 （4.54） and GH 56.67 （5.87）, respectively. There were no differences for maximum load between surgeries （p = 0.004） and between treatments （p = 0.000）. Differences were found also for the relationship surgery diet treatment （p = 0.007）. For the variable stiffness （N/mm）, there were not statistically significant differences： GA 5.03 （0.72）, GB 5.08 （1.09）, GC 5.17 （0.53）, GD 5.35 （0.80）, GE 5.52 （1.20）, GF 5.36 （1.07）, GG 4.83 （1.03） and GH 5.40 （0.73）. For the toughness （N/mm）, there were differences between treatments （p = 0.010） and the ratio diet treatment （p = 0.024）： GA 455.00 （107.21）, GB 541.96 （126.80）, GC 394.97 （84.67）, GD 566.90 （157.07）; GE 424.63 （113.03）, GF 478.07 （106.03）; GG 517.44 （98.65?     

Effects of Spray-Drying Conditions on the Physicochemical Properties of Blackberry Powder

The purpose of this work was to study the effects of spray-drying conditions on the physicochemical characteristics of blackberry powder using a central composite rotatable design. Inlet air temperature (140–180°C) and maltodextrin concentration (5–25%) were employed as independent variables. Moisture content, hygroscopicity, anthocyanin retention, color, powder morphology, and particle size were analyzed. A higher inlet air temperature significantly increased the hygroscopicity of the powder, decreased its moisture content, and led to the formation of larger particles with smooth surfaces. Powders produced with higher maltodextrin concentrations were less hygroscopic, slightly lighter and less red, and had a lower moisture content. Anthocyanin retention was mainly affected by drying temperature due to the heat sensitivity of the pigment. The optimal processing conditions were an inlet air temperature of 140–150°C and maltodextrin concentration of 5–7%. Overall, these results indicate that good quality powders can be obtained by spray drying, with potential applications for the food industry.