The dynamic evolution of aggregated lithium dendrites in lithium metal batteries

Lithium (Li) metal anodes promise an ultrahigh theoretical energy density and low redox potential,thus being the critical energy material for next-generation batteries.Unfortunately,the formation of Li den-drites in Li metal anodes remarkably hinders the practical applications of Li metal anodes.Herein,the dynamic evolution of discrete Li dendrites and aggregated Li dendrites with increasing current densities is visualized by in-situ optical microscopy in conjunction with ex-situ scanning electron microscopy.As revealed by the phase field simulations,the formation of aggregated Li dendrites under high current den-sity is attributed to the locally concentrated electric field rather than the depletion of Li ions.More specif-ically,the locally concentrated electric field stems from the spatial inhomogeneity on the Li metal surface and will be further enhanced with increasing current densities.Adjusting the above two factors with the help of the constructed phase field model is able to regulate the electrodeposited morphology from aggregated Li dendrites to discrete Li dendrites,and ultimately columnar Li morphology.The methodol-ogy and mechanistic understanding established herein give a significant step toward the practical appli-cations of Li metal anodes.     

Effect of supports on the redox performance of pyrite cinder in chemical looping combustion

Chemical looping combustion (CLC) is a clean and efficient flame-free combustion technology,which combust the fuels by lattice oxygen from a solid oxygen carrier with inherent CO2 capture.The develop-ment of oxygen carriers with low cost and high redox performance is crucial to the whole efficiency of CLC process.As the solid by-product from the sulfuric acid production,pyrite cinder presented excellent redox performance as an oxygen carrier in CLC process.The main components in pyrite cinder are Fe2O3,CaSO4,Al2O3 and SiO2 in which Fe2O3 is the active component to provide lattice oxygen.In order to sys-tematic investigate the functions of supports (CaSO4,Al2O3 and SiO2) in pyrite cinder,three oxygen car-riers (Fe2O3-CaSO4,Fe2O3-Al2O3 and Fe2O3-SiO2) were prepared and evaluated in this study.The results showed that Fe2O3-CaSO4 displayed high redox activity and cycling stability in the multiple redox cycles.However,both Fe2O3-Al2O3 and Fe2O3-SiO2 experienced serious deactivation during redox reactions.It indicated that the inert Fe-Si solid solution (Fe2SiO4) was formed in the spent Fe2O3-SiO2 sample,which decreased the oxygen carrying capacity of this sample.The XPS results showed that the oxygen species on the surface of Fe2O3-CaSO4 could be fully recovered after the 20 redox cycles.It can be concluded that CaSO4 is the key to the high redox activity and cycling stability of pyrite cinder.     

人工气候老化后状态调节时间对芳纶纤维拉伸测试的影响

依据GJB 8496—2015标准中的拉伸方法,对人工气候老化前及老化后不进行状态调节、状态调节1 h、状态调节24 h、状态调节48 h、状态调节96 h后的芳纶纤维的拉伸强度进行测量、比较,从而得到结论:芳纶纤维在人工气候老化后,样品的性能有一定程度下降。在刚刚结束老化后立即进行测试,性能下降达到峰值,待状态调节24 h以后,其老化后性能逐步达到一个相对稳定的状态。建议在实际测试中,人工气候老化后的样品应该在老化结束后,放入恒温恒湿间调节24 h以后再测试。     

夹层玻璃中间膜(离子聚合物)的表征与性能探究

离子聚合物中间膜具有较强的力学特征,在力学要求较高的结构性幕墙、栏杆、透明栈道等玻璃建筑上具有广泛的应用.通过对离子聚合物中间膜进行力学、光学等相关的物理性能测试,并与PVB中间膜的数据对比,凸显出离子聚合物的力学、光学等性能优势.利用傅立叶红外光谱(FTIR)、扫描电镜与X光谱区分析联用(SEM-EDS)确定离子聚合物中的主要成分,通过有机元素分析仪、物化分析对离子聚合物各组分基团进行定量分析.对不同厂家及实验室自制的离子聚合物中间膜性能进行比较和探究.     

