添加Zn^2+对ZIRLO合金在模拟压水堆一回路含LiOH和H3BO3水溶液工况下耐腐蚀性能的影响

对ZIRLO合金在360℃,18.6 MPa,含LiOH和H3BO3溶液的高温高压釜中进行了水侧腐蚀实验;并通过在其中的一个高压釜中加入乙酸锌,从而对比研究了加Zn对ZIRLO合金耐腐蚀性能的影响。结果表明:在腐蚀介质溶液中添加50μg/kg乙酸锌对ZIRLO合金的腐蚀增重情况、氧化膜厚度、氧化膜中第二相种类及大小、氧化膜表层元素的种类、分布及价态并无显著影响,但降低了氧化膜表层沉积物中Fe的含量,并抑制了国产新锆合金腐蚀过程中的吸氢。     

Effect of ultrasonic vibration on the dechromisation corrosion of a CuCr alloy in HCl solution

The effect of ultrasonic vibration on the dechromisation corrosion of a CuCr alloy in HC1 solution was studied and the corrosion mechanisms were analyzed. It is found that ultlasonic vibration reduces the dechromisation incubation time, accelerates the dechromisafion corrosion rate, decreases the temperature and concentration of HC1 solution, and when the dechromisation occurs it seriously weakens the microstmcture of dechromisation layer. It is concluded that ultrasonic vibration can accelerate destruction of the passivation film on the Cr surface and increase the activities of Cl^- and Cr.     

NdFeB铸块HD工艺中温度和压力对吸氢行为的影响

对NdFeB铸块在HD工艺中温度和压力对吸氢行为的影响进行了研究。研究发现，NdFeB铸块在氢爆过程中明显存在孕育期，其吸氢过程分为四个阶段：孕育期阶段、慢速吸氢阶段、快速吸氢阶段和缓慢吸氢阶段；随着氢气压力(1～4atm)的升高，孕育时间缩短，吸氢越快；随着温度的升高，NdFeB铸块吸氢越迅速，当温度升至一定程度时，孕育期消失。扫描电镜观察发现，NdFeB合金氢爆破碎中的断裂方式包括沿晶和穿晶断裂，氢爆粉末尺寸小于50μm，取得了较好的氢爆效果。     

渑池铝矿铁路装车检斤系统的开发与应用

针对长铝矿山公司渑池铝矿矿石专列装车过程中出现的超、亏吨问题 ,成功地开发了称重轨型装车检斤控制系统 ,本文详细介绍了该系统的原理、安装、检定、运行等情况 ,对类似铁路装车线路改造有借鉴意义。     

AZ91D摩托车发动机壳体压铸模设计

针对摩托车发动机壳体的结构特点及工艺要求,介绍了一种切实可行的压铸模设计方案。该压铸模选择最大截面为分型面,浇注系统设计时采用FLOW-3D仿真软件进行模拟填充,用模温机及循环的冷却水控制模具温度,设置斜销式抽芯机构。经生产实践证明,铸件达到了图纸的各项要求,并已进行小批量生产。     

表面渗铬T8钢中碳迁移的热力学分析

采用双辉等离子渗铬技术，对T8钢进行了900℃温度表面渗铬合金化；使用GDA750．测量了试样渗铬合金层中Fe、Cr和C等元素的浓度分布。通过热力学分析计算，研究了渗铬合金化层形成过程中碳迁移机理和规律。指出驱动碳迁移的动力是碳的括度梯度，并推导出富碳区碳质量分数随铬质量分数变化的数学关系式：w(C）=0．8 0.3536w(Cr)。计算结果与试验结果相当吻合。     

Thermal expansion anomaly and spontaneous magnetostriction of Dy2AlFe14Mn2 compound

The structure and magnetic properties of Dy₂AlFe₁₄Mn₂ compound were investigated by X-ray diffractometry and magnetization measurements. Dy₂AlFe₁₄Mn₂ compound has a hexagonal Th₂Ni₁₇-type structure. Zero thermal expansion and negative thermal expansion were found in Dy₂AlFe₁₄Mn₂ compound in the temperature range from 184 to 264 K, and from 264 to 383 K, respectively, by X-ray dilatometry. The spontaneous magnetostrictive deformations from 104 to 400 K were calculated. The results show that the spontaneous volume magnetostrictive deformation increases firstly with increasing temperature, and then decreases with further increasing temperature.     

基于视觉传感的焊缝中心检测技术研究

通过视觉传感器获取焊缝图像，采用多种去噪技术对焊缝图像中的噪声进行滤波试验。针对焯缝图像中的干扰噪声特性，对各种滤波方法进行了分析和比较，并对滤波效果较好的焊缝图像进行边缘检测计算。提出3种识别焊缝特征的组合图像处理方法，并研究提取焊缝中心特征信息的效果和精度。试验结果表明，对焊缝图像采用Wiener滤波与Robert边缘检测算法能较好地提取焊缝中心位置的特征信息。     

WCp增强钢基表层复合材料的两体磨粒磨损性能

在室温条件下,选用销盘磨粒磨损试验机,绿碳化硅磨料,研究增强相WC颗粒直径对WCp增强钢基表层复合材料磨损性能的影响,以正火ZG45作为标样,计算相对耐磨性ε值.研究结果表明,WCp增强钢基表层复合材料相对于正火ZG45的相对耐磨性ε值,随其增强相WC颗粒直径的变小而降低,当增强相WC颗粒直径大于150μm时,相对耐磨性ε值高达40左右,而当增强相WC颗粒直径小于100μm时,相对耐磨性ε值降低到5以下.     

基于VERICUT的虚拟龙门加工中心建模和仿真关键技术研究

为减少零部件试切,检验数控工艺合理性,构建了虚拟龙门加工中心。研究了龙门加工中心运动,阐述了侧面铣头运动由旋转中心和换刀点控制,提出了虚拟机床侧面铣削运动构建方法,可实现各角度侧面铣。搭建了虚拟加工环境,通过零件仿真加工,完成了零件顶面及4个侧面的铣削加工,验证了数控代码的正确性,检验了数控工艺合理性,减少了零件试切,缩短了开发周期,仿真结果表明虚拟龙门加工中心的正确性。