Crack initiation and propagation induced by inclusions in a nickel-base P/M superalloy under fatigue load

1 IntroductionRecently the key components in advanced aircraftengines are widely made of nickel-base P/M super-alloy. However, non-metallic inclusions are intro-duced into this material during powder metallurgyprocessing. In industry, although many method…     

ECAP制备的亚微米7050铝合金的力学性能和微观结构

采用等通道角挤压法 (ECAP法 )制备亚微米 70 5 0铝合金。为了提高合金的力学性能 ,在挤压过程中增加了固溶时效处理工艺 ,并对 70 5 0铝合金在不同处理工艺条件下的显微组织和力学性能的变化进行了研究。结果表明 :ECAP挤压后进行固溶和时效处理能明显提高合金的力学性能。退火态合金经过ECAP后 ,晶粒尺寸明显细化到亚微米级。将挤压一次的试样进行固溶处理和时效处理 ,合金的强度在 5 75MPa左右 ,而延伸率能达到2 5 .5 %左右 ;若经等通道角挤压过的试样在固溶处理后立即进行再次挤压 ,并配合时效处理 ,合金强度能迅速达到 6 16MPa ,延伸率为 16 .9%。     

Preparation and electrochemical performance of nanosized Co3O4 via hydrothermal method

The hydrotalcite-type cobalt compounds were prepared through oxidation of Co（OH）2 gel using NH4OH as precipitating agent and H2O2 as oxidant. These hydrotalcite-type cobalt compounds were transformed into Co3O4 through hydrothermal decomposition with nanostructural deformation. The precursor and product were characterized by Fourier-transform infrared（FT-IR） spectrum, X-ray diffractometry（XRD） and transmission electron microscopy（TEM）. The electrochemical performances of as-prepared nanosized Co3O4 as anode materials in lithium-ion batteries were tested by charge-discharge test in the voltage range of 0-3.0 V. The influence of morphology of Co3O4 particle on the capacity and cycling performance was studied. The results show that the shape and size of the final product can be controlled by altering cobalt sources. The irregular cubic Co3O4 with the average particle size of about 10 nm shows the best electrochemical performance. After 10 charge-discharge cycles, the specific charge capacity retains 555 mA.h/g.     

BEHAVIOR OF Mg AND ITS EFFECT ON MECHANICAL PROPERTIES OF CAST Fe_3Al ALLOYS

Proper addition of 0.002 wt-% Mg to cast Fe_3Al alloy may obviously improve the room andhigh temperature tensile properties.Auger spectra show that Mg segregates near grainboundaries as very thin layers.Observation under TEM reveals that a suitable amount of Mgenhances ability of cooperative internal deformation so that the dislocations will ease the con-tinuous slip deformation through grain boundaries.The fracture feature of Fe_3Al alloy is oftransgranular cleavage at room temperature and cracks initiate at grain boundaries.     

金相显微镜三维自动平台

运用现代计算机信息处理技术和自动控制技术，成功地对一台国产显微镜和一台进口显微镜的载物台进行了自动化改造，实现了X、Y方向自动移动和Z方向自动聚焦。本方案改造加工工作小，成本低，不破坏原有显微镜结构，同时还保留了传统的手动调节方法，使用户更容易接受。同时，系统控制软件还中嵌了软件可编程技术，从而简化了操作过程，明显减轻了劳动强度。本系统符合我国国情，是进口设备优良的替代品。     

铝锡合金摩擦磨损性能的研究

研究了含锡量3%～30%铝锡合金的摩擦磨损性能,结果表明:随着含锡量的增加,铝锡合金的承载能力下降,摩擦系数下降.该合金的显微组织为硬的铝锡固溶体基体上分布着软的锡相质点.常温下含锡量在9%时,合金具有优良的耐磨减摩的综合性能.     

PCD用钎料及钎焊工艺的研究

PCD的广泛应用给钎焊技术提出了更高的技术要求，常规钎料已不能满足高疲劳，高温抗剪的要求，根据Ag,Cu,Zn,Cd,Ni,Co,Mn等元素在钎料中的作用和特点，进行分析和选择从而配制了十几种牌号的钎料，并对其熔点，强度，钎焊工艺进行了研究，研制出一系列新型的银基钎料，研究和使用结果表明，研制的系列钎料分别适宜不同工作条件下的PCD工具的钎焊。     

MnCl2对镁合金废旧料组织性能的影响

利用等离子发射光谱仪、金相分析、电镜、万能电子材料试验机、腐蚀试验等方法研究了含有不同量的MnCl2熔剂对镁合金废旧料的力学性能、组织、断口形貌以及腐蚀行为的影响。研究表明,MnCl2可以降低镁合金废旧料中的Fe含量,同时会增加镁合金的Mn量,使用含MnCl2的熔剂可将镁废旧料中的Fe含量降到0 0072%以下。采用含MnCl2的熔剂可以提高试样的σb和δ。当合金中的Mn量超过一定程度后,对镁合金的力学性能会产生不利的影响。金相观察表明,净化处理对断口形貌无明显的影响,不改变AZ91镁合金的断裂机理,断口均成准解理断裂。腐蚀试验表明,采用含30%MnCl2的熔剂可以使试样的腐蚀速率从20 9mg/(cm2·d)降到6 4mg/(cm2·d)。     

SiCp/Al复合材料热处理及统计分析

采用四因素多水平组合热处理试验与统计分析相结合的方法研究了粉末冶金制备的12%SiCp/6066Al(体积分数)复合材料的热处理工艺参数与硬度间的关系.结果表明,复合材料与基体合金相比具有峰值提前效应;热处理工艺参数主效应由强到弱依次为时效时间、固溶温度、时效温度、固溶时间;时效时间与时效温度一级交互作用也较重要,其他一级、二级和三级交互作用较小.12%SiCp/6066Al复合材料的优化热处理工艺参数为530℃固溶90min,水淬170℃时效6h.     

两种类型活套的张力控制模型

介绍了带钢热连轧过程中电动活套和液压活套各自的张力控制模型，前者以电机电流作为控制对象，后者以液压缸压力作为控制对象。