共沉淀法制备透明质酸修饰超小纳米氧化铁影响因素的研究

采用共沉淀法,通过改变透明质酸及氨水与铁离子的比例、反应物浓度、温度和反应体系大小等反应参数制备出透明质酸修饰的超小超顺磁氧化铁纳米颗粒(Fe3 O4@HA),并对所合成的样品进行了尺寸、形貌和磁性的表征.实验结果表明:使用共沉淀方法时,所制备的Fe3 O4@HA的饱和磁化率受反应参数的影响较小,且都介于55～80 emu/g之间;但纳米颗粒的形貌、水合粒径受反应参数的影响较大.对于初始反应体积为50 mL的体系,透明质酸1.5 g、铁离子0.9 mmol、氨水用量15 mL、温度为80℃是本实验筛出的最佳条件.此外,根据最佳反应条件进行30倍放大,可一次制备出2 L的Fe3 O4@HA溶液,证明本体系具备工业化生产的潜力.     

磷酸二苯酯催化的2-吲哚甲烷胺衍生物的合成

以磷酸二苯酯为催化剂,3-甲基吲哚类化合物与亚胺通过Friedel-Crafts加成反应一步合成了具有广泛药理活性的2-吲哚基甲烷胺类化合物,对反应条件进行优化。结果表明,当n(3-甲基吲哚类)∶n(亚胺)∶n(磷酸二苯酯)=1.0∶2.0∶0.1,其中,磷酸二苯酯0.0025 mmol,1 mL无水二氯甲烷作溶剂,室温下反应0.5 h时,即可得到高收率2-吲哚基甲烷胺类衍生物（85%~90%）。产物经 1HNMR、13CNMR 和 HRMS 进行了结构确定。     

主变方向过流保护拒动原因分析

针对某变电站主变10 kV方向过流保护拒动情况,从保护原理、现场接线、定值设置等方面,分析电流互感器的极性选择及方向元件控制字的设置对短路功率方向的影响,提出规范二次接线、合理设置控制字等防止保护拒动和误动的相关措施,确保方向过流保护动作的正确性.     

锌铝镁镀层钢板前处理与电泳性能研究

以镀锌钢板作为对比,考察锌铝镁钢板涂装前处理和电泳性能.结果显示:锌铝镁钢板的脱脂性能与镀锌钢板相近,磷化膜外观、膜重、覆盖率和结晶尺寸与镀锌钢板差异较小,电泳漆膜外观、膜厚、附着力和耐冲击性与镀锌钢板一致,但电泳漆膜的杯突极限性能和划线循环腐蚀性能优于镀锌钢板.     

充填型单缝煤岩水力脉动解堵试验研究

利用室内自行研制的可调频脉动水力压裂系统及预制充填型单缝的煤岩,开展不同频率条件下水力脉动解堵试验,研究脉动作用下解堵水压演化过程和解堵效果。试验结果表明,水力脉动解堵压力演化过程可分为三个阶段:压力上升阶段、压力下降阶段和压力波动稳定阶段。在疲劳损伤和脉动波的双重作用下,脉动作用下的煤岩解堵表现出解堵压力阀值比定常流作用下更低、压降持续时间更短、压降幅值更小的特点。定常流作用下煤粉运移集中在压力下降阶段;脉动压力作用下煤粉在压力下降阶段和压力波动稳定阶段均有运移,且压力下降时间与运移煤粉总量成正相关关系,但煤粉总的运移量和定常流作用下的相当。脉动作用和定常流作用下径向渗透主要发生在压力上升至压力峰值阶段,但脉动流的解堵时间短,则滤液渗透半径小对储层的伤害小。综合考虑解堵压力、煤粉运移、解堵渗透路径和解堵渗流深度,特别是解堵压力和解堵渗流深度作为主要评价因素,在3 Hz条件下解堵效果最好,其具有较低的解堵压力和最小的解堵渗流深度。