PIXE study on recovery of making-technology of Chinese Longquan celadon made in the Southern Song Dynasty (1127–1279 CE)

Proton induced X-ray emission (PIXE) technique and factor analysis were used to study the recovery of making-technology of Chinese Longquan celadon made in the late Southern Song Dynasty (1127–1279 CE). Based on factor analysis, for the raw material for body and the recipe for glaze, there is a close but slightly different relationship between these Longquan celadons unearthed from the core area of Dayao and the non-core area, despite all the Longquan celadons belong to the high-calcium-glaze system. The chemical compositions of most of the tentative body and glaze samples are very close to those of Longquan celadons unearthed from the core area of Dayao and the non-core area. This study can provide a guidance for recovery of making-technology of Longquan celandon.     

Preparation and electrochromism of pyrochlore-type tungsten oxide film

Pyrochlore-type WO_3 powder was synthesized via hydrothermal method using aqueous sodium tungstate solution and oxalic acid as raw materials. The as-prepared powder was made into a soliquoid,from which films were made by dip coating process with indium-tin oxide(ITO).The obtained films were characterized by thermogravimetric and differential thermal analysis(TG-DTA), X-ray diffraction(XRD),scanning electron microscopy(SEM),transmission electron microscopy(TEM), cyclic voltammetry(CV), chronoamperometry(CA) and ultravioletvisible(UV-Vis) absorption. Results show that the crystal of the pyrochlore-type WO_3 powder is perfect. When the calcination temperature rises from room temperature to500 ℃,the pyrochlore-type structure first becomes deformed, then it is destroyed and turns into amorphous phase,finally it will completely convert to WO_3 with a monoclinic structure. Electrochemical and optical tests demonstrate that the film calcined at 300 ℃ exhibits the best electrochromic performance and has a coloration efficiency of up to 68.5 cm~2 C~(-1) at 884 nm.     

A novel bio‐based phthalonitrile resin derived from catechin: synthesis and comparison of curing behavior with petroleum‐based counterpart

The development of bio‐based thermosetting resins with good thermal stability can potentially afford sustainable polymers as replacements for petroleum‐based polymers. We report a practical route to a novel catechin‐based phthalonitrile resin precursor (CA‐Ph), which contains free phenolic hydroxyl groups that result in ‘self‐curing’ at elevated temperatures to afford a thermostable polymer. Comparison of the performance of this CA‐Ph resin with that of a conventional petroleum‐based bisphenol A phthalonitrile resin (BPA‐Ph; containing 5 wt% of the curing agent 4,4′‐diaminodiphenylsulfone) revealed that CA‐Ph exhibits a lower melting point and curing temperature. Cured CA‐Ph resin retains 95% of its weight at 520 °C under a nitrogen atmosphere, which compares favorably with results obtained for BPA‐Ph resin that retains 95% of its weight at a lower temperature of 484 °C. Kinetic results indicated that the curing reactions of both CA‐Ph and BPA‐Ph systems follow an autocatalytic mechanism. These results suggest that catechin is a useful bio‐based feedstock for the preparation of self‐curing and thermally stable phthalonitrile resins for advanced technological applications. © 2017 Society of Chemical Industry     

内插法在相关干涉仪测向体制中的应用

测向误差的减小一直以来都是无线电测向精度提高的一个难点,对于不同的测向体制所采用的减小测向误差的方法都不尽相同。本文主要介绍的是相关干涉仪测向体制的基本原理以及通过内插法的应用来减小测向误差的方法。     

Design and optimization of ceramic membrane structure: From the perspective of flux matching between support and membrane

The support flux was first investigated as a separate influencing factor for its effect on performances of ceramic filtration membranes. Three pre-membranes were prepared by tape-casting and then transfer-coated to supports to form dual-layer ceramic membranes after sintering. Experiments demonstrated that membrane layers with almost the same properties were obtained despite the huge difference in support flux. When the support flux increases from 3.120 to 97.53 m³m^?2h^?1, the flux of these three membrane series have increased by 75%, 186% and 228%, respectively. Experimental rules can provide structural design and evaluation from the perspective of permeability. The limit membrane flux of a certain system was derived according to the resistance distribution law of internal membrane structure and the Darcy's theorem. On this basis, a method for designing support flux was proposed. Furthermore, we present a criterion to quickly and easily evaluate the match between the support and the top layer, which is the ratio of membrane resistance to total resistance. Finally, the filtration resistance of penetration caused by suction of membrane particles into the support was measured for the first time, taking the advantage of the transfer-coating method that inherently free of penetration. Our works are expected to deepen the understanding of the ceramic membrane structure and provided guidance for its rational design and optimization.