Effects of oxygen-plasma treatment in La0.7Ca0.3MnO3−δ thin films

Oxygen-plasma effects have been investigated for La_0.7Ca_0.3MnO_3−δ thin film samples. As a result, an increase in the metal-insulator transition temperature was observed in a thin film sample. On the other hand, an increase in the resistivity as well as a decrease of the metal-insulator transition temperature was observed in a sample showing considerable structural disorder.     

Multifunctional polyimide/graphene oxide composites via in situ polymerization

In this article, we detail an effective way to improve electrical, thermal, and gas barrier properties using a simple processing method for polymer composites. Graphene oxide (GO) prepared with graphite using a modified Hummers method was used as a nanofiller for r‐GO/PI composites by in situ polymerization. PI composites with different loadings of GO were prepared by the thermal imidization of polyamic acid (PAA)/GO. This method greatly improved the electrical properties of the r‐GO/PI composites compared with pure PI due to the electrical percolation networks of reduced graphene oxide within the films. The conductivity of r‐GO/PI composites (30:70 w/w) equaled 1.1 × 10¹ S m^?1, roughly 10¹⁴ times that of pure PI and the oxygen transmission rate (OTR, 30:70 w/w) was reduced by about 93%. The Young's modulus of the r‐GO/PI composite film containing 30 wt % GO increased to 4.2 GPa, which was an approximate improvement of 282% compared with pure PI film. The corresponding strength and the elongation at break decreased to 70.0 MPa and 2.2%, respectively. © 2013 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2014 , 131, 40177.