Wear and Creep Characteristics of a Carbon‐Derived Si3N4/SiC Micro/Nanocomposite

In the presented work some properties of a recently developed Si₃N₄/SiC micro/nanocomposite have been investigated. The material was tested using a pin on disc configuration. Under unlubricated sliding conditions using Si₃N₄ pin at 50 % humidity, the friction coefficient was in the range of 0,6 ‐ 0,7. The reduction of humidity resulted in a lower coefficient of friction, in vacuum the coefficient of friction had a value of about 0,6. The wear resistance in vacuum was significantly lower then that in air. The wear patterns on the Si₃N₄+SiC disc revealed that mechanical fracture was the wear controlling mechanism. Creep tests were realized in four point bending configuration in the temperature interval 1200‐1400 °C at stresses 50,100 and 150 MPa and the minimal creep deformation rate was established for each stress level. The activation energy, established from the minimal creep deformation had a value of about 360 kJ/mol and the stress exponent values were in the range of 0.8‐1.28. From the achieved stress exponents it can be assumed that under the studied load/temperature conditions the diffusion creep was the most probable creep controlling mechanism.     

Colloidal processing of polymer ceramic nanocomposite integral capacitors

Polymer ceramic composites form a suitable material system for low temperature fabrication of embedded capacitors appropriate for the MCM-L technology. Improved electrical properties such as permittivity can be achieved by efficient filling of polymers with high dielectric constant ceramic powders such as lead magnesium niobate-lead titanate (PMN-PT) and barium titanate (BT). Photodefinable epoxies as the matrix polymer allow fine feature definition of the capacitor elements by conventional lithography techniques. The optimum weight percent of dispersant is tuned by monitoring the viscosity of the suspension. The dispersion mechanism (steric and electrostatic contribution) in a slightly polar solvent such as propylene glycol methyl ether acetate (PGMEA) is investigated from electrophoretic measurements. A high positive zeta potential is observed in the suspension, which suggests a strong contribution of electrostatic stabilization. By optimizing the particle packing using a bimodal distribution and modified processing methodology, a dielectric constant greater than 135 was achieved in PMN-PT/epoxy system. Suspensions are made with the lowest PGMEA content to ensure the efficiency of the dispersion and efficient particle packing in the dried film. Improved colloidal processing of nanoparticle-filled epoxy is a promising method to obtain ultra-thin capacitor films (<2/spl mu/m) with high capacitance density and improved yield. Capacitance of 35 nF/cm/sup 2/ was achieved with the thinnest films (2.5-3.0 /spl mu/m).     

Modeling of the Solubility of Solid High-Molecular-Weight Organic Substances in Supercritical Fluids

A method is proposed to calculate the solubility of solid high-molecular-weight substances in organic supercritical fluids on the basis of the Soave and Peng–Robinson equations of state. The mixing rules are modified taking into account the Gibbs energy of mixing calculated for a particular equation of state. The accuracy of calculation of the concentration of the substance dissolved in supercritical fluids is analyzed for different mixing rules. The modeling results are compared with observed data.     

Enhanced Photoelectrochemistry in CdS/Au Nanoparticle Bilayers

Three different configurations of Au‐nanoparticle/CdS‐nanoparticle arrays are organized on Au/quartz electrodes for enhanced photocurrent generation. In one configuration, Au‐nanoparticles are covalently linked to the electrode and the CdS‐nanoparticles are covalently linked to the bare Au‐nanoparticle assembly. The resulting photocurrent, φ = 7.5 %, is ca. 9‐fold higher than the photocurrent originating from a CdS‐nanoparticle layer that lacks the Au‐nanoparticles, φ = 0.8 %. The enhanced photocurrent in the Au/CdS nanoparticle array is attributed to effective charge separation of the electron–hole pair by the injection of conduction‐band electrons from the CdS‐ to the Au‐nanoparticles. Two other configurations involving electrostatically stabilized bipyridinium‐crosslinked Au/CdS or CdS/Au nanoparticle arrays were assembled on the Au/quartz crystal. The photocurrent quantum yields in the two systems are φ = 10 % and φ = 5 %, respectively. The photocurrents in control systems that include electrostatically bridged Au/CdS or CdS/Au nanoparticles by oligocationic units that lack electron‐acceptor units are substantially lower than the values observed in the analogous bipyridinium‐bridged systems. The enhanced photocurrents in the bipyridinium‐crosslinked systems is attributed to the stepwise electron transfer of conduction‐band electrons to the Au‐nanoparticles by the bipyridinium relay bridge, a process that stabilizes the electron–hole pair against recombination and leads to effective charge separation.     

Development of a Continuous Segmented Flow Tubular Reactor and the “Scale‐out” Concept – In Search of Perfect Powders

The synthesis of powders with controlled shape and narrow particle size distributions is still a major challenge for many industries. A continuous Segmented Flow Tubular Reactor (SFTR) has been developed to overcome homogeneity and scale‐up problems encountered when using batch reactors. Supersaturation is created by mixing the co‐reactants in a micromixer inducing precipitation; the suspension is then segmented into identical micro‐volumes by a non‐miscible fluid and sent through a tube. These micro‐volumes are more homogeneous when compared to large batch reactors leading to narrower size distributions, better particle morphology, polymorph selectivity and stoichiometry. All these features have been demonstrated on single tube SFTR for different chemical systems. To increase productivity for commercial application the SFTR is being “scaled‐out” by multiplying the number of tubes running in parallel instead of scaling‐up by increasing their size. The versatility of the multi‐tube unit will allow changes in type of precipitate with a minimum of new investment as new chemistry can be researched, developed and optimised in a single tube SFTR and then transferred to the multi‐tube unit for powder production.     

