Catalytic Hydrocracking of a Bitumen‐Derived Asphaltene over NiMo/γ‐Al2O3 at Various Temperatures

Hydrocracking of a bitumen‐derived asphaltene over NiMo/γ‐Al₂O₃ was investigated in a microbatch reactor at varying temperatures. The molar kinetics of asphaltene cracking reaction was examined by fitting the experimental data. Below a defined temperature, the molar reaction showed the first‐order kinetic feature while at higher temperatures secondary reactions such as coke formation became significant, causing deviation of the reaction behavior from the proposed first‐order kinetic model. Selectivity analysis proved that dominant products varied from gases to liquids to gases with increasing temperature, shifting the dominant reaction from C–S bonds cleavage to C–C bonds cleavage.     

Structures and properties of chicken myofibrillar protein gel induced by microwave heating

Structures and properties of myofibrillar protein gel prepared at different power (300–800 W) were evaluated. Amino acid analysis demonstrated that changes in microwave power did not alter primary structure of gel. However, an increase in microwave power could change higher structures of gel. As microwave power increased, α-helix content decreased and β-sheet content increased. Increased microwave power probably facilitated protein to unfold and expose the internal groups, causing surface hydrophobicity and the formation of disulphide bonds were enhanced, which indicated changes in tertiary and quaternary structures of protein. At 500 W, gel had the best ultrastructure where surface morphology, springiness and water holding capacity reached the optimum. Our findings suggested that microwave at an appropriate power (500 W) could change higher structures of myofibrillar protein gel to achieve desired processing and quality protein gel characteristics.     

Preparation of ZrC/SiC porous self-supporting monoliths via sol-gel process using polyethylene glycol as phase separation inducer

We present a straightforward method via sol-gel process using polyethylene glycol (PEG) as phase separation inducer to prepare zirconium carbide/silicon carbide (ZrC/SiC) porous monoliths. Organic/inorganic hybrid gels are prepared using zirconium oxychloride, furfuryl alcohol, and tetraethyl orthosilicate as major starting materials. In the presence of PEG, crack-free hybrid monoliths are obtained by drying the wet gels under ambient pressure, whereas in the absence of PEG, the wet gels break into pieces as expected. PEG plays a key role in maintaining the macroscopic shape of the monoliths. After ceramization at 1300–1500?°C, ZrC/SiC porous monoliths are obtained. SEM and mercury intrusion porosimetry data show that PEG also has strong influence on the microstructures of the monoliths. The compressive strengths of the ceramic monoliths are in the range of 0.3 to 0.7?MPa. And their compressive behavior starts to differ due to the changes in their microstructures, especially the pore structure.     

Alloy optimisation of bainitic steel for large plastic mould

Based on the phase transformation theories, especially the T₀ concept of bainite transformation, alloy optimisation of bainitic steel with carbides has been carried out aiming at the produce of plastic mould with large cross-section. The effect of manganese and silicon on proeutectoid ferrite and bainite transformation is explored by dilatometric analysis, XRD and different microscopy techniques. The results show that after the alloy optimisation, the transformation of proeutectoid ferrite is suppressed and when the cooling rate is lower than 0·1°C?s^??1, the new lower bainite transformation appears by decreasing carbon capacity of austenite and promoting carbide precipitation. Industrial production proves that the optimised alloy SDP1 can meet the demand for the plastic mould with the thickness of 1050?mm.