Reliability investigation of 0.07-/spl mu/m InGaAs-InAlAs-InP HEMT MMICs with pseudomorphic In/sub 0.75/Ga/sub 0.25/As channel

The authors have investigated the reliability performance of G-band (183 GHz) monolithic microwave integrated circuit (MMIC) amplifiers fabricated using 0.07-/spl mu/m T-gate InGaAs-InAlAs-InP HEMTs with pseudomorphic In/sub 0.75/Ga/sub 0.25/As channel on 3-in wafers. Life test was performed at two temperatures (T/sub 1/ = 200 /spl deg/C and T/sub 2/ = 215 /spl deg/C), and the amplifiers were stressed at V/sub ds/ of 1 V and I/sub ds/ of 250 mA/mm in a N/sub 2/ ambient. The activation energy is as high as 1.7 eV, achieving a projected median-time-to-failure (MTTF) /spl ap/ 2 /spl times/ 10/sup 6/ h at a junction temperature of 125 /spl deg/C. MTTF was determined by 2-temperature constant current stress using /spl Delta/G/sub mp/ = -20% as the failure criteria. The difference of reliability performance between 0.07-/spl mu/m InGaAs-InAlAs-InP HEMT MMICs with pseudomorphic In/sub 0.75/Ga/sub 0.25/As channel and 0.1-/spl mu/m InGaAs-InAlAs-InP HEMT MMICs with In/sub 0.6/Ga/sub 0.4/As channel is also discussed. The achieved high-reliability result demonstrates a robust 0.07-/spl mu/m pseudomorphic InGaAs-InAlAs-InP HEMT MMICs production technology for G-band applications.     

The hot compaction behaviour of woven oriented polypropylene fibres and tapes. I. Mechanical properties

The aim of this work was to establish the important parameters that control the hot compaction behaviour of woven oriented polypropylene. Five commercial woven cloths, based on four different polypropylene polymers, were selected so that the perceived important variables could be studied. These include the mechanical properties of the original oriented tapes or fibres, the geometry of the oriented reinforcement (fibres or tapes), the mechanical properties of the base polymer (which are crucially dependant on the molecular weight and morphology), and the weave style. The five cloths were chosen so as to explore the boundaries of these various parameters, i.e. low and high molecular weight: circular or rectangular reinforcement (fibres or tapes): low or high tape initial orientation: coarse or fine weave.A vital aspect of this study was the realisation that hot compacted polypropylene could be envisaged as a composite, comprising an oriented ‘reinforcement’ bound together by a matrix phase, formed by melting and recrystallisation of the original oriented material. We have established the crucial importance of the properties of the melted and recrystallised matrix phase, especially the level of ductility, in controlling the properties of the hot compacted composite.     

Thermal conductivity of doped PbTe-based solid solutions with off-center impurities

The coefficients of thermopower and electrical and thermal conductivity in the PbTe_0.8Se_0.1 S _0.1 solid solution with electron concentration (4.6–54) × 10¹⁸ cm^?3 are studied in the range of 85–300 K (and in some cases up to 700 K). The temperature dependences of electrical and thermal conductivity indicate that the low-temperature electron and phonon scattering initiated by the off-center impurity of sulfur exists. The temperature dependences of the electronic and lattice components of thermal conductivity are calculated in the approximation of a parabolic spectrum and electron scattering by acoustic phonons and neutral substitutional impurities. The lattice thermal conductivity is found to have a feature in the form of a shallow minimum in the range of 85–250 K. A similar feature, while not so clearly pronounced, is found to exist also in Pb_1?x Sn_xTe_1?x Se_x alloys (x≥0.15) with an off-center tin impurity. An analysis of the possible origins of this effect suggests that, at low temperatures, the Lorentz numbers L of the materials under study are smaller than the L₀ numbers employed which correspond to the above scattering mechanisms. The cause of the decrease in L is related to electron scattering at two-level systems, a mechanism whose effect grows with increasing electron energy. An analysis of experimental data obtained at high temperatures, as well as on undoped samples with the lowest possible carrier concentrations, yields the values of L for samples with different electron densities. The minimum value L/L₀ = 0.75 is obtained for a lightly doped sample at ～130 K.     

A simple impulsiveness correction factor for control of electromagnetic interference in dynamic wireless applications

The emerging software defined radio technologies will be an enabler for a new generation of dynamic wireless systems. It will also open up the possibility of allocating frequencies in a, more dynamic way than today. From an intersystem-interference point of view, this can cause unforeseen problems to occur due to the increased complexity in such applications. In such applications, a measure indicating whether or not a frequency band is possible to use from an electromagnetic interference point of view, must be found. A simple approach is to use the measured total average interference power within the receiver band. Since the interference impact on modern digital communication systems from an interference signal does not only depend on the power but also on the actual waveform of the interference signal, some kind of quality measure of the average-power approach would be convenient to use. In this paper, we introduce a simple quality measure of the average-power approach so that a rough adjustment for the interference-waveform properties can be